Hot-pressed ionic fluoride optical bodies free of absorption bands and method of making them
Assignee: Solon Technologies Inc
•
Filing: 1973-08-27
•
Granted: 1977-03-22
•
Expires: 1993-08-27
Abstract
Abstract A hot-pressed optical body is disclosed which is free from absorption bands due to carbon dioxide, water, hydroxyl ion and acid fluorides in the ultraviolet, visible and near-infrared wavelength regions. Typically, the optical body is formed from a powder of an alkaline earth metal fluoride, alkali metal fluoride, or rare earth metal fluoride. One or more absorption bands due to a single impurity may be reduced or eliminated, or bands due to plural impurities may be reduced or eliminated sequentially, or simultaneously. The optical body is made by flowing a reactive, reducing gas, optionally, in combination with hydrogen fluoride gas, directly into the die cavity containing a pressable powder, and either hot-pressing or extruding the powder.
Inventors
- 👤 Carl F. Swinehart
- 👤 Herbert Packer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 01:25
CPC Classifications
G; G02; G02B; G02B1/00; C; C04; C04B; C04B35/00; C04B35/515; C04B35/553
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
147 words
An optical body consisting essentially of a hot-pressed polycrystalline mass of pressable fluoride represented by the general formula: M m F n wherein M represents one or two elements selected from the group consisting of an alkali metal, and an alkaline earth metal, m is an integer representing the number of atoms of said one or two elements, and n is an integer which satisfies the valence requirements of M m , said body characterized by a transmittance in excess of about 90%, without correction for reflection losses, in a portion of a predetermined usable wavelength range from about 1 micron to about 7 microns, and, less than 1% per millimeter absorption due to absorption bands in the transmission spectra within said range wherein said absorption is due to at least one impurity selected from the group consisting of carbon dioxide, water, hydroxyl ion and acid fluorides.
Claim 2
Dependent Claim
147 words
An optical body consisting essentially of a hot-pressed polycrystalline mass of pressable fluoride represented by the general formula: M m F n wherein M represents one or two elements selected from the group consisting of an alkali metal, and an alkaline earth metal, m is an integer representing the number of atoms of said one or two elements, and n is an integer which satisfies the valence requirements of M m , said body characterized by a transmittance in excess of about 90%, without correction for reflection losses, in a portion of a predetermined usable wavelength range from about 1 micron to about 7 microns, and, less than 1% per millimeter absorption due to absorption bands in the transmission spectra within said range wherein said absorption is due to at least one impurity selected from the group consisting of carbon dioxide, water, hydroxyl ion and acid fluorides.
Claim 3
Dependent Claim
20 words
The optical body of claim 1 wherein said transmission spectra is characterized by an essential freedom of said absorption bands.
Claim 4
Dependent Claim
48 words
The optical body of claim 1 wherein said M represents magnesium, m is 1 and n is 2, and said transmission spectra is characterized by an essential freedom of said absorption bands in a major portion of the wavelength range from about 2 μ to about 7 μ.
Claim 5
Dependent Claim
32 words
The optical body of claim 1 wherein said M represents calcium, m is 1, and n is 2, and said transmission spectra is characterized by an essential freedom of said absorption bands.
Claim 6
Dependent Claim
50 words
The optical body of claim 1 characterized by essentially complete freedom from an absorption band due to (a) hydroxy OH ion at about 2.8 μ, and (b) acid fluorides at about 1.4 μ, 2.2 μ, 2.3 μ, 2.45 μ, 2.56 μ, 2.66 μ, 2.9 μ, 5 μ and 6.7 μ.
Claim 7
Dependent Claim
66 words
The optical body of claim 1 characterized by essentially complete freedom from an absorption band due to (a) CO 2 at about 4.2 μ, (b) water at about 3.0 μ and 6.1 μ, (c) hydroxyl OH ion at about 2.8 μ, and (d) acid fluorides at about 1.4 μ, 2.2 μ, 2.3 μ, 2.45 μ, 2.56 μ, 2.66 μ, 2.9 μ, 5 μ, and 6.7 μ.
Claim 8
Dependent Claim
98 words
An infrared transmitting optical body consisting essentially of a relatively thick hot-pressed polycrystalline pressable ionic fluoride selected from the group consisting of an alkaline earth metal fluoride, and an alkali metal fluoride, said body having a thickness greater than about 0.20 centimeter, characterized by a transmittance in excess of about 90%, without correction for reflection losses, in a portion of a predetermined usable wavelength range from about 1 micron to about 7 microns, and, an essential freedom of all absorption bands in the transmission spectra of said body in the range from about 2 to about 7 μ.
Claim 9
Dependent Claim
98 words
An infrared transmitting optical body consisting essentially of a relatively thick hot-pressed polycrystalline pressable ionic fluoride selected from the group consisting of an alkaline earth metal fluoride, and an alkali metal fluoride, said body having a thickness greater than about 0.20 centimeter, characterized by a transmittance in excess of about 90%, without correction for reflection losses, in a portion of a predetermined usable wavelength range from about 1 micron to about 7 microns, and, an essential freedom of all absorption bands in the transmission spectra of said body in the range from about 2 to about 7 μ.
References Cited (Backward Citations)
US2550173A
Cited
GB913175A
Cited
US3114601A
Cited
US3359066A
Cited
US3206279A
Cited
US3282641A
Cited
US3408430A
Cited
GB1100519A
Cited
US3365271A
Cited
US3649552A
Cited
US3565700A
Cited
US3615169A
Cited
US3816600A
Cited
US3920802A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-03-21 | 1980-09-20 | 1981-03-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-03-21 | 1984-09-20 | 1985-03-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-03-21 | 1988-09-20 | 1989-03-22 | $7700.00 | Window Closed / Lapsed |