Process for forming pattern with negative resist using quinone diazide compound
Assignee: Oki Electric Industry Co Ltd
•
Filing: 1984-03-27
•
Granted: 1986-09-02
•
Expires: 2004-03-27
Abstract
Abstract A process for forming patterns with a negative type resist which comprises the steps of forming a negative type resist film made of quinone diazide oligomer having a polymerization degree of 10 or less, such as a quinone diazide sulfonic ester on a substrate, irradiating the resist film selectively with far ultraviolet rays having a wavelength of 180-300 nm to expose the above film, and then developing the film thus exposed by the use of a suitable developer such as a solution containing any one of an acetic ester, an alkyl ketone and cyclohexanone, and another process wherein the above described exposing step is carried out in such a manner that the quinone diazide sulfonic ester film is subjected to blanket exposure by means of ultraviolet rays having a longer wavelength than 300 nm, and then the resist film, thus exposed, is further subjected to selective exposure by means of far ultraviolet rays of 300 nm or less.
Inventors
- 👤 Yoshio Yamashita
- 👤 Ryuji Kawazu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 09:54
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/004; G03F7/022
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
111 words
A process for forming patterns with a negative type resist consisting essentially of the steps of: forming, on a substrate, a negative type resist film made of a quinone diazide sulfonic ester of a novolak resin having a polymerization degree of 10 or less; selectively irradiating the thus-formed film with far ultraviolet rays having a wavelength of 180-300 nm to expose said film; heating the resist film on the substrate to a temperature of 50°-120° C. prior to development; and developing the film, thus exposed, by the use of a solution of an acetic ester, an alkyl ketone or cyclohexanone and, in addition, water or a mixture of water and alcohol.
Claim 2
Dependent Claim
111 words
A process for forming patterns with a negative type resist consisting essentially of the steps of: forming, on a substrate, a negative type resist film made of a quinone diazide sulfonic ester of a novolak resin having a polymerization degree of 10 or less; selectively irradiating the thus-formed film with far ultraviolet rays having a wavelength of 180-300 nm to expose said film; heating the resist film on the substrate to a temperature of 50°-120° C. prior to development; and developing the film, thus exposed, by the use of a solution of an acetic ester, an alkyl ketone or cyclohexanone and, in addition, water or a mixture of water and alcohol.
Claim 3
Dependent Claim
31 words
A process for forming patterns with a negative type resist as claimed in claim 1 wherein said developer is a solution containing any one of acetic ester, alkyl ketone and cyclohexanone.
Claim 4
Dependent Claim
34 words
A process for forming patterns with a negative type resist as claimed in claim 1 wherein said developer is a solution containing acetic ester or cyclohexanone and, in addition, water or water and alcohol.
Claim 5
Dependent Claim
77 words
A process for forming patterns with a negative type resist as claimed in claim 1 wherein said exposure comprises the steps of selectively exposing the resist film to far ultraviolet rays having a wavelength of 200-300 nm, and then exposing all the unexposed portions of said resist film, which have not yet been subjected to said selective exposure by means of said far ultraviolet rays, by means of ultraviolet rays having a wavelength longer than 300 nm.
Claim 6
Dependent Claim
135 words
A process for forming patterns with a negative type resist wherein a resist film formed on the surface of a substrate is exposed and said substrate with the resist film is heated to a temperature of 50°-120° C. and then developed in a solution of an acetic ester, an alkyl ketone or cyclohexanone and, in addition, water or a mixture of water and alcohol to form resist patterns, said exposure being carried out in such a manner that said resist film, made of a quinone diazide sulfonic ester novolak resin film, is subjected to blanket exposure by means of ultraviolet rays having a wavelength longer than 300 nm, and wherein the resist film, thus exposed, is further subjected to selective exposure by means of far ultraviolet rays having a wavelength of 300 nm or less.
Claim 7
Dependent Claim
135 words
A process for forming patterns with a negative type resist wherein a resist film formed on the surface of a substrate is exposed and said substrate with the resist film is heated to a temperature of 50°-120° C. and then developed in a solution of an acetic ester, an alkyl ketone or cyclohexanone and, in addition, water or a mixture of water and alcohol to form resist patterns, said exposure being carried out in such a manner that said resist film, made of a quinone diazide sulfonic ester novolak resin film, is subjected to blanket exposure by means of ultraviolet rays having a wavelength longer than 300 nm, and wherein the resist film, thus exposed, is further subjected to selective exposure by means of far ultraviolet rays having a wavelength of 300 nm or less.
References Cited (Backward Citations)
US3046120A
Cited
US3502470A
Cited
US3837860A
Cited
DE2461912A1
Cited
SU595694A1
Cited
US4211834A
Cited
EP0045639A2
Cited
US4395481A
Cited
US4499177A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-09-01 | 1990-03-03 | 1990-09-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-09-01 | 1994-03-03 | 1994-09-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-09-01 | 1998-03-03 | 1998-09-02 | $7700.00 | Window Closed / Lapsed |