US4604273A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for the growth of alpha silicon nitride whiskers
Assignee: Osram Sylvania Inc
•
Filing: 1985-04-19
•
Granted: 1986-08-05
•
Expires: 2005-04-19
Abstract
Abstract A process for the growth of silicon nitride whiskers consists of reacting a mixture of carbon and silicon dioxide powders at elevated temperature in a stream of nitrogen, said reaction mixture containing small amounts of metals such as chromium, magnesium, and nickel which promote the growth of silicon nitride whiskers by vapor phase transport. The whiskers obtained as a result of this invention are of much higher purity than those obtained by prior art.
Inventors
- 👤 Gary Czupryna
- 👤 Samuel Natansohn
- 👤 Robert A. Long
- 👤 Robin W. Munn
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 05:25
CPC Classifications
C; C30; C30B; C30B25/00; C30B25/005; C30B29/00; C30B29/10; C30B29/38
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
145 words
A method of making silicon nitride whiskers having a purity greater than 99.9% comprising the steps: Step 1--mixing from about 0.5 to about 10 parts of carbon with one part silicon dioxide forming a mixture; Step 2--adding from about 0.001 to about 0.5 weight percent of a whisker forming additive to the mixture from step 1, said whisker forming additive being selected from the group consisting of the metal, oxide, salt of chromium, nickel, magnesium, and combinations thereof, said salt being convertible to an oxide by heating; Step 3--heating the produce from step 2 in a graphite container from about 1400° C. to about 1550° C. for about 2 to about 12 hours in a flowing nitrogen atmosphere at about 0.5 to about 5 cm/sec to form whiskers of alpha silicon nitride having an aspect ratio greater than 10 and a purity greater than 99.9%.
Claim 2
Independent Claim
145 words
A method of making silicon nitride whiskers having a purity greater than 99.9% comprising the steps: Step 1--mixing from about 0.5 to about 10 parts of carbon with one part silicon dioxide forming a mixture; Step 2--adding from about 0.001 to about 0.5 weight percent of a whisker forming additive to the mixture from step 1, said whisker forming additive being selected from the group consisting of the metal, oxide, salt of chromium, nickel, magnesium, and combinations thereof, said salt being convertible to an oxide by heating; Step 3--heating the produce from step 2 in a graphite container from about 1400° C. to about 1550° C. for about 2 to about 12 hours in a flowing nitrogen atmosphere at about 0.5 to about 5 cm/sec to form whiskers of alpha silicon nitride having an aspect ratio greater than 10 and a purity greater than 99.9%.
Claim 3
Dependent Claim
37 words
A method of making silicon nitride whiskers in accordance with claim 1 wherein said step 2 comprises adding from about 0.005 to about 0.05 weight percent of a whisker forming additive to the mixture from step 1.
Claim 4
Dependent Claim
36 words
A method of making silicon nitride whiskers in accordance with claim 1 wherein said step 1 comprises mixing from about 1 to about 4 parts of carbon with one part of silicon dioxide forming a mixture.
Claim 5
Dependent Claim
32 words
A method of making silicon nitride whiskers in accordance with claim 1 wherein said step 1 comprises mixing about 2 parts of carbon with one part of silicon dioxide forming a mixture.
Claim 6
Dependent Claim
33 words
A method of making silicon nitride whiskers in accordance with claim 1 wherein said whiskers forming additive being selected from the group consisting of the metals of chromium, nickel, magnesium, and combinations thereof.
References Cited (Backward Citations)
GB1028977A
Cited
US3244480A
Cited
US4117095A
Cited
US4017319A
Cited
US4122152A
Cited
US4122140A
Cited
US4368180A
Cited
US4388255A
Cited
EP0080050A1
Cited
JPS59152271A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-08-04 | 1990-02-03 | 1990-08-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-08-04 | 1994-02-03 | 1994-08-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-08-04 | 1998-02-03 | 1998-08-05 | $7700.00 | Window Closed / Lapsed |