Induction hardening of steel
Assignee: National Forge Co
•
Filing: 1983-11-22
•
Granted: 1986-07-08
•
Expires: 2003-11-22
Abstract
Abstract A method for induction hardening through hardened chromium-molybdenum hot work die steel comprising the steps of induction heating to a uniform temperature above the upper critical temperature, cooling, and double tempering at temperatures below the lower critical temperature to produce a workpiece having a tough core and a hard wear resistant surface. An apparatus is provided for induction hardening long workpieces with minimum distortion by providing an inductor coil which always remains centered around the workpiece during induction coil traverse. Mandrel bars for tube piercing mills can be induction hardened using this process and apparatus.
Inventors
- 👤 Ashok Khare
- 👤 Paul Duliba
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 21:07
CPC Classifications
C; C21; C21D; C21D1/00; C21D1/06; C21D1/09; C21D1/10; Y; Y02; Y02P; Y02P10/00; Y02P10/25
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
55 words
A process for induction hardening through hardened chromium-molybdenum hot work die steel to achieve a uniform surface hardness and case depth without cracking or peeling through the case depth comprising the steps of induction heating to a uniform temperature about an upper critical temperature, cooling, and double tempering at temperatures below a lower critical temperature.
Claim 2
Dependent Claim
55 words
A process for induction hardening through hardened chromium-molybdenum hot work die steel to achieve a uniform surface hardness and case depth without cracking or peeling through the case depth comprising the steps of induction heating to a uniform temperature about an upper critical temperature, cooling, and double tempering at temperatures below a lower critical temperature.
Claim 3
Dependent Claim
22 words
A process as claimed in claim 1 wherein the steel has been through hardened to 321 to 375 Brinell before induction hardening.
Claim 4
Dependent Claim
38 words
A process as claimed in claim 1 wherein the surface hardness of the steel is at least 60 Rc and case hardness is at least 48 Rc at about 3/16 inch (4.76 mm.) case depth after induction hardening.
Claim 5
Dependent Claim
13 words
A process as claimed in claim 1 wherein the steel is type H-11.
Claim 6
Dependent Claim
22 words
A process as claimed in claim 1 wherein the uniform temperature above the upper critical temperature is about 1900° F. (1037.8° C.).
Claim 7
Dependent Claim
15 words
A process as claimed in claim 1 wherein the cooling step is by air cooling.
Claim 8
Dependent Claim
24 words
A process as claimed in claim 1 wherein the double tempering temperatures below the lower critical temperature are both about 1010° F. (543.3° C.).
Claim 9
Dependent Claim
86 words
A process for induction hardening type H-11 steel through hardened to 321 to 341 Brinell to achieve a uniform surface hardness of at least 60 Rc and a case hardness of at least 48 Rc at about 3/16 inch (4.76 mm.) comprising the steps of heating by inductor coil to about 1900° F. (1037.8° C.) with an inductor coil travel speed of about 43/4 inches/min. (121 mm./min.) while rotating at about 15 revolutions per minute, air cooling, and double tempering at about 1010° F. (543.3° C.).
Claim 10
Dependent Claim
86 words
A process for induction hardening type H-11 steel through hardened to 321 to 341 Brinell to achieve a uniform surface hardness of at least 60 Rc and a case hardness of at least 48 Rc at about 3/16 inch (4.76 mm.) comprising the steps of heating by inductor coil to about 1900° F. (1037.8° C.) with an inductor coil travel speed of about 43/4 inches/min. (121 mm./min.) while rotating at about 15 revolutions per minute, air cooling, and double tempering at about 1010° F. (543.3° C.).
Claim 11
Independent Claim
213 words
An apparatus for continuously induction heating a workpiece to obtain a hardened workpiece with minimum distortion, said apparatus comprising: a frame; a stationary bed supported by said frame; means for supporting a workpiece in said apparatus; a headstock drive assembly for engaging one end of a workpiece and rotating such workpiece; an inductor head support assembly adapted to be supported by a workpiece; a carriage assembly slidably supported on said stationary bed for moving said inductor head support assembly in a line of movement along a workpiece; counterweight means pivotably connected to said inductor head support assembly by at least one intermediate connecting means, with said intermediate connecting means being pivotably connected to said carriage assembly, whereby said counterweight means has a sufficient weight to cause said inductor support assembly to apply a minimum force on said workpiece supporting said inductor head support assembly; a drive means connected to said carriage assembly for driving said carriage assembly and inductor head support assembly along the longitudinal length of said workpiece; and at least one pivotable connection between said inductor head support assembly and said carriage assembly for allowing free movement of said inductor head support assembly in a plane perpendicular to the line of movement of said inductor head support assembly along a workpiece.
Claim 12
Independent Claim
213 words
An apparatus for continuously induction heating a workpiece to obtain a hardened workpiece with minimum distortion, said apparatus comprising: a frame; a stationary bed supported by said frame; means for supporting a workpiece in said apparatus; a headstock drive assembly for engaging one end of a workpiece and rotating such workpiece; an inductor head support assembly adapted to be supported by a workpiece; a carriage assembly slidably supported on said stationary bed for moving said inductor head support assembly in a line of movement along a workpiece; counterweight means pivotably connected to said inductor head support assembly by at least one intermediate connecting means, with said intermediate connecting means being pivotably connected to said carriage assembly, whereby said counterweight means has a sufficient weight to cause said inductor support assembly to apply a minimum force on said workpiece supporting said inductor head support assembly; a drive means connected to said carriage assembly for driving said carriage assembly and inductor head support assembly along the longitudinal length of said workpiece; and at least one pivotable connection between said inductor head support assembly and said carriage assembly for allowing free movement of said inductor head support assembly in a plane perpendicular to the line of movement of said inductor head support assembly along a workpiece.
Claim 13
Dependent Claim
85 words
An apparatus as claimed in claim 9 wherein said inductor head support assembly comprises an inductor head, an inductor coil, a roller guide, and a shoe guide, wherein said inductor head supports said inductor coil, said roller guide, and said shoe guide, said inductor coil being supported between said roller guide and said shoe guide, and wherein said inductor coil surrounds a workpiece so that when such workpiece is held in said apparatus there is a uniform gap between said inductor coil and such workpiece.
Claim 14
Dependent Claim
121 words
An apparatus as claimed in claim 10 wherein said roller guide