Method for producing pre-shaped α-silicon nitride whisker compacts and loose whiskers for composite material reinforcement
Assignee: Boeing Aerospace Co
•
Filing: 1981-03-27
•
Granted: 1983-06-14
•
Expires: 2001-03-27
Abstract
Abstract Method for producing α-silicon nitride whiskers. Silicon is blended with composition particles able to sublime without leaving a residue, such as naphthalene particles. The blend is compacted to a desired shape, after which the composition particles are sublimed from the blend to form a porous silicon precursor compact having the desired shape. The silicon precursor is reacted with a substance that releases free nitrogen, such as nitrogen or dry ammonia. The reaction is carried out at a temperature sufficiently high to form an identically shaped porous compact of α-silicon nitride whiskers but sufficiently low to avoid subliming substantially all of the formed whiskers. Preferably, the reaction is carried out in a range between about 2100° F. and 2750° F. The shaped porous compact of α-silicon nitride whiskers may be impregnated with a resin binder, a liquid metal, a colloidal suspension, an ionic solution or a gaseous material to form an isotropic composite. Alternatively, the compact of α-silicon nitride whiskers formed by the method described above may be broken down by crushing or grinding to form individual whiskers. Preferably, silicon particles in powder form are mixed with about 5 to 20 weight percent of composition particles, such as naphthalene particles, and treated so that the silicon particles are coated by the composition particles. The coated silicon particles are blended with more of the composition particles, followed by the steps outlined above to produce a loose compact of α-silicon nitride whiskers. A loose compact so produced breaks down more easily into individual whiskers, which whiskers can be added as reinforcement to metal, ceramic or resin molding powders and then formed by conventional methods, such as compacting, to produce composite parts in which α-silicon nitride is the reinforcing phase.
Inventors
- 👤 Frederick H. Simpson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 21:54
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/71; C04B35/78; C04B35/80; C04B35/01; C04B35/10; C04B35/111; C04B35/117; C04B35/14; C04B35/515; C04B35/52; C04B35/58; C04B35/581; C04B35/622; C04B35/62227; C04B35/62272; C04B35/62286; C04B35/62295; C04B35/626; C04B35/62605; C04B35/62645; C04B35/6268; C04B35/63; C04B35/6303; C04B35/6316; C04B35/64; C04B35/645; C30; C30B; C30B25/00; C30B25/005; C30B29/00; C30B29/10; C30B29/38; C04B2235/00; C04B2235/02; C04B2235/30; C04B2235/34; C04B2235/3409; C04B2235/42; C04B2235/428; C04B2235/46; C04B2235/465; C04B2235/50; C04B2235/52; C04B2235/5208; C04B2235/5216; C04B2235/524; C04B2235/5268; C04B2235/5276; C04B2235/54; C04B2235/5418; C04B2235/5436; C04B2235/60; C04B2235/604; C04B2235/616; C04B2235/70; C04B2235/96; C04B2235/9607; C04B2235/9623; C04B38/00; C04B38/0051; C04B38/0058
Claims Analysis
Total Claims: 43
Claim 1
Independent Claim
108 words
A method for producing a pre-shaped compact of α-silicon nitride whiskers comprising the steps of: (a) blending silicon particles with fugitive composition particles able to sublime without leaving a residue; (b) compacting the blend to a desired shape; (c) subliming and fugitive composition particles from said compacted shape to form a porous silicon precursor compact having said desired shape; (d) reacting said shaped silicon compact with a substance that releases free nitrogen, said reaction occurring at a temperature sufficiently high to convert said shaped silicon compact to an identically shaped porous compact of α-silicon nitride whiskers but sufficiently low to avoid subliming substantially all of said formed whiskers.
Claim 2
Independent Claim
108 words
A method for producing a pre-shaped compact of α-silicon nitride whiskers comprising the steps of: (a) blending silicon particles with fugitive composition particles able to sublime without leaving a residue; (b) compacting the blend to a desired shape; (c) subliming and fugitive composition particles from said compacted shape to form a porous silicon precursor compact having said desired shape; (d) reacting said shaped silicon compact with a substance that releases free nitrogen, said reaction occurring at a temperature sufficiently high to convert said shaped silicon compact to an identically shaped porous compact of α-silicon nitride whiskers but sufficiently low to avoid subliming substantially all of said formed whiskers.
