Low consistency, one-part silicone elastomers
Assignee: Dow Silicones Corp
•
Filing: 1985-09-27
•
Granted: 1986-09-30
•
Expires: 2005-09-27
Abstract
Abstract A one-part silicone elastomeric composition that is flowable or easily extruded is prepared by mixing a hydroxyl endblocked polydiorganosiloxane, a difunctional silane having two amido radicals, and an organic peroxide suitable for vulcanizing silicone rubber. A nonacidic filler is optional. After being put in place, the composition is exposed to moisture to activate a chain extension reaction that increases the molecular weight of the polydiorganosiloxane, to improve the physical properties of the cured silicone elastomer. After chain extension has taken place, the composition is heated to activate the organic peroxide, thereby crosslinking the composition into a silicone elastomer. The composition is useful as a potting and encapsulating material.
Inventors
- 👤 Gary R. Homan
- 👤 Chi-Long Lee
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 11:41
CPC Classifications
C; C08; C08K; C08K9/00; C08K9/10; C08K13/00; C08K13/02; C08K5/00; C08K5/04; C08K5/14; C08K5/54; C08K5/541; C08K5/5425; C08K5/544; C08K5/5455; C08K5/5477; C08K5/549
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
211 words
A composition, stable in the absence of moisture, comprising a product obtained by mixing (A) 100 parts by weight of a hydroxyl endblocked polydiorganosiloxane where the organic radicals are monovalent radicals selected from the group consisting of methyl, vinyl, phenyl, and 3,3,3-trifluoropropyl radicals, the organic radicals being at least 50 mol percent methyl radicals, the viscosity of the polydiorganosiloxane being from 0.05 Pa.sup.. s to 100 Pa.sup.. s at 25° C. (B) a silane selected from the group consisting of a silane of the formula CH 3 RSiX 2 in which R is selected from the group consisting of methyl and vinyl radicals, X is a monovalent amido radical selected from the group consisting of ##STR5## where R' is a monovalent radical selected from the group consisting of an alkyl radical of from 1 to 4 carbon atoms per radical and phenyl radical and a silane of the formula ##STR6## in which X is as defined above, the silane being present in an amount sufficient to provide at least one mole of silane per mole of available hydroxyl radical in the composition, (C) from 0 to 150 parts by weight of nonacidic filler, and (D) from 0.1 to 8 parts by weight of an organic peroxide suitable for vulcanizing silicone rubber.
Claim 2
Dependent Claim
211 words
A composition, stable in the absence of moisture, comprising a product obtained by mixing (A) 100 parts by weight of a hydroxyl endblocked polydiorganosiloxane where the organic radicals are monovalent radicals selected from the group consisting of methyl, vinyl, phenyl, and 3,3,3-trifluoropropyl radicals, the organic radicals being at least 50 mol percent methyl radicals, the viscosity of the polydiorganosiloxane being from 0.05 Pa.sup.. s to 100 Pa.sup.. s at 25° C. (B) a silane selected from the group consisting of a silane of the formula CH 3 RSiX 2 in which R is selected from the group consisting of methyl and vinyl radicals, X is a monovalent amido radical selected from the group consisting of ##STR5## where R' is a monovalent radical selected from the group consisting of an alkyl radical of from 1 to 4 carbon atoms per radical and phenyl radical and a silane of the formula ##STR6## in which X is as defined above, the silane being present in an amount sufficient to provide at least one mole of silane per mole of available hydroxyl radical in the composition, (C) from 0 to 150 parts by weight of nonacidic filler, and (D) from 0.1 to 8 parts by weight of an organic peroxide suitable for vulcanizing silicone rubber.
Claim 3
Dependent Claim
21 words
The composition in accordance with claim 1 in which the polydiorganosiloxane is polydimethylsiloxane and the silane is of the formula ##STR7##
Claim 4
Dependent Claim
21 words
The composition in accordance with claim 1 in which the polydiorganosiloxane is polydimethylsiloxane and the silane is of the formula ##STR8##
Claim 5
Dependent Claim
13 words
The composition in accordance with claim 2 in which the silane is methylvinyldi(N-methylacetamido)silane.
Claim 6
Dependent Claim
13 words
The composition in accordance with claim 1 in which the silane is silacyclopentyl-di-epsilon-caprolactam.
Claim 7
Dependent Claim
21 words
The composition in accordance with claim 1, in which there is present from 5 to 100 parts of ground quartz filler.
Claim 8
Dependent Claim
21 words
The composition in accordance with claim 1, in which there is present from 5 to 50 parts of diatomaceous earth filler.
Claim 9
Dependent Claim
21 words
The composition in accordance with claim 1, in which there is present from 5 to 100 parts of calcium carbonate filler.
Claim 10
Dependent Claim
50 words
The composition in accordance with claim 4 in which the polydimethylsiloxane has a viscosity of from 0.1 Pa.sup.. s to 25 Pa.sup.. s at 25° C., the organic peroxide is vinyl specific, and there is from 5 to 50 parts of diatomaceous earth filler, the filler being treated with methylvinyldichlorosilane.
Claim 11
Dependent Claim
17 words
The composition in accordance with claim 4 in which there is also present resinous microcapsules containing water.
Claim 12
Independent Claim
254 words
A method of producing a cured silicone elastomer consisting essentially of (I) mixing under essentially anhydrous conditions (A) 100 parts by weight of a hydroxyl endblocked polydiorganosiloxane where the organic radicals are monovalent radicals selected from the group consisting of methyl, vinyl, phenyl, and 3,3,3-trifluoropropyl radicals, the organic radicals being at least 50 mol percent methyl radicals, the viscosity of the polydiorganosiloxane being from 0.05 Pa.sup.. s to 100 Pa.sup.. s at 25° C. (B) a silane selected from the group consisting of a silane of the formula CH 3 RSiX 2 in which R is selected from the group consisting of methyl and vinyl radicals, X is a monovalent amido radical selected from the group consisting of ##STR9## where R' is a monovalent radical selected from the group consisting of an alkyl radical of from 1 to 4 carbon atoms per radical and phenyl radical and a silane of the formula ##STR10## in which X is as defined above, the silane being present in an amount sufficient to provide at least one mole of silane per mole of available hydroxyl radical in the composition, (C) from 0 to 150 parts by weight of nonacidic filler, and (D) from 0.1 to 8 parts by weight of an organic peroxide suitable for vulcanizing silicone rubber to form a composition, (II) forming the composition, (III) exposing the formed composition to moisture sufficient to allow a chain extension reaction, then, (IV) heating to a temperature sufficient to activate the organic peroxide, to yield a cured silicone elastomer.
Claim 13
Independent Claim
254 words
A method of producing a cured silicone elastomer consisting essentially of (I) mixing under essentially anhydrous conditions (A) 100 parts by weight of a hydroxyl endblocked polydiorganosiloxane where the organic radicals are monovalent radicals selected from the group consisting of methyl, vinyl, phenyl, and 3,3,3-trifluoropropyl radicals, the organic radicals being at least 50 mol percent methyl radicals, the viscosity of the polydiorganosiloxane being from 0.05 Pa.sup.. s to 100 Pa.sup.. s at 25° C. (B) a silane selected from the group consisting of a silane of the formula CH 3 RSiX 2 in which R is selected from the group consisting of methyl and vinyl radicals, X is a monovalent amido radical selected from the group consisting of ##STR9## where R' is a monovalent radical selected from the group consisting of an alkyl radical of from 1 to 4 carbon atoms per radical and phenyl radical and a silane of the formula ##STR10## in which X is as defined above, the silane being present in an amount sufficient to provide at least one mole of silane per mole of available hydroxyl radical in the composition, (C) from 0 to 150 parts by weight of nonacidic filler, and (D) from 0.1 to 8 parts by weight of an organic peroxide suitable for vulcanizing silicone rubber to form a composition, (II) forming the composition, (III) exposing the formed composition to moisture sufficient to allow a chain extension reaction, then, (IV) heating to a temperature sufficient to activate the organic peroxide, to yield a cured silicone elastomer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-09-29 | 1990-03-31 | 1990-09-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-09-29 | 1994-03-31 | 1994-09-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-09-29 | 1998-03-31 | 1998-09-30 | $7700.00 | Window Closed / Lapsed |