Method of making paper having improved tearing strength
Assignee: Brooks Rand Ltd
•
Filing: 1984-06-15
•
Granted: 1986-09-02
•
Expires: 2004-06-15
Abstract
Abstract The tearing strength of paper is improved by providing a furnish in which the fiber content is predominantly refined fiber with a minor amount, preferably 2 to 10 wt. %, of added unrefined fiber having incorporated therein a heat activatable bonding agent, particularly starch. The bonding agent adheres to and coats the added fiber without chemically reacting with the fiber. A cationic material, particularly polyethyleneimine, is premixed with the raw starch to cause it to adhere to the added fiber. During heat drying of the formed paper the starch is gelatinized to effect enhanced bonding of the added fiber.
Inventors
- 👤 Albert Brucato
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 23:01
CPC Classifications
D; D21; D21C; D21C9/00; D21C9/001; D21H; D21H11/00; D21H11/08; D21H17/00; D21H17/03; D21H17/05; D21H17/09; D21H17/20; D21H17/33; D21H17/34; D21H17/41; D21H17/42
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
285 words
A method of making paper having improved tearing strength by introducing fiber bonds of increased strength that are distributed non-uniformly on a microscale, said method comprising the steps of providing a first aqueous slurry of a refined cellulosic pulp comprising a principal fiber, providing a second aqueous slurry of a cellulosic pulp that comprises an added fiber and that is unrefined or that has a substantially lesser degree of refining than the pulp of said first slurry so that said added fiber is longer and stronger than said principal fiber, incorporating only in the second of said slurries a heat activatable fiber bonding agent that adheres to said added fiber to provide chemically unreacted fiber that is coated with said bonding agent, whereby said coated added fiber is capable of forming stronger bonds with the principal fiber or with itself than the principal fiber can form with itself, thereafter admixing a predetermined amount of said second slurry with a predetermined amount of said first slurry to provide a furnish in which the fiber content is predominantly said principal fiber with a minor amount of said added fiber coated with said bonding agent, and forming said furnish into a sheet and heat drying the sheet to activate said bonding agent and thereby effect enhanced bonding of said added fiber in the finished sheet, whereby said finished sheet comprises a relatively coarse network of said added fiber interposed within, and having bonds of increased strength with, a relatively fine network of said principal fiber, and said bonds of increased strength being distributed non-uniformly on a microscale, whereby a tearing stress applied to the sheet is dispersed by said added fiber around the moving point of tear propagation.
Claim 2
Independent Claim
285 words
A method of making paper having improved tearing strength by introducing fiber bonds of increased strength that are distributed non-uniformly on a microscale, said method comprising the steps of providing a first aqueous slurry of a refined cellulosic pulp comprising a principal fiber, providing a second aqueous slurry of a cellulosic pulp that comprises an added fiber and that is unrefined or that has a substantially lesser degree of refining than the pulp of said first slurry so that said added fiber is longer and stronger than said principal fiber, incorporating only in the second of said slurries a heat activatable fiber bonding agent that adheres to said added fiber to provide chemically unreacted fiber that is coated with said bonding agent, whereby said coated added fiber is capable of forming stronger bonds with the principal fiber or with itself than the principal fiber can form with itself, thereafter admixing a predetermined amount of said second slurry with a predetermined amount of said first slurry to provide a furnish in which the fiber content is predominantly said principal fiber with a minor amount of said added fiber coated with said bonding agent, and forming said furnish into a sheet and heat drying the sheet to activate said bonding agent and thereby effect enhanced bonding of said added fiber in the finished sheet, whereby said finished sheet comprises a relatively coarse network of said added fiber interposed within, and having bonds of increased strength with, a relatively fine network of said principal fiber, and said bonds of increased strength being distributed non-uniformly on a microscale, whereby a tearing stress applied to the sheet is dispersed by said added fiber around the moving point of tear propagation.
Claim 3
Dependent Claim
23 words
The process of claim 1 wherein said bonding agent is selected from the group consisting of uncooked starch and heat activatable resinous materials.
Claim 4
Dependent Claim
26 words
The process of claim 1 wherein said added fiber comprises from about 2% to about 10% by wt. of the total fiber content of said furnish.
Claim 5
Dependent Claim
32 words
The process of claim 1 wherein said bonding agent comprises uncooked starch that is admixed or coated with a cationic material capable of causing the starch to adhere to said added fiber.
Claim 6
Dependent Claim
11 words
The process of claim 4 wherein said cationic material comprises polyethyleneimine.
Claim 7
Dependent Claim
26 words
The process of claim 5 wherein a premixture is prepared by combining dry starch with aqueous polyethyleneimine and said premixture is added to said second slurry.
Claim 8
Dependent Claim
23 words
The process of claim 4 wherein the amount of starch is from about 20 to about 200% by wt. of said added fiber.
Claim 9
Dependent Claim
23 words
The process of claim 5 wherein the amount of polyethyleneimine is from about 0.01 to about 0.1% by wt. of said added fiber.
Claim 10
Dependent Claim
15 words
The process of claim 1 wherein said bonding agent comprises a heat activatable resinous material.
Claim 11
Dependent Claim
13 words
The process of claim 9 wherein said resinous material is in cationic form.
Claim 12
Dependent Claim
40 words
The process of claim 5 wherein the amount of starch is from about 20 to about 200% by wt. of said added fiber and the amount of polyethyleneimine is from 0.01 to about 0.1% by wt. of said added fiber.
Claim 13
Dependent Claim
29 words
The process of claim 1, wherein said bonding agent is admixed or coated with a cationic material capable of causing the bonding agent to adhere to said added fiber.
Claim 14
Dependent Claim
23 words
The process of claim 9 wherein said resinous material is selected from the group consisting of polyvinylchloride resins, acrylic resins, and polyurethane resins.
Claim 15
Dependent Claim
12 words
A paper sheet made in accordance with the method of claim 1.
Claim 16
Independent Claim
214 words
A method of making paper having improved tearing strength by introducing fiber bonds of increased strength that are distributed non-uniformly on a microscale, said method comprising the steps of providing a furnish comprising an aqueous slurry of cellulosic pulp in which the fiber content is predominantly a refined principal fiber with a minor amount of an added fiber, said added fiber being unrefined or substantially less refined than said principal fiber whereby said added fiber is longer and stronger than said principal fiber, and only said added fiber being precoated with a heat activatable fiber bonding agent so that said added fiber is capable of forming stronger bonds with the principal fiber or with itself than the principal fiber can form with itself, and forming said furnish into a sheet and heat drying to activate said bonding agent and thereby effect enhanced bonding of said added fiber in the finished sheet, whereby said finished sheet comprises a relatively coarse network of said added fiber interposed within, and having bonds of increased strength with, a relatively fine network of said principal fiber, and said bonds of increased strength being distributed non-uniformly on a microscale, whereby a tearing stress applied to the sheet is dispersed by said added fiber around the moving point of tear propagation.
Claim 17
Independent Claim
214 words
A method of making paper having improved tearing strength by introducing fiber bonds of increased strength that are distributed non-uniformly on a microscale, said method comprising the steps of providing a furnish comprising an aqueous slurry of cellulosic pulp in which the fiber content is predominantly a refined principal fiber with a minor amount of an added fiber, said added fiber being unrefined or substantially less refined than said principal fiber whereby said added fiber is longer and stronger than said principal fiber, and only said added fiber being precoated with a heat activatable fiber bonding agent so that said added fiber is capable of forming stronger bonds with the principal fiber or with itself than the principal fiber can form with itself, and forming said furnish into a sheet and heat drying to activate said bonding agent and thereby effect enhanced bonding of said added fiber in the finished sheet, whereby said finished sheet comprises a relatively coarse network of said added fiber interposed within, and having bonds of increased strength with, a relatively fine network of said principal fiber, and said bonds of increased strength being distributed non-uniformly on a microscale, whereby a tearing stress applied to the sheet is dispersed by said added fiber around the moving point of tear propagation.
Claim 18
Dependent Claim
23 words
The process of claim 15 wherein said bonding agent is selected from the group consisting of uncooked starch and heat activatable resinous materials.
Claim 19
Dependent Claim
29 words
The process of claim 15 wherein said bonding agent is admixed or coated with a cationic material capable of causing the bonding agent to adhere to said added fiber.
Claim 20
Dependent Claim
26 words
The process of claim 15 wherein said added fiber comprises from about 2% to about 10% by wt. of the total fiber content of said furnish.
Claim 21
Dependent Claim
32 words
The process of claim 15 wherein said bonding agent comprises uncooked starch that is admixed or coated with a cationic material capable of causing the starch to adhere to said added fiber.
Claim 22
Dependent Claim
11 words
The process of claim 19 wherein said cationic material comprises polyethyleneimine.
Claim 23
Dependent Claim
27 words
The process of claim 20 wherein a premixture is prepared by combining dry starch with aqueous polyethyleneimine and said premixture is used to precoat said added fiber.
Claim 24
Dependent Claim
23 words
The process of claim 19 wherein the amount of starch is from about 20 to about 200% by wt. of said added fiber.
Claim 25
Dependent Claim
23 words
The process of claim 20 wherein the amount of polyethyleneimine is from about 0.01 to about 0.1% by wt. of said added fiber.
Claim 26
Dependent Claim
40 words
The processes of claim 19 wherein the amount of starch is from about 20 to about 200% by wt. of said added fiber and the amount of polyethyleneimine is from 0.01 to about 0.1% by wt. of said added fiber.
Claim 27
Dependent Claim
15 words
The process of claim 15 wherein said bonding agent comprises a heat activatable resinous material.
Claim 28
Dependent Claim
13 words
The process of claim 25 wherein said resinous material is in cationic form.
Claim 29
Dependent Claim
23 words
The process of claim 25 wherein said resinous material is selected from the group consisting of polyvinylchloride resins, acrylic resins, and polyurethane resins.
Claim 30
Dependent Claim
12 words
A paper sheet made in accordance with the method of claim 15.
References Cited (Backward Citations)
US2765229A
Cited
GB764147A
Cited
US2998344A
Cited
US3151017A
Cited
US3194727A
Cited
US3325346A
Cited
US3436305A
Cited
US4309247A
Cited
US4210488A
Cited
US4269657A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-09-01 | 1990-03-03 | 1990-09-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-09-01 | 1994-03-03 | 1994-09-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-09-01 | 1998-03-03 | 1998-09-02 | $7700.00 | Window Closed / Lapsed |