Process for preparing high purity alpha-alumina
Assignee: Honeywell International Inc
•
Filing: 1986-02-03
•
Granted: 1986-10-07
•
Expires: 2006-02-03
Abstract
Abstract High purity alumina with a low sodium content and with a friable, easily ball milled structure is produced in this invention through a modified sol-gel procedure which includes digestion of the contaminant containing aluminum metal with hydrochloric acid in the presence of excess aluminum, removal of the contaminants, seeding the resulting sol with high purity alumina, drying to a solid, and then calcining said seeded sol solids to produce said high purity alpha alumina.
Inventors
- 👤 Stephen T. Gonczy
- 👤 Roy T. Mitsche
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 19:19
CPC Classifications
C; C01; C01F; C01F7/00; C01F7/02; C01F7/42; C01F7/428; C01P; C01P2004/00; C01P2004/60; C01P2004/61; C01P2004/62; C01P2006/00; C01P2006/10; Y; Y10; Y10S; Y10S516/00; Y10S516/921
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
100 words
A method for the preparation of high purity, fine particulate, friable alpha alumina from an alumina sol comprising the steps of (a) digesting aluminum metal containing contaminants in an excess of aluminum metal with hydrochloric acid and water at digestion conditions to produce an alumina sol containing solid contaminants and excess aluminum metal; (b) purifying said sol; (c) seeding said purified sol with fine particulate alpha alumina; (d) drying said seeded sol to produce an alpha alumina precursor; (e) calcining said dried precursor at calcination conditions to produce a high purity, friable alpha alumina; and, (f) recovering said alpha alumina.
Claim 2
Independent Claim
100 words
A method for the preparation of high purity, fine particulate, friable alpha alumina from an alumina sol comprising the steps of (a) digesting aluminum metal containing contaminants in an excess of aluminum metal with hydrochloric acid and water at digestion conditions to produce an alumina sol containing solid contaminants and excess aluminum metal; (b) purifying said sol; (c) seeding said purified sol with fine particulate alpha alumina; (d) drying said seeded sol to produce an alpha alumina precursor; (e) calcining said dried precursor at calcination conditions to produce a high purity, friable alpha alumina; and, (f) recovering said alpha alumina.
Claim 3
Dependent Claim
45 words
The method as set forth in claim 1 further characterized in that said digestion conditions include a temperature in the range of from about 25° C. to about 100° C. and a time in the range of from about 24 hours to about 48 hours.
Claim 4
Dependent Claim
21 words
The method as set forth in claim 1 further characterized in that said purification of said sol is effected by filtration.
Claim 5
Dependent Claim
24 words
The method as set forth in claim 1 further characterized in that said drying of said sol is effected by spray drying said sol.
Claim 6
Dependent Claim
24 words
The method as set forth in claim 1 further characterized in that said drying of said sol is effected by spin drying said sol.
Claim 7
Dependent Claim
24 words
The method as set forth in claim 1 further characterized in that said drying of said sol is effected by flash drying said sol.
Claim 8
Dependent Claim
45 words
The method as set forth in claim 1 further characterized in that said calcination conditions include a temperature in the range of from about 1000° C. to about 1100° C. and a time in the range of from about 60 minutes to about 120 minutes.
Claim 9
Dependent Claim
30 words
The method as set forth in claim 1 further characterized in that said hydrochloric acid is present in a molarity in the range of from about 3M to about 12M.
Claim 10
Dependent Claim
21 words
The method as set forth in claim 1 further characterized in that said purification is effected in the absence of oxygen.
Claim 11
Dependent Claim
21 words
The method as set forth in claim 1 further characterized in that said purification is effected in the presence of oxygen.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-10-06 | 1990-04-07 | 1990-10-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-10-06 | 1994-04-07 | 1994-10-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-10-06 | 1998-04-07 | 1998-10-07 | $7700.00 | Window Closed / Lapsed |