Free radical initiated polymerization of polymerizable ethylenically unsaturated monomer component in the presence of hydrogen peroxide
Assignee: PPG Industries Inc
•
Filing: 1985-04-03
•
Granted: 1986-07-15
•
Expires: 2005-04-03
Abstract
Abstract A method of preparing a free radical initiated addition polymer in the presence of hydrogen peroxide solution is disclosed. The hydrogen peroxide solution is added incrementally to the reaction mixture during the course of the polymerization with water and low boiling organic solvents being continuously removed from the reaction mixture. The invention enables the polymerization to occur at high temperatures which is conducive to the preparation of low molecular weight polymers.
Inventors
- 👤 Suryya K. Das
- 👤 Rostyslaw Dowbenko
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 14:14
CPC Classifications
C; C08; C08F; C08F4/00; C08F4/28; C08F4/30
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
88 words
A method of preparing a free radical initiated addition polymer by polymerizing a polymerizable ethylenically unsaturated monomer component in the presence of a solution of hydrogen peroxide characterized in adding an aqueous hydrogen peroxide solution to the polymerizing monomer component incrementally throughout the course of the polymerization and simultaneously removing low boiling organic solvents and water from the polymerizing monomer component as the aqueous hydrogen peroxide solution is being added; the resulting free radical initiated addition polymer having a number average molecular weight of no greater than 8000.
Claim 2
Independent Claim
88 words
A method of preparing a free radical initiated addition polymer by polymerizing a polymerizable ethylenically unsaturated monomer component in the presence of a solution of hydrogen peroxide characterized in adding an aqueous hydrogen peroxide solution to the polymerizing monomer component incrementally throughout the course of the polymerization and simultaneously removing low boiling organic solvents and water from the polymerizing monomer component as the aqueous hydrogen peroxide solution is being added; the resulting free radical initiated addition polymer having a number average molecular weight of no greater than 8000.
Claim 3
Dependent Claim
14 words
The method of claim 1 in which the polymerization is conducted at ambient pressure.
Claim 4
Dependent Claim
19 words
The method of claim 1 in which the polymerizable ethylenically unsaturated monomer component is dissolved in an organic solvent.
Claim 5
Dependent Claim
17 words
The method of claim 1 in which the polymerizable ethylenically unsaturated monomer component contains a hydroxyl-containing monomer.
Claim 6
Dependent Claim
23 words
The method of claim 4 in which the hydroxyl-containing monomer comprises at least 10 percent by weight of the ethylenically unsaturated monomer component.
Claim 7
Dependent Claim
19 words
The method of claim 1 in which the polymerizable ethylenically unsaturated monomer component contains a carboxylic acid group-containing monomer.
Claim 8
Dependent Claim
20 words
The method of claim 1 in which the addition polymer has a number average molecular weight between 1000 and 4000.
Claim 9
Dependent Claim
19 words
The method of claim 1 in which the polymerization is conducted at a temperature of at least 140° C.
Claim 10
Dependent Claim
22 words
The method of claim 3 in which the organic solvent is selected from the class consisting of aromatic hydrocarbons, ketones and esters.
Claim 11
Dependent Claim
18 words
The method of claim 1 in which the water and low boiling organic solvents are removed by distillation.
Claim 12
Dependent Claim
42 words
The method of claim 1 in which the aqueous hydrogen peroxide is used in amounts of about 0.2 to 20 percent by weight, the percentage by weight being of hydrogen peroxide and being based on total weight of the polymerizable monomer component.
Claim 13
Independent Claim
91 words
A method of preparing a free radical initiated addition polymer by polymerizing a polymerizable ethylenically unsaturated monomer component dissolved in an organic solvent, said polymerization being conducted in the presence of aqueous hydrogen peroxide, the improvement comprising adding the aqueous hydrogen peroxide to the polymerizing monomer component incrementally throughout the course of the polymerization and simultaneously removing water from the polymerizing monomer component as it is being added with the aqueous hydrogen peroxide, said resultant free radical initiated addition polymer having a number average molecular weight of no greater than 8000.
Claim 14
Independent Claim
91 words
A method of preparing a free radical initiated addition polymer by polymerizing a polymerizable ethylenically unsaturated monomer component dissolved in an organic solvent, said polymerization being conducted in the presence of aqueous hydrogen peroxide, the improvement comprising adding the aqueous hydrogen peroxide to the polymerizing monomer component incrementally throughout the course of the polymerization and simultaneously removing water from the polymerizing monomer component as it is being added with the aqueous hydrogen peroxide, said resultant free radical initiated addition polymer having a number average molecular weight of no greater than 8000.
Claim 15
Dependent Claim
18 words
The method of claim 12 in which the polymerization is conducted at a temperature greater than 140° C.
Claim 16
Dependent Claim
13 words
The method of claim 12 in which the water is removed by distillation.
Claim 17
Dependent Claim
42 words
The method of claim 1 in which the aqueous hydrogen peroxide is used in amounts of about 0.2 to 20 percent by weight, the percentage by weight being of hydrogen peroxide and being based on total weight of the polymerizable monomer component.
Claim 18
Dependent Claim
14 words
The method of claim 12 in which the polymerization is conducted at ambient pressure.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-07-14 | 1990-01-13 | 1990-07-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-07-14 | 1994-01-13 | 1994-07-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-07-14 | 1998-01-13 | 1998-07-15 | $7700.00 | Window Closed / Lapsed |