Process for the removal of impurities from optical component materials
Assignee: Raytheon Co
•
Filing: 1984-08-14
•
Granted: 1986-07-15
•
Expires: 2004-08-14
Abstract
Abstract A process is disclosed for the removal of water and water derived impurities, e.g. OH-, substitutionally or interstitially incorporated in the structure of crystalline and amorphous materials, more specifically, in metal oxides, e.g. fused silica or aluminum oxide, wherein the material is exposed in powdered form to a gaseous mixture of halogen and carbon monoxide at a predetermined elevated temperature. The mixture of halogen and carbon monoxide reacts to cause the water and OH- ion concentration in the processed material to be reduced to an extremely low level. Materials purified by the process can be used to produce optical fibers and laser windows of excellent mechanical, thermal and optical properties.
Inventors
- 👤 Ricardo C. Pastor
- 👤 Luisa E. Gorre
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 20:20
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; C01; C01F; C01F7/00; C01F7/02; C01F7/30; C01F7/32; C03; C03C; C03C1/00; C03C1/02; C03C1/022; C04B41/53; C04B41/80; C04B41/91; Y; Y10; Y10S; Y10S65/00; Y10S65/90
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
129 words
A process for the removal of water and water derived impurities substitutionally or interstitially incorporated in the structures of crystalline and amorphous optical materials consisting of metal oxides, comprising heating the optical material to a temperature of greater than 1000° C., and thereafter exposing the heated optical material at said temperature to a gas phase reactive atmosphere containing a mixture of a halogen and carbon monoxide for a period of time, the molar amount of carbon monoxide is substantially greater than the stoichiometric amount necessary for carbon monoxide to react with halogen to form carbonyl halide, the amounts of carbon monoxide and halogen being sufficient to react with the water and water derived impurities surrounding and within the optical material to reduce the impurities to an extremely low level.
Claim 2
Dependent Claim
129 words
A process for the removal of water and water derived impurities substitutionally or interstitially incorporated in the structures of crystalline and amorphous optical materials consisting of metal oxides, comprising heating the optical material to a temperature of greater than 1000° C., and thereafter exposing the heated optical material at said temperature to a gas phase reactive atmosphere containing a mixture of a halogen and carbon monoxide for a period of time, the molar amount of carbon monoxide is substantially greater than the stoichiometric amount necessary for carbon monoxide to react with halogen to form carbonyl halide, the amounts of carbon monoxide and halogen being sufficient to react with the water and water derived impurities surrounding and within the optical material to reduce the impurities to an extremely low level.
Claim 3
Dependent Claim
27 words
The process of claim 1 wherein the optical material is selected from the group consisting of metal oxides of Periodic Table Group II, III and IV materials.
Claim 4
Dependent Claim
11 words
The process of claim 2 wherein the material is fused silica.
Claim 5
Dependent Claim
11 words
The process of claim 2 wherein the material is aluminum oxide.
Claim 6
Dependent Claim
14 words
The process of claim 1 wherein the halogen/carbon monoxide molar ratio is about 1:18.
Claim 7
Dependent Claim
11 words
The process of claim 1 wherein the halogen is elemental iodine.
Claim 8
Dependent Claim
40 words
The process of claim 1 wherein the optical material is exposed to the mixture of halogen and carbon monoxide at temperatures ranging between about 1000° C. to about 1500° C. for a period of about 10 to about 100 hours.
References Cited (Backward Citations)
US2550173A
Cited
US3114601A
Cited
US3026210A
Cited
US3282641A
Cited
US4013796A
Cited
US4315832A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-07-14 | 1990-01-13 | 1990-07-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-07-14 | 1994-01-13 | 1994-07-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-07-14 | 1998-01-13 | 1998-07-15 | $7700.00 | Window Closed / Lapsed |