Incorporation of a hydrophile in fibrous webs to enhance absorbency
Assignee: Fort James Corp
•
Filing: 1985-04-18
•
Granted: 1986-07-15
•
Expires: 2005-04-18
Abstract
Abstract An air laid fibrous web product of enhanced absorbency and method of making same having a basis weight of between about 8 to about 50 pounds per ream, and a bulk of at least 0.40 mils per pound per ream, the web product comprising a multiplicity of papermaking fibers distributed randomly in the form of a web, an adhesive material, preferably a latex, essentially permeating said web of randomly distributed fibers and upon curing bonding adjacent fibers, the adhesive material representing between about 15 to about 30% of the basis weight of the web product and between about 0.1 to about 5.0 by weight of a hydrophile, said hydrophile substantially coating the bonded fibers. The hydrophile is applied to the web as an aqueous solution downstream of the bonding station, either in an immersion or spray treating step.
Inventors
- 👤 William R. Watt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 18:51
CPC Classifications
A; A61; A61L; A61L15/00; A61L15/16; A61L15/42; A61F; A61F13/00; A61F13/15; A61F13/15577; A61F13/15617; A61F13/15658; D; D21; D21H; D21H21/00; D21H21/14; D21H21/22; D21H25/00; D21H5/00; D21H5/26; D21H5/265; Y; Y10; Y10S; Y10S428/00; Y10S428/913; Y10T; Y10T442/00; Y10T442/20; Y10T442/2484; Y10T442/60; Y10T442/69
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
173 words
A process for making an air laid soft. high bulk, absorbent fibrous web having a basis weight in the range between about 8 to about 50 lbs./ream, consisting essentially of the steps of: (a) air laying a loose web; (b) bonding said web with a substantially hydrophobic adhesive material; (c) curing said adhesive material; (d) incorporating into said web an aqueous solution of a water soluble hydrophile at any stage in said process contemporary with or subsequent to said step (b) to enhance the absorbency rate of the web by neutralizing the anti-wetting effects of the substantially hydrophobic adhesive material; and (e) drying said web while retaining between about 0.1 to about 5.0% by weight of said hydrophile, wherein said water soluble hydrophile is selected from the group consisting of polyethylene oxide, cellulose ethers, hydroxymethyl cellulose, polyvinyl alcohol, polyvinyl pyrrolidone, gelatin, graft copolymers of starch, crosslinked polyacrylates, acrylate polymers, crosslinked carboxymethyl cellulose alkali salts, starch or guar gum grafted with acrylamide acid salts in combination with divinyl compounds, glycerin, and compatible combinations thereof.
Claim 2
Dependent Claim
173 words
A process for making an air laid soft. high bulk, absorbent fibrous web having a basis weight in the range between about 8 to about 50 lbs./ream, consisting essentially of the steps of: (a) air laying a loose web; (b) bonding said web with a substantially hydrophobic adhesive material; (c) curing said adhesive material; (d) incorporating into said web an aqueous solution of a water soluble hydrophile at any stage in said process contemporary with or subsequent to said step (b) to enhance the absorbency rate of the web by neutralizing the anti-wetting effects of the substantially hydrophobic adhesive material; and (e) drying said web while retaining between about 0.1 to about 5.0% by weight of said hydrophile, wherein said water soluble hydrophile is selected from the group consisting of polyethylene oxide, cellulose ethers, hydroxymethyl cellulose, polyvinyl alcohol, polyvinyl pyrrolidone, gelatin, graft copolymers of starch, crosslinked polyacrylates, acrylate polymers, crosslinked carboxymethyl cellulose alkali salts, starch or guar gum grafted with acrylamide acid salts in combination with divinyl compounds, glycerin, and compatible combinations thereof.
Claim 3
Dependent Claim
171 words
A process for making an air laid soft, high bulk absorbent fibrous web having a basis weight in the range between about 8 to about 50 lbs./ream, comprising the steps of: (a) air laying a loose web; (b) bonding said web with a substantially hydrophobic adhesive material; (c) curing said adhesive material; (d) incorporating into said web an aqueous solution of a water soluble hydrophile at any stage in said process contemporary with or subsequent to said step (b) to enhance the absorbency rate of the web by neutralizing the antiwetting effects of the substantially hydrophobic adhesive material; and (e) drying said web while retaining between about 0.1 to about 5.0% by weight of said hydrophile, wherein said water soluble hydrophile is selected from the group consisting of polyethylene oxide, cellulose ethers, hydroxymethyl cellulose, polyvinyl alcohol, polyvinyl pyrrolidone, gelatin, graft copolymers of starch, crosslinked polyacrylates, acrylate polymers, crosslinked carboxymethyl cellulose alkali salts, starch or guar gum grafted with acrylamide acid salts in combination with divinyl compounds, glycerin, and compatible combinations thereof.
Claim 4
Dependent Claim
171 words
A process for making an air laid soft, high bulk absorbent fibrous web having a basis weight in the range between about 8 to about 50 lbs./ream, comprising the steps of: (a) air laying a loose web; (b) bonding said web with a substantially hydrophobic adhesive material; (c) curing said adhesive material; (d) incorporating into said web an aqueous solution of a water soluble hydrophile at any stage in said process contemporary with or subsequent to said step (b) to enhance the absorbency rate of the web by neutralizing the antiwetting effects of the substantially hydrophobic adhesive material; and (e) drying said web while retaining between about 0.1 to about 5.0% by weight of said hydrophile, wherein said water soluble hydrophile is selected from the group consisting of polyethylene oxide, cellulose ethers, hydroxymethyl cellulose, polyvinyl alcohol, polyvinyl pyrrolidone, gelatin, graft copolymers of starch, crosslinked polyacrylates, acrylate polymers, crosslinked carboxymethyl cellulose alkali salts, starch or guar gum grafted with acrylamide acid salts in combination with divinyl compounds, glycerin, and compatible combinations thereof.
Claim 5
Dependent Claim
15 words
The method of claim 2 wherein the hydrophile material is incorporated within the adhesive material.
Claim 6
Dependent Claim
20 words
The method of claim 2 wherein the hydrophile solution is sprayed onto the web, the spray essentially permeating said web.
Claim 7
Dependent Claim
14 words
The method of claim 2 wherein the web is immersed in the hydrophile solution.
Claim 8
Dependent Claim
26 words
The methods of claim 4 or 5 wherein the web is treated after bonding of the web, the adhesive material being cured in the drying step.
Claim 9
Dependent Claim
27 words
The methods of claim 4 or 5 wherein the adhesive material is cured by heating, and the web is then treated with the hydrophile solution and dried.
Claim 10
Dependent Claim
35 words
The method of claim 4 wherein each surface of the web is bonded, and one or both surfaces of the web is treated with the hydrophile solution, said web being dried after each hydrophile treatment.
Claim 11
Dependent Claim
26 words
The methods of claim 3, 4, 5, or 8 wherein the concentration of the hydrophile in solution is between about 0.1 to about 10% by weight.
Claim 12
Dependent Claim
29 words
The methods of claim 9 wherein the absorbency rate is enhanced by at least 20% as compared to untreated webs of similar bulk as measured by mirror wipe time.
Claim 13
Dependent Claim
26 words
The methods of claim 10 wherein the amount of the hydrophile preferably retained within the web product is between about 0.5 to about 2.5% by weight.
Claim 14
Dependent Claim
14 words
The methods of claim 10 wherein mirror wipe time is less than 18 seconds.
Claim 15
Dependent Claim
21 words
The methods of claim 11 wherein the preferred concentration of the hydrophile in solution is between 1.0 to 5.0% by weight.
Claim 16
Dependent Claim
14 words
The method of claim 9 wherein the adhesive material is an aqueous latex emulsion.
References Cited (Backward Citations)
US3674632A
Cited
US3617439A
Cited
US3664343A
Cited
US3686024A
Cited
US3808165A
Cited
US4008353A
Cited
US4105033A
Cited
US4096311A
Cited
US4156628A
Cited
US4154647A
Cited
US4309469A
Cited
US4145248A
Cited
US4292105A
Cited
US4392861A
Cited
US4362781A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-07-14 | 1990-01-13 | 1990-07-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-07-14 | 1994-01-13 | 1994-07-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-07-14 | 1998-01-13 | 1998-07-15 | $7700.00 | Window Closed / Lapsed |