Assignee: Mitsubishi Chemical Corp
•
Filing: 1985-05-14
•
Granted: 1986-09-02
•
Expires: 2005-05-14
Abstract
Abstract A process for producing a carbon fiber having a tenacity of 450 kg/mm2 or more, preferably 500 kg/mm2 or more, and a modulus of elasticity of 25 ton/mm2 or more which comprises subjecting a polyacrylonitrile-type fiber to a flame-resisting treatment in a flame-resisting treatment furnace provided with a plural number of driving rolls in an oxidizing atmosphere at 200 DEG to 400 DEG C. under application of multistep elongation, during said treatment the respective percentage of elongation in said multistep elongation being set respectively at a value which is equal to or within +/-3% of the value of the percentage of elongation En indicating an inflection point Pn obtainable from the load and the percentage of elongation determined in advance by experimental measurements, and then subjecting the treated fiber to carbonization.
Inventors
- 👤 Jinko Izumi
- 👤 Yoshitaka Imai
- 👤 Munetsugu Nakatani
- 👤 Yoshiteru Tanuku
- 👤 Naoyuki Fukahori
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 18:07
CPC Classifications
D; D01; D01F; D01F9/00; D01F9/08; D01F9/12; D01F9/14; D01F9/32; D01F9/20; D01F9/21; D01F9/22
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
105 words
A process for producing a carbon fiber which comprises subjecting a polyacrylonitrile-type polymer fiber to a flame-resisting treatment in a flame-resisting treatment furnace provided with a plural number of driving rolls in an oxidizing atmosphere at 200° to 400° C. under application of multistep elongation, during said treatment the respective percentage of elongation in each step the elongation being set respectively at a value which is equal to or within ±3% of the value of the precentage of elongation, En, indicating an inflection point, Pn, obtainable from a plot of the percentage of elongation versus the load, and then subjecting the treated fiber to carbonization.
Claim 2
Dependent Claim
105 words
A process for producing a carbon fiber which comprises subjecting a polyacrylonitrile-type polymer fiber to a flame-resisting treatment in a flame-resisting treatment furnace provided with a plural number of driving rolls in an oxidizing atmosphere at 200° to 400° C. under application of multistep elongation, during said treatment the respective percentage of elongation in each step the elongation being set respectively at a value which is equal to or within ±3% of the value of the precentage of elongation, En, indicating an inflection point, Pn, obtainable from a plot of the percentage of elongation versus the load, and then subjecting the treated fiber to carbonization.
Claim 3
Dependent Claim
29 words
A process for producing a carbon fiber according to claim 1, wherein the fiber subjected to the flame-resisting treatment has a density of 1.26 to 1.38 g/cm 3 .
Claim 4
Dependent Claim
89 words
A process for producing a carbon fiber according to claim 1, wherein the fiber subjected to the flame-resisting treatment is subjected to a heat treatment in an inert atmosphere under tension to attain a density of not less than 1.40 g/cm 3 and less than 1.57 g/cm 3 , then to another heat treatment in an inert atmosphere under tension to attain a density of 1.57 to 1.75 g/cm 3 , and further to a heat treatment in an inert atmosphere at a temperature not lower than 800° C.
Claim 5
Dependent Claim
99 words
A process for producing a carbon fiber according to claim 1, wherein the fiber subjected to the flame-resisting treatment is subjected in an inert atmosphere to a heat treatment at 300° to 800° C. and then to a heat treatment at a temperature not lower than 1000° C., in said former heat treatment the rate of temperature increase between 350° C. and 450° C. being within the range of 10° to 100° C./minute and an elongation not less than 3% and not more than 30% being applied to the fiber, in the temperature range of 350° to 450° C.
Claim 6
Dependent Claim
112 words
A process for producing a carbon fiber according to claim 1, wherein a polyacrylonitrile-type polymer fiber is subjected to a flame-resisting treatment which fiber has been prepared by spinning an acrylonitrile copolymer containing 80% by mole or more of acrylonitrile monomer unit to form an acrylic fiber precursor, then attaching to the precursor an aminosiloxane-type oil by impregnation so as to give a content of the oil of 0.01 to 0.5% by weight based on the weight of the fiber, and subjecting the resulting precursor to a washing treatment in cold or hot water at constant fiber length or while stretching the precursor at a draw ratio of not more than 1.8.
Claim 7
Dependent Claim
32 words
A process for producing a carbon fiber according to claim 1, wherein the residence time of the fiber between respective driving rolls in the multistep elongation is not more than 20 minutes.
References Cited (Backward Citations)
US3632798A
Cited
US3914960A
Cited
JPS49127121A
Cited
US3972984A
Cited
US4080417A
Cited
US4100004A
Cited
US4452860A
Cited
JPS54147222A
Cited
JPS59106522A
Cited
JPS59137512A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-09-01 | 1990-03-03 | 1990-09-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-09-01 | 1994-03-03 | 1994-09-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-09-01 | 1998-03-03 | 1998-09-02 | $7700.00 | Window Closed / Lapsed |