Claim 3
Dependent Claim
74 words
The method of claim 1 wherein said composition particles are selected from the group consisting of napthalene, camphor and carbon dioxide; wherein said substance is selected from the group consisting of nitrogen, dry ammonia, a mixture of hydrogen and dry ammonia, a mixture of nitrogen and dry ammonia, mixture of hydrogen and nitrogen, and a mixture of nitrogen, dry ammonia and hydrogen; and wherein said temperature ranges between about 2100° F. and 2750° F.
Claim 4
Dependent Claim
16 words
The method of claim 2 wherein said temperature ranges between about 2550° F. and 2600° F.
Claim 5
Dependent Claim
35 words
The method of claim 2 wherein said composition particles are form about 100 to 10,000 times larger than said silicon particles and wherein said compacting step utilizes pressures ranging from about 1,000 to 30,000 psi.
Claim 6
Dependent Claim
26 words
The method of claim 2 wherein said substance and said silicon compact are reacted for a paired of time ranging from about 1 to 48 hours.
Claim 7
Dependent Claim
38 words
The method of claim 2 wherein said composition particles are naphthalene and wherein said substance is nitrogen containing from about 1 to 10 volume percent of a chemical selected from the group consisting of hydrogen and dry ammonia.
Claim 8
Dependent Claim
23 words
The method of claim 6 wherein said subliming is accomplished by baking said blend at a temperature below the melting point of naphthalene.
Claim 9
Dependent Claim
12 words
The method of claim 7 wherein said baking occurs in a vacuum.
Claim 10
Dependent Claim
37 words
The method of claim 6 wherein said silicon particles range from about 2 to 6 microns (equivalent diameter) in size and further wherein said naphthalene particles range from about 0.20 to 0.60 mm. (equivalent diameter) in size.
Claim 11
Dependent Claim
14 words
The method of claim 6 wherein said silicon particles are blended in powder form.
Claim 12
Dependent Claim
13 words
The method of claim 2 wherein said compacting is accomplished by die pressing.
Claim 13
Dependent Claim
13 words
The method of claim 2 wherein said compacting is accomplished by hydrostatic pressing.
Claim 14
Dependent Claim
14 words
The method of claim 2 wherein said blend is compacted into a shaped part.
Claim 15
Dependent Claim
22 words
The method of claim 2 further including the step of converting said compact of silicon nitride whiskers into individual α-silicon nitride whiskers.
Claim 16
Dependent Claim
20 words
The method of claim 2 wherein about 25% to 90% by weight silicon particles are blended with said composition particles.
Claim 17
Dependent Claim
20 words
The method of claim 15 wherein about 25% to 60% by weight silicon particles are blended with said composition particles.
Claim 18
Independent Claim
154 words
A method for producing isotropic composites reinforced by α-silicon nitride whiskers comprising the steps of: (a) blending silicon particles with fugitive composition particles able to sublime without leaving a residue; (b) compacting the blend to a desired shape; (c) subliming said fugitive composition particles from said compacted shape to form a porous silicon precursor compact having said desire shape; (d) reacting said shaped silicon compact with a substance that releases free nitrogen, said reaction occurring at a temperature sufficiently high to convert said compact to an identically shaped porous compact of α-silicon nitride whiskers but sufficiently low to avoid subliming substantially all of said formed whiskers; and (e) impregnating said shaped porous compact of α-silicon nitride whiskers with a material selected from the group consisting of a resin binder, a liquid metal, a colloidal suspension, an ionic solution and at least one gaseous material to form an isotropic composite reinforced by α-silicon nitride whiskers.
Claim 19
Independent Claim
154 words
A method for producing isotropic composites reinforced by α-silicon nitride whiskers comprising the steps of: (a) blending silicon particles with fugitive composition particles able to sublime without leaving a residue; (b) compacting the blend to a desired shape; (c) subliming said fugitive composition particles from said compacted shape to form a porous silicon precursor compact having said desire shape; (d) reacting said shaped silicon compact with a substance that releases free nitrogen, said reaction occurring at a temperature sufficiently high to convert said compact to an identically shaped porous compact of α-silicon nitride whiskers but sufficiently low to avoid subliming substantially all of said formed whiskers; and (e) impregnating said shaped porous compact of α-silicon nitride whiskers with a material selected from the group consisting of a resin binder, a liquid metal, a colloidal suspension, an ionic solution and at least one gaseous material to form an isotropic composite reinforced by α-silicon nitride whiskers.
Claim 20
Dependent Claim
24 words
The method of claim 17 wherein said material is a resin binder selected from the group consisting of acrylic, polyimide, phenolic, epoxy and silicone.
Claim 21
Dependent Claim
17 words
The method of claim 18, further including the step of polymerizing the material in said reinforced composite.
Claim 22
Dependent Claim
23 words
The method of claim 17 wherein said material is a liquid metal selected from the group consisting of aluminum, magnesium, silver and copper.
Claim 23
Dependent Claim
33 words
The method of claim 20 further including the step of treating said liquid metal with a wetting agent prior to said impregnating step to facilitate the wetting of said whiskers by said metal.
Claim 24
Dependent Claim
18 words
The method of claim 20 further including the step of solidifying the liquid metal after said impregnating step.
Claim 25
Dependent Claim
22 words
The method of claim 17 wherein said material is an aqueous colloidal suspension selected from the group consisting of silica and alumina.
Claim 26
Dependent Claim
27 words
The method of claim 23 further including the steps of: (a) drying said impregnated matrix to remove said aqueous phase; and (b) sintering said dried impregnated matrix.
Claim 27
Dependent Claim
25 words
The method of claim 17 wherein said material is an ionic solution selected from the group consisting of aluminum nitrate, nickel chloride and boric acid.
Claim 28
Dependent Claim
21 words
The method of claim 25 further including the step of decomposing said solution after said impregnating step to form a solid.
Claim 29
Dependent Claim
21 words
The method of claim 17 wherein said material is at least one gaseous material which can be converted to a solid.
Claim 30
Dependent Claim
25 words
The method of claim 27 wherein said gaseous material is selected from the group consisting of silicon tetrachloride, silicon tetrafluoride, ammonia, nitrogen, hydrogen and methane.
Claim 31
Dependent Claim
29 words
The method of claim 28, wherein said gaseous material is methane and further including the step of pyrolyzing said methane after said impregnating step to convert it to carbon.
Claim 32
Dependent Claim
97 words
The method of claim 28, wherein about 60-90 weight percent of said silicon particles are blended with said composition particles and wherein said gaseous material is a mixture containing at least one gaseous material selected from the group consisting of silicon tetrachloride and silicon tetrafluoride, and at least one gaseous material selected from the group consisting of dry ammonia, nitrogen and nitrogen with hydrogen, and further including the step of heating said porous shaped compact of α-silicon nitride whiskers whereby said gasous material mixture reacts to form of silicon nitride, which is reinforced with α-silicon nitride whiskers.
Claim 33
Dependent Claim
20 words
The method of claim 17, wherein about 60-90 weight percent of said silicon particles are blended with said composition particles.
Claim 34
Independent Claim
140 words
A method for producing individual α-silicon nitride whiskers comprising the steps of: (a) coating silicon particles in powder form with about 5 to 20 weight percent of fugitive composition particles able to sublime without leaving a residue; (b) blending the coated silicon particles with additional fugitive composition particles, said additional fugitive composition particles being larger than said composition particles coating said silicon particles; (c) compacting the blend; (d) subliming said fugitive composition particles from said blend to form a loosely-compacted silicon precursor; (e) reacting said silicon precursor with a substance that releases free nitrogen, said reaction occurring at a temperature sufficiently high to convert said loosely-compacted silicon precursor to loosely-compacted α-silicon nitride whiskers but sufficiently low to avoid subliming substantially all of said whiskers which are formed; and (f) breaking down said loosely-compacted α-silicon nitride whiskers to obtain individual whiskers.
Claim 35
Independent Claim
140 words
A method for producing individual α-silicon nitride whiskers comprising the steps of: (a) coating silicon particles in powder form with about 5 to 20 weight percent of fugitive composition particles able to sublime without leaving a residue; (b) blending the coated silicon particles with additional fugitive composition particles, said additional fugitive composition particles being larger than said composition particles coating said silicon particles; (c) compacting the blend; (d) subliming said fugitive composition particles from said blend to form a loosely-compacted silicon precursor; (e) reacting said silicon precursor with a substance that releases free nitrogen, said reaction occurring at a temperature sufficiently high to convert said loosely-compacted silicon precursor to loosely-compacted α-silicon nitride whiskers but sufficiently low to avoid subliming substantially all of said whiskers which are formed; and (f) breaking down said loosely-compacted α-silicon nitride whiskers to obtain individual whiskers.
Claim 36
Dependent Claim
96 words
The method of claim 32 wherein said coating of said silicon particles is accomplished by mixing said silicon particles and said fugitive composition particles by ball milling; wherein said composition is selected from the group consisting of naphthalene, camphor and carbon dioxide; wherein said substance is selected from the group consisting of nitrogen, dry ammonia, a mixture of hydrogen and dry ammonia, a mixture of nitrogen and dry ammonia, a mixture of hydrogen and nitrogen, and a mixture of nitrogen, dry ammonia and hydrogen; and wherein said temperature ranges between about 2100° F. and 2750° F.
Claim 37
Dependent Claim
16 words
The method of claim 33 wherein said temperature ranges between about 2300° F. and 2600° F.
Claim 38
Dependent Claim
37 words
The method of claim 33 wherein said composition is napthalene and wherein said substance is nitrogen containing from about 1 to 10 volume percent of a chemical selected from the group consisting of hydrogen and dry ammonia.
Claim 39
Independent Claim
175 words
A method for producing composite parts using a molding powder reinforced by α-silicon nitride whiskers comprising the steps of: (a) mixing silicon particles in powder form with about 5 to 20 weight percent of fugitive composition particles able to sublime without leaving a residue; (b) treating said mixture of silicon particles and composition particles to coat said silicon particles with said composition particles; (c) blending the coated silicon particles with more of said composition particles; (d) compacting the blend; (e) subliming said composition particles from said blend to form a loosely-compacted silicon precursor; (f) reacting said silicon precursor with a substance that releases free nitrogen, said reaction occurring at a temperature sufficiently high to convert said loosely-compacted silicon precursor to loosely-compacted α-silicon nitride whiskers but sufficiently low to avoid subliming substantially all of said whiskers which are formed; (g) breaking down said loosely-compacted α-silicon nitride whiskers to obtain individual whiskers; (h) mixing said α-silicon nitride whiskers with a molding powder; and (i) forming said mixture of whiskers and molding powder into a reinforced composite part.
Claim 40
Independent Claim
175 words
A method for producing composite parts using a molding powder reinforced by α-silicon nitride whiskers comprising the steps of: (a) mixing silicon particles in powder form with about 5 to 20 weight percent of fugitive composition particles able to sublime without leaving a residue; (b) treating said mixture of silicon particles and composition particles to coat said silicon particles with said composition particles; (c) blending the coated silicon particles with more of said composition particles; (d) compacting the blend; (e) subliming said composition particles from said blend to form a loosely-compacted silicon precursor; (f) reacting said silicon precursor with a substance that releases free nitrogen, said reaction occurring at a temperature sufficiently high to convert said loosely-compacted silicon precursor to loosely-compacted α-silicon nitride whiskers but sufficiently low to avoid subliming substantially all of said whiskers which are formed; (g) breaking down said loosely-compacted α-silicon nitride whiskers to obtain individual whiskers; (h) mixing said α-silicon nitride whiskers with a molding powder; and (i) forming said mixture of whiskers and molding powder into a reinforced composite part.
Claim 41
Dependent Claim
26 words
The method of claim 36 wherein said molding powder is selected from the group consisting of metal molding powder, ceramic molding powder and resin molding powder.
Claim 42
Dependent Claim
37 words
The method of claim 36 wherein the particle sizes of said composition particles after completion of said treatment step are relatively smaller than the sizes of said composition particles which are blended with said coated silicon particles.
Claim 43
Dependent Claim
22 words
The method of claim 36 wherein said forming step (i) is accomplished by compacting, said compacting being accompanied by heat and pressure.
References Cited (Backward Citations)
US3394991A
Cited
US3413090A
Cited
US3520740A
Cited
US3519399A
Cited
GB1274212A
Cited
DE1949587A1
Cited
US3835211A
Cited
US3615878A
Cited
US3607067A
Cited
CA938776A
Cited
DE2356921A1
Cited
US4127630A
Cited
US3959446A
Cited
US4145224A
Cited
GB1490543A
Cited
US4117095A
Cited
US4122152A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-06-13 | 1986-12-13 | 1987-06-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-06-13 | 1990-12-13 | 1991-06-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-06-13 | 1994-12-13 | 1995-06-14 | $7700.00 | Window Closed / Lapsed |