Method for bonding metallic structural elements
Assignee: BBC Brown Boveri AG Switzerland
•
Filing: 1984-04-27
•
Granted: 1986-09-16
•
Expires: 2004-04-27
Abstract
Abstract Method for bonding metallic structural elements to form a component, in particular for stationary gas turbines, wherein at least one intermediate layer with a defined thickness is located between the structural elements and is heated together with the structural elements to a temperature which can be specified in advance, and pressure of a magnitude which can be specified in advance is exerted on the structural elements before or after this heating. The temperature and the pressure are maintained sufficiently long that isothermal solidification of the intermediate layer and/or of the alloying material of the structural elements is attained in the joint zone.
Inventors
- 👤 Bernd Jahnke
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 00:15
CPC Classifications
B; B23; B23P; B23P15/00; B23P15/04; B23K; B23K20/00; B23K20/16; B23K35/00; B23K35/001; B23K35/004
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
125 words
Method for bonding metallic structural elements to form a component, in particular for stationary gas turbines, which comprises locating at least one intermediate layer of nickel-chromium-boron with a thickness between 1 and 50 μm between the structural elements to be bonded, heating the intermediate layer together with the structural elements to a temperature of 1120° to 1230° C., exerting a pressure of 1 to 200 MPa before or after said heating on the structural elements together with the intermediate layer therebetween and maintaining the temperature and the pressure for a sufficient length of time to effect isothermal solidification of the intermediate layer and the alloying material of the structural elements in the joint zone with the formation of a strong bond between the structural elements.
Claim 2
Dependent Claim
125 words
Method for bonding metallic structural elements to form a component, in particular for stationary gas turbines, which comprises locating at least one intermediate layer of nickel-chromium-boron with a thickness between 1 and 50 μm between the structural elements to be bonded, heating the intermediate layer together with the structural elements to a temperature of 1120° to 1230° C., exerting a pressure of 1 to 200 MPa before or after said heating on the structural elements together with the intermediate layer therebetween and maintaining the temperature and the pressure for a sufficient length of time to effect isothermal solidification of the intermediate layer and the alloying material of the structural elements in the joint zone with the formation of a strong bond between the structural elements.
Claim 3
Dependent Claim
18 words
Method according to claim 1, wherein the intermediate layer has a melting point between 1050° and 1230° C.
Claim 4
Dependent Claim
18 words
Method according to claim 1, wherein the intermediate layer has a melting point between 1220° and 1230° C.
Claim 5
Dependent Claim
25 words
Method according to claim 1, wherein said pressure exerted on the structural elements together with the intermediate layer therebetween is between 10 and 100 MPa.
Claim 6
Dependent Claim
43 words
Method according to claim 1, wherein the intermediate layer is a member selected from the group consisting of an amorphous brazing foil, a brazing layer, a brazing powder and a powder to reduce the melting point of the material forming the structural elements.
Claim 7
Dependent Claim
13 words
Method according to claim 5, wherein the intermediate layer is a nickel-chromium-boron foil.
Claim 8
Dependent Claim
42 words
Method according to claim 1, wherein the structural elements formed of a cobalt base or nickel base alloy of the γ-γ' type are used for manufacturing the component and wherein the bonding of the structural elements is carried out in a vacuum.
Claim 9
Dependent Claim
78 words
Method according to claim 7, wherein structural elements are formed of an alloy which contains 5 to 24% chromium, 0 to 11% molybdenum, 0 to 2% niobium, 0 to 7% tantalum and niobium, 0 to 22% cobalt, 0 to 6% titanium, 0 to 7% aluminum, 0.01 to 0.05% carbon, 0.01 to 0.2% beryllium, 0 to 3% zirconium, 0 to 2% hafnium, 0 to 6% iron and 0 to 12% tungsten, referred to the total weight of the alloy.
Claim 10
Dependent Claim
17 words
Method according to claim 1, wherein the pressure is applied to the structural elements by pressing tools.
Claim 11
Dependent Claim
15 words
Method according to claim 1, wherein the pressure is applied to the structural elements isostatically.
Claim 12
Dependent Claim
88 words
Method for bonding metallic structural elements to form a component, in particular for stationary gas turbines, which comprises locating at least one intermediate layer of nickel-chromium-boron with a thickness of between 1 and 50 microns between the structural elements and subsequently heating to effect brazing for a short period in the joint zone at least until the attainment of brazing seam sealing, subsequently cooling the structural elements and the intermediate layer and then subjecting the joint region to isostatic post-pressing at a temperature between 1120° and 1220° C.
Claim 13
Dependent Claim
88 words
Method for bonding metallic structural elements to form a component, in particular for stationary gas turbines, which comprises locating at least one intermediate layer of nickel-chromium-boron with a thickness of between 1 and 50 microns between the structural elements and subsequently heating to effect brazing for a short period in the joint zone at least until the attainment of brazing seam sealing, subsequently cooling the structural elements and the intermediate layer and then subjecting the joint region to isostatic post-pressing at a temperature between 1120° and 1220° C.
Claim 14
Dependent Claim
16 words
Method according to claim 11, wherein the isostatic post-pressing temperature is between 1120° and 1220° C.
Claim 15
Dependent Claim
17 words
Method according to claim 11, wherein the isostatic post-pressing temperature is between 1180 ° and 1220° C.
Claim 16
Dependent Claim
43 words
Method according to claim 11, wherein the intermediate layer is a member selected from the group consisting of an amorphous brazing foil, a brazing layer, a brazing powder and a powder to reduce the melting point of the material forming the structural elements.
Claim 17
Dependent Claim
13 words
Method according to claim 14, wherein the intermediate layer is a nickel-chromium-boron foil.
Claim 18
Dependent Claim
41 words
Method according to claim 11, wherein the structural elements formed of a cobalt base of nickel base alloy of the γ-γ' type used for manufacturing the component and wherein the bonding of the structural elements is carried out in a vacuum.
Claim 19
Dependent Claim
78 words
Method according to claim 16, wherein structural elements are formed of an alloy which contains 5 to 24% chromium, 0 to 11% molybdenum, 0 to 2% niobium, 0 to 7% tantalum and niobium, 0 to 22% cobalt, 0 to 6% titanium, 0 to 7% aluminum, 0.01 to 0.05% carbon, 0.01 to 0.2% beryllium, 0 to 3% zirconium, 0 to 2% hafnium, 0 to 6% iron and 0 to 12% tungsten, referred to the total weight of the alloy.
Claim 20
Dependent Claim
17 words
Method according to claim 11, wherein the pressure is applied to the structural elements by pressing tools.
Claim 21
Dependent Claim
15 words
Method according to claim 11, wherein the pressure is applied to the structural elements isostatically.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-09-15 | 1990-03-17 | 1990-09-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-09-15 | 1994-03-17 | 1994-09-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-09-15 | 1998-03-17 | 1998-09-16 | $7700.00 | Window Closed / Lapsed |