Method for preparing hydroisomerization catalysts
Assignee: Mobil Oil AS
•
Filing: 1985-06-03
•
Granted: 1986-10-07
•
Expires: 2005-06-03
Abstract
Abstract A method for preparing hydroisomerization zeolite catalysts containing a highly dispersed noble metal is described. The method includes mix mulling the zeolite, noble metal and binder into an extrudate and chemically treating the formed particles in order to achieve a high dispersion of noble metal on the catalyst.
Inventors
- 👤 Nai Y. Chen
- 👤 Sharon B. McCullen
- 👤 Stephen M. Oleck
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 16:24
CPC Classifications
B; B01; B01J; B01J29/00; B01J29/04; B01J29/06; B01J29/70; B01J29/72; B01J29/74; B01J29/7415; B01J29/064; B01J29/068; B01J2229/00; B01J2229/30; B01J2229/36; B01J37/00; B01J37/22
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
107 words
A method for preparing a highly dispersed noble metal-containing hydroisomerization catalyst comprising a zeolite having a Constraint Index less than 2 and a binder, said method comprising: (a) incorporating at least one noble metal in anionic or cationic form with said zeolite and binder by physical intimate mixing; (b) calcining the product of step (a) in air containing from 0.5 to 1.0 atm H 2 O at a temperature ranging from about 450° to 540° C.; and (c) contacting the product of step (b) with a stream of inert gas containing about 0.001 to 10 wt % chlorine at temperatures ranging from about 250° to 550° C.
Claim 2
Independent Claim
107 words
A method for preparing a highly dispersed noble metal-containing hydroisomerization catalyst comprising a zeolite having a Constraint Index less than 2 and a binder, said method comprising: (a) incorporating at least one noble metal in anionic or cationic form with said zeolite and binder by physical intimate mixing; (b) calcining the product of step (a) in air containing from 0.5 to 1.0 atm H 2 O at a temperature ranging from about 450° to 540° C.; and (c) contacting the product of step (b) with a stream of inert gas containing about 0.001 to 10 wt % chlorine at temperatures ranging from about 250° to 550° C.
Claim 3
Dependent Claim
29 words
The method of claim 1, wherein said at least one noble metal is selected from any of Groups IB, IVB, VIIA or VIII of the Periodic Table of Elements.
Claim 4
Dependent Claim
25 words
The method of claim 1, wherein said at least one noble metal is selected from the group consisting of platinum, palladium, osmium, rhenium and ruthenium.
Claim 5
Dependent Claim
27 words
The method of claim 1, wherein the noble metal content of said at least one noble metal ranges from between about 0.01 to about 10 wt %.
Claim 6
Dependent Claim
27 words
The method of claim 1, wherein the noble metal content of said at least one noble metal ranges from between about 0.3 to about 3 wt %.
Claim 7
Dependent Claim
26 words
The method of claim 1, wherein said binder is an inorganic oxide binder selected from the group consisting of alumina, silica, silica-alumina, magnesia, titania and zirconia.
Claim 8
Dependent Claim
28 words
The method of claim 1, wherein said zeolite is selected from the group consisting of Zeolite Y, Ultrastable Y, Dealuminized Y, Mordenite, faujasite, ZSM-3, ZSM-4, ZSM-18 and ZSM-20.
Claim 9
Dependent Claim
11 words
The method of claim 1, wherein said zeolite is Zeolite Beta.
Claim 10
Dependent Claim
22 words
The method of claim 8, wherein said Zeolite Beta has a SiO 2 /Al 2 O 3 ratio of at least 120:1.
Claim 11
Dependent Claim
43 words
The method of claim 1, further comprising, after step (b) and prior to step (c), contacting product of step (b) with a stream of inert gas containing about 0.001 to 10 wt % chloride at temperatures ranging from about 25° to 550° C.
Claim 12
Dependent Claim
12 words
The method according to claim 10, wherein said chloride is hydrochloric acid.
Claim 13
Independent Claim
150 words
A method for preparing a highly dispersed noble metal-containing hydroisomerization zeolite catalyst, said zeolite catalyst comprising a zeolite having a Constraint Index not more than 2 and a binder, which comprises: (a) physically, intimately contacting at least one noble metal in anionic or cationic form with said zeolite and binder and water; (b) extruding the product of step (a); (c) drying the product of step (b) at a temperature of about 130° C.; (d) calcining the combination of said zeolite, said binder and said at least one noble metal in air containing from 0.5 to 1.0 atm H 2 O at a temperature ranging from about 450° to 540° C.; (e) reducing the product of step (d) in hydrogen; and; (f) contacting the product of step (e) with a stream of inert gas containing about 0.001 to 10 wt % chlorine at temperatures ranging from about 250° to 550° C.
Claim 14
Independent Claim
150 words
A method for preparing a highly dispersed noble metal-containing hydroisomerization zeolite catalyst, said zeolite catalyst comprising a zeolite having a Constraint Index not more than 2 and a binder, which comprises: (a) physically, intimately contacting at least one noble metal in anionic or cationic form with said zeolite and binder and water; (b) extruding the product of step (a); (c) drying the product of step (b) at a temperature of about 130° C.; (d) calcining the combination of said zeolite, said binder and said at least one noble metal in air containing from 0.5 to 1.0 atm H 2 O at a temperature ranging from about 450° to 540° C.; (e) reducing the product of step (d) in hydrogen; and; (f) contacting the product of step (e) with a stream of inert gas containing about 0.001 to 10 wt % chlorine at temperatures ranging from about 250° to 550° C.
Claim 15
Dependent Claim
29 words
The method of claim 12, wherein said at least one noble metal is selected from any of Groups IB, IVB, VIIA or VIII of the Periodic Table of Elements.
Claim 16
Dependent Claim
25 words
The method of claim 12, wherein said at least one noble metal is selected from the group consisting of platinum, palladium, osmium, rhenium and ruthenium.
Claim 17
Dependent Claim
27 words
The method of claim 12, wherein the noble metal content of said at least one noble metal ranges from between about 0.01 to about 10 wt %.
Claim 18
Dependent Claim
27 words
The method of claim 12, wherein the noble metal content of said at least one noble metal ranges from between about 0.3 to about 3 wt %.
Claim 19
Dependent Claim
26 words
The method of claim 12, wherein said binder is an inorganic oxide binder selected from the group consisting of alumina, silica, silica-alumina, magnesia, titania and zirconia.
Claim 20
Dependent Claim
28 words
The method of claim 12, wherein said zeolite is selected from the group consisting of Zeolite Y, Ultrastable Y, Dealuminized Y, Mordenite, faujasite, ZSM-3, ZSM-4, ZSM-18 and ZXM-20.
Claim 21
Dependent Claim
11 words
The method of claim 12, wherein said zeolite is Zeolite Beta.
References Cited (Backward Citations)
US28341A
Cited
USRE28341E
Cited
US3691255A
Cited
US3986982A
Cited
US4016218A
Cited
US4188282A
Cited
US4312790A
Cited
US4444895A
Cited
US4518708A
Cited
US4539305A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-10-06 | 1990-04-07 | 1990-10-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-10-06 | 1994-04-07 | 1994-10-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-10-06 | 1998-04-07 | 1998-10-07 | $7700.00 | Window Closed / Lapsed |