Process for forming transparent aerogel insulating arrays
Assignee: THERMALUX HOLDINGS
•
Filing: 1985-09-04
•
Granted: 1986-09-09
•
Expires: 2005-09-04
Abstract
Abstract An improved supercritical drying process for forming transparent silica aerogel arrays is described. The process is of the type utilizing the steps of hydrolyzing and condensing aloxides to form alcogels. A subsequent step removes the alcohol to form aerogels. The improvement includes the additional step, after alcogels are formed, of substituting a solvent, such as CO2, for the alcohol in the alcogels, the solvent having a critical temperature less than the critical temperature of the alcohol. The resulting gels are dried at a supercritical temperature for the selected solvent, such as CO2, to thereby provide a transparent aerogel array within a substantially reduced (days-to-hours) time period. The supercritical drying occurs at about 40 DEG C. instead of at about 270 DEG C. The improved process provides increased yields of large scale, structurally sound arrays. The transparent aerogel array, formed in sheets or slabs, as made in accordance with the improved process, can replace the air gap within a double glazed window, for example, to provide a substantial reduction in heat transfer. The thus formed transparent aerogel arrays may also be utilized, for example, in windows of refrigerators and ovens, or in the walls and doors thereof or as the active material in detectors for analyzing high energy elementry particles or cosmic rays.
Inventors
- 👤 Param H. Tewari
- 👤 Arlon J. Hunt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 18:57
CPC Classifications
C; C01; C01B; C01B33/00; C01B33/113; C01B33/12; C01B33/14; C01B33/157; C01B33/158; C01B33/1585; B; B01; B01J; B01J13/00; B01J13/0091; C04; C04B; C04B38/00; C04B38/0045
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
91 words
In a drying process for forming transparent aerogel insulating arrays of the type utilizing the steps of hydrolyzing and condensing alkoxides to form alcogels, and subsequently removing the alcohol therefrom to form aerogels, the improvement comprising the additional step, after alcogels are formed, of substituting a solvent having a critical temperature less than the critical temperature of the alcohol for the alcohol in the alcogels, and drying the resulting gels at a supercritical temperature for the solvent, to thereby provide a transparent aerogel array within a substantially reduced drying time period.
Claim 2
Dependent Claim
91 words
In a drying process for forming transparent aerogel insulating arrays of the type utilizing the steps of hydrolyzing and condensing alkoxides to form alcogels, and subsequently removing the alcohol therefrom to form aerogels, the improvement comprising the additional step, after alcogels are formed, of substituting a solvent having a critical temperature less than the critical temperature of the alcohol for the alcohol in the alcogels, and drying the resulting gels at a supercritical temperature for the solvent, to thereby provide a transparent aerogel array within a substantially reduced drying time period.
Claim 3
Dependent Claim
27 words
The improvement of claim 1, wherein the step of substituting a solvent for the alcohol in the alcogels comprises replacing the alcohol with liquid CO 2 .
Claim 4
Dependent Claim
61 words
The improvement of claim 2, wherein the CO 2 is substituted by: placing the alcogels in a pressurizable chamber filled with alcohol, sealing the chamber and cooling same to a temperature below 40° C., repetitive directing pressurized CO 2 into the chamber causing purging of the alcohol, heating the thus purged gels under pressure to a temperature not greater than about
Claim 5
Dependent Claim
36 words
4° C. for a period of time, slowly venting the CO 2 from the chamber and slowly dropping the pressure in the chamber to atmospheric pressure to dry the gels, and removing the thus formed aerogels.
Claim 6
Dependent Claim
36 words
4° C. for a period of time, slowly venting the CO 2 from the chamber and slowly dropping the pressure in the chamber to atmospheric pressure to dry the gels, and removing the thus formed aerogels.
Claim 7
Dependent Claim
53 words
The improvement of claim 3, wherein the step of cooling the alcogels is carried out at a temperature of about 18° C., wherein the CO 2 is directed into the chamber at about 800 psi, and wherein the heating of the purged gels is carried out at a pressure of about 1200 psi.
Claim 8
Dependent Claim
67 words
The improvement of claim 1, wherein the step of substituting a solvent for the alcohol includes the step of selecting a solvent having a critical temperature less than the critical temperature of alcohol from the group consisting of carbon dioxide (CO 2 ), nitrous oxide (N 2 O), Freon 13 (CClF 3 ), Freon 23 (CHF 3 ), and Freon 116 2 (CF 3 -CF 3 ).
Claim 9
Independent Claim
74 words
A method for forming transparent silica aerogels for insulative applications comprising the steps of: using a base catalyzed hydrolysis and condensation of alkoxides to form alcogels, and removal of alcohol from the alcogels to achieve aerogels, which includes the substitution of the alcohol with a solvent having a critical temperature less than that of alcohol, and supercritically drying the gels at the solvent's supercritical temperature to produce silica aerogels having transparency, strength and stability.
Claim 10
Independent Claim
74 words
A method for forming transparent silica aerogels for insulative applications comprising the steps of: using a base catalyzed hydrolysis and condensation of alkoxides to form alcogels, and removal of alcohol from the alcogels to achieve aerogels, which includes the substitution of the alcohol with a solvent having a critical temperature less than that of alcohol, and supercritically drying the gels at the solvent's supercritical temperature to produce silica aerogels having transparency, strength and stability.
Claim 11
Dependent Claim
59 words
The method of claim 6, additionally including the steps of: mixing an alkoxide solution in alcohol, and a catalyst, pouring the mixture into a mold, gelling the mixture and aging the alcogel for a time period under alcohol, and removing the alcogels from the molds for subsequent substitution of the alcohol with a solvent and supercritically drying the gels.
Claim 12
Dependent Claim
33 words
The method of claim 7, wherein the alkosol solution is formed from Si(OC 2 H 5 ) 4 and H 2 O, and wherein the catalyst is selected from ammonia and ammonium fluoride.
Claim 13
Dependent Claim
47 words
The method of claim 6, wherein the step of removal of alcohol from the alcogels is carried out by substituting for the alcohol a solvent selected from the group consisting of carbon dioxide, nitrous oxide, Freon 13, Freon 23, Freon 116 2 , and Freon TF (113).
Claim 14
Dependent Claim
32 words
The method of claim 9, wherein the step of supercritically drying the gels is carried out at pressures not greater than about 1200 psi and temperatures not greater than about 40° C.
Claim 15
Dependent Claim
39 words
The method of claim 10, wherein the step of substituting solvent for the alcohol includes the step of: cooling the alcogels to a temperature of about 18° C. and repetitively purging the alcohol from the alcogels with the solvent.
Claim 16
Dependent Claim
23 words
The method of claim 11, wherein the alcohol is purged by a solvent of CO 2 at a pressure of about 800 psi.
Claim 17
Dependent Claim
84 words
The method of claim 12, wherein the repetitive purging of the alcohol by the CO 2 is over a time period of 2 to 3 hours, and wherein the supercritical drying of the gels at about 40° C. and pressure of about 1200 psi is maintained for a time period of about 30 minutes, and includes the steps of venting the CO 2 from the thus dried gels and reducing the pressure thereon to atmospheric, wherein the total drying time is about 6-10 hours.
Claim 18
Dependent Claim
88 words
In a process for forming transparent silica aerogels of the type utilizing the steps of hydrolyzing and condensing alkoxides to form alcogels, and subsequently removing the alcohol therefrom to form aerogels, the improvement comprising the steps of: substituting a selected solvent for the alcohol in the alcogels, the selected solvent having a critical temperature less than the critical temperature of the alcohol, and supercritically drying the resulting gels at temperatures and pressures above the critical point for the solvent, thereby providing silica aerogels having transparency, strength and stability.
Claim 19
Dependent Claim
88 words
In a process for forming transparent silica aerogels of the type utilizing the steps of hydrolyzing and condensing alkoxides to form alcogels, and subsequently removing the alcohol therefrom to form aerogels, the improvement comprising the steps of: substituting a selected solvent for the alcohol in the alcogels, the selected solvent having a critical temperature less than the critical temperature of the alcohol, and supercritically drying the resulting gels at temperatures and pressures above the critical point for the solvent, thereby providing silica aerogels having transparency, strength and stability.
Claim 20
Dependent Claim
148 words
The process of claim 14, wherein the improvement is carried out by: placing the alcogels in an enclosure which can be cooled and heated under pressure while maintaining the alcogels under alcohol to retain transparency, cooling the enclosure to a temperature of about 18° C., repetitively directing CO 2 at a pressure of about 800 psi into the enclosure to displace the alcohol in the enclosure and to purge the alcohol from the gels, periodically sampling the composition within the enclosure to determine the removal of the alcohol, heating the enclosure to a temperature of about 40° C. and increasing the pressure to about 1200 psi, maintaining the temperature and pressure in the enclosure for a time period of about 30 minutes, slowly venting the CO 2 from the enclosure and thereby reducing the pressure to atmospheric, and removing the thus formed transparent silica aerogel from the enclosure.
Claim 21
Dependent Claim
35 words
The method of claim 15, wherein the steps of venting the CO 2 and reducing the pressure in the enclosure is carried out over a time period in the range of 3 to 4 hours.
Claim 22
Dependent Claim
22 words
The method of claim 14, additionally including the step of treating the thus formed silica aerogels to protect same from adverse environments.
Claim 23
Dependent Claim
11 words
A transparent silica aerogel produced by the process of claim 14.
References Cited (Backward Citations)
US2631966A
Cited
US2927083A
Cited
US3672833A
Cited
US3652215A
Cited
US3977993A
Cited
US4402927A
Cited
US4432956A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-09-08 | 1990-03-10 | 1990-09-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-09-08 | 1994-03-10 | 1994-09-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-09-08 | 1998-03-10 | 1998-09-09 | $7700.00 | Window Closed / Lapsed |