US4606813A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Fluid catalytic cracking catalyst for cracking sulfur containing petroleum feedstocks and a process for using it
Assignee: BASF Catalysts LLC
•
Filing: 1985-05-03
•
Granted: 1986-08-19
•
Expires: 2005-05-03
Abstract
Abstract The present invention is directed to a fluid catalytic cracking catalyst comprising a blend of a catalytically active first component and a second component for reducing the emissions of oxides of sulfur from the regenerator of a catalytic cracking unit and the use of that catalyst to crack sulfur containing petroleum feedstocks. The catalytically active first component contains Y-faujasite zeolite and comprises about 10-70% by weight, preferably about 25-50% by weight, of the catalyst. The second component of the catalyst comprises about 30-90% by weight, preferably about 50-75% by weight, of the catalyst. The second component comprises fluidizable particles containing at least about 70% by weight, preferably at least about 90% by weight, alumina and having an equilibrium surface area in the range of about 40-100 m2/g., preferably in the range of about 50-90 m2/g.
Inventors
- 👤 John W. Byrne
- 👤 Barry K. Speronello
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 23:14
CPC Classifications
C; C10; C10G; C10G11/00; C10G11/02; C10G11/04; C10G11/05; B; B01; B01J; B01J29/00; B01J29/04; B01J29/06; B01J29/08; B01J29/084; B01J35/00; B01J35/30; B01J35/34; B01J35/38; B01J35/70
Claims Analysis
Total Claims: 41
Claim 1
Independent Claim
86 words
A fluid catalytic cracking catalyst comprising a blend of a catalytically active first component and a second component for reducing the emissions of oxides of sulfur from the regenerator of a fluid catalytic cracking unit, said catalyst comprising: (a) about 10-70% by weight of fluidizable particles comprising at least about 40% by weight Y-faujasite; and (b) about 30-90% by weight of fluidizable particles comprising at least about 70% by weight alumina and having an equilibrium surface area in the range of about 40-100 m 2 /g.
Claim 2
Dependent Claim
86 words
A fluid catalytic cracking catalyst comprising a blend of a catalytically active first component and a second component for reducing the emissions of oxides of sulfur from the regenerator of a fluid catalytic cracking unit, said catalyst comprising: (a) about 10-70% by weight of fluidizable particles comprising at least about 40% by weight Y-faujasite; and (b) about 30-90% by weight of fluidizable particles comprising at least about 70% by weight alumina and having an equilibrium surface area in the range of about 40-100 m 2 /g.
Claim 3
Dependent Claim
19 words
The fluid catalytic cracking catalyst of claim 1 wherein component (b) comprises at least about 90% by weight alumina.
Claim 4
Dependent Claim
26 words
The fluid catalytic cracking catalyst of claim 2 wherein the equilibrium surface area of component (b) is in the range of about 50-90 m 2 /g.
Claim 5
Dependent Claim
27 words
The fluid catalytic cracking catalyst of claim 2 wherein the catalyst comprises about 25-50% by weight of component (a) and about 50-75% by weight of component (b).
Claim 6
Dependent Claim
25 words
The fluid catalytic cracking catalyst of claim 2 wherein component (a) has a deactivated activity at least about 1.5 times that of standard commercial catalyst.
Claim 7
Dependent Claim
25 words
The fluid catalytic cracking catalyst of claim 5 wherein component (a) has a deactivated activity at least about 2.0 times that of standard commercial catalyst.
Claim 8
Dependent Claim
19 words
The fluid catalytic cracking catalyst of claim 6 wherein component (a) comprises microspheres comprising about 50-70% by weight Y-faujasite.
Claim 9
Dependent Claim
16 words
The fluid catalytic cracking catalyst of claim 2 wherein component (b) comprises attrition resistant rehydrated alumina.
Claim 10
Dependent Claim
20 words
The fluid catalytic cracking catalyst of claim 2 wherein component (b) comprises attrition resistant calcined alumina made from rehydrated alumina.
Claim 11
Dependent Claim
16 words
The fluid catalytic cracking catalyst of claim 3 wherein component (b) comprises attrition resistant rehydrated alumina.
Claim 12
Dependent Claim
20 words
The fluid catalytic cracking catalyst of claim 3 wherein component (b) comprises attrition resistant calcined alumina made from rehydrated alumina.
Claim 13
Dependent Claim
38 words
The fluid catalytic cracking catalyst of claim 2 wherein component (b) comprises a compound of a metal selected from the group consisting of cerium, lanthanum, neodymium, praseodymium, samarium, dysprosium, platinum, ruthenium, rhodium, palladium, osmium, iridium and mixtures thereof.
Claim 14
Dependent Claim
19 words
The fluid catalytic cracking catalyst of claim 12 wherein the compound of a metal comprises a compound of cerium.
Claim 15
Dependent Claim
18 words
The fluid catalytic cracking catalyst of claim 13 wherein component (b) comprises about 1-4% by weight of cerium.
Claim 16
Dependent Claim
95 words
A fluid catalytic cracking catalyst comprising a blend of a catalytically active first component and a second component for reducing the emissions of oxides of sulfur from the regenerator of a fluid catalytic cracking unit, said catalyst comprising: (a) about 10-70% by weight of fluidizable particles comprising Y-faujasite and having a deactivated activity at least about 1.5 times that of standard commercial catalyst; and (b) about 30-90% by weight of fluidizable particles comprising at least about 70% by weight alumina and having an equilibrium surface area in the range of about 40-100 m 2 /g.
Claim 17
Dependent Claim
95 words
A fluid catalytic cracking catalyst comprising a blend of a catalytically active first component and a second component for reducing the emissions of oxides of sulfur from the regenerator of a fluid catalytic cracking unit, said catalyst comprising: (a) about 10-70% by weight of fluidizable particles comprising Y-faujasite and having a deactivated activity at least about 1.5 times that of standard commercial catalyst; and (b) about 30-90% by weight of fluidizable particles comprising at least about 70% by weight alumina and having an equilibrium surface area in the range of about 40-100 m 2 /g.
Claim 18
Dependent Claim
19 words
The fluid catalytic cracking catalyst of claim 15 wherein component (b) comprises at least about 90% by weight alumina.
Claim 19
Dependent Claim
26 words
The fluid catalytic cracking catalyst of claim 16 wherein the equilibrium surface area of component (b) is in the range of about 50-90 m 2 /g.
Claim 20
Dependent Claim
27 words
The fluid catalytic cracking catalyst of claim 16 wherein the catalyst comprises about 25-50% by weight of component (a) and about 50-75% by weight of component (b).
Claim 21
Dependent Claim
25 words
The fluid catalytic cracking catalyst of claim 16 wherein component (a) has a deactivated activity at least about 2.0 times that of standard commercial catalyst.
Claim 22
Dependent Claim
19 words
The fluid catalytic cracking catalyst of claim 16 wherein component (a) comprises microspheres comprising about 50-70% by weight Y-faujasite.
Claim 23
Dependent Claim
16 words
The fluid catalytic cracking catalyst of claim 16 wherein component (b) comprises attrition resistant rehydrated alumina.
Claim 24
Dependent Claim
20 words
The fluid catalytic cracking catalyst of claim 16 wherein component (b) comprises attrition resistant calcined alumina made from rehydrated alumina.
Claim 25
Dependent Claim
16 words
The fluid catalytic cracking catalyst of claim 17 wherein component (b) comprises attrition resistant rehydrated alumina.
Claim 26
Dependent Claim
20 words
The fluid catalytic cracking catalyst of claim 17 wherein component (b) comprises attrition resistant calcined alumina made from rehydrated alumina.
Claim 27
Dependent Claim
38 words
The fluid catalytic cracking catalyst of claim 16 wherein component (b) comprises a compound of a metal selected from the group consisting of cerium, lanthanum neodymium, praseodymium, samarium, dysprosium, platinum, ruthenium, rhodium, palladium, osmium, iridium and mixtures thereof.
Claim 28
Dependent Claim
19 words
The fluid catalytic cracking catalyst of claim 25 wherein the compound of a metal comprises a compound of cerium.
Claim 29
Dependent Claim
18 words
The fluid catalytic cracking catalyst of claim 26 wherein component (b) comprises about 1-4% by weight of cerium.
Claim 30
Dependent Claim
25 words
A process for cracking a sulfur containing petroleum feedstock comprising cracking the feedstock in the presence of the fluid catalytic cracking catalyst of claim 1.
Claim 31
Dependent Claim
25 words
A process for cracking a sulfur containing petroleum feedstock comprising cracking the feedstock in the presence of the fluid catalytic cracking catalyst of claim 3.
Claim 32
Dependent Claim
25 words
A process for cracking a sulfur containing petroleum feedstock comprising cracking the feedstock in the presence of the fluid catalytic cracking catalyst of claim 18.
Claim 33
Dependent Claim
24 words
A process for cracking a sulfur containing petroleum feedstock comprising cracking the feedstock in the presence of the catalytic cracking catalyst of claim 17.
Claim 34
Dependent Claim
100 words
The fluid catalytic cracking catalyst of claim 1 wherein the fluidizable particles comprising at least about 40% by weight Y-faujasite have less than about 0.20 cc/g. of pores having diameters in the range of 20-100Å and have the following characteristics: (a) a deactivated activity at least about 1.5 times that of standard commercial catalyst; (b) a severely deactivated activity at least about 1.5 times that of standard commercial catalyst; (c) a coke yield no greater than about that of standard commercial catalyst at 70% conversion; and (d) an EAI no more than about 5.0 times that of standard commercial catalyst.
Claim 35
Dependent Claim
68 words
The fluid catalytic cracking catalyst of claim 32 wherein the fluidizable particles comprising at least about 40% by weight Y-faujasite have the following characteristics: (a) a deactivated activity at least about 2.0 times that of standard commercial catalyst; (b) a severely deactivated activity at least about 2.0 times that of standard commercial catalyst; and (c) an EAI no more than about 3.0 times that of standard commercial catalyst.
Claim 36
Dependent Claim
60 words
The fluid catalytic cracking catalyst of claim 32 wherein the fluidizable particles comprising at least about 40% by weight Y-faujasite contain a non-zeolitic component comprising the zeolite crystallization process residue of calcined clay, said calcined clay comprising about 30-60% by weight metakaolin and about 40-70% by weight kaolin clay that had been calcined at least substantially through its characteristic exotherm.
Claim 37
Dependent Claim
163 words
The fluid catalytic cracking catalyst of claim 1 wherein the fluidizable particles comprising at least about 40% by weight Y-faujasite contain less than about 0.7% by weight Na 2 O, more than about 4% by weight REO, and have a SiO 2 /Al 2 O 3 molar ratio of about 1.7-3.4, less than about 0.20 cc/g. of pores having diameters in the range of 20-100∪ less than about 0.30 cc/g. of pores having diameters in the range of 600-20,000Å, a surface area of about 300-750m 2 /g. and a bulk density of the 200/270 mesh fraction of about 0.8-1.2 g./cc., the Y-faujasite containing particles comprising: (a) a non-zeolitic component comprising the zeolite crystallization process residue of calcined clay, said calcined clay comprising about 30-60% by weight metakaolin and about 40-70% by weight kaolin clay that had been calcined at least substantially through its characteristic exotherm; and (b) Y-faujasite having, in the sodium form, a crystalline unit cell size of less than about 24.73Å.
Claim 38
Dependent Claim
88 words
The fluid catalytic cracking catalyst of claim 15 wherein the fluidizable particles comprising Y-faujasite contain at least about 40% by weight Y-faujasite, have less than about 0.20 cc/g of pores having diameters in the range of 20-100Å, and have the following characteristics: (a) a severely deactivated activity at least about 1.5 times that of standard commercial catalyst; (b) a coke yield no greater than about that of standard commercial catalyst at 70% conversion; and (c) an EAI no more than about 5.0 times that of standard commercial catalyst.
Claim 39
Dependent Claim
62 words
The fluid catalytic cracking catalyst of claim 36 wherein the fluidizable particles comprising Y-faujasite have the following characteristics: (a) a deactivated activity at least about 2.0 times that of standard commercial catalyst; (b) a severely deactivated activity at least about 2.0 times that of standard commercial catalyst; and (c) an EAI no more than about 3.0 times that of standard commercial catalyst.
Claim 40
Dependent Claim
54 words
The fluid catalytic cracking catalyst of claim 36 wherein the fluidizable particles comprising Y-faujasite contain a non-zeolitic component comprising the zeolite crystallization process residue of calcined clay, said calcined clay comprising about 30-60% by weight metakaolin and about 40-70% by weight kaolin clay that had been calcined at least substantially through its characteristic exotherm.
Claim 41
Dependent Claim
164 words
The fluid catalytic cracking catalyst of claim 19 wherein the fluidizable particles comprising Y-faujasite contain more than about 40% by weight Y-faujasite, less than about 0.7% by weight Na 2 O, more than about 4% by weight REO, and have a SiO 2 /Al 2 O 3 molar ratio of about 1.7-3.4, less than about 0.20 cc/g. of pores having diameters in the range of 20-100Å, less than about 0.30 cc/g. of pores having diameters in the range of 600-20,000Å, a surface area of about 300-750m 2 /g. and a bulk density of the 200/270 mesh fraction of about 0.8-1.2 g./cc., the Y-faujasite containing particles comprising: (a) a non-zeolitic component comprising the zeolite crystallization process residue of calcined clay, said calcined clay comprising about 30-60% by weight metakaolin and about 40-70% by weight kaolin clay that had been calcined at least substantially through its characteristic exotherm; and (b) Y-faujasite having, in the sodium form, a crystalline unit cell size of less than about 24.73Å.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-08-18 | 1990-02-17 | 1990-08-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-08-18 | 1994-02-17 | 1994-08-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-08-18 | 1998-02-17 | 1998-08-19 | $7700.00 | Window Closed / Lapsed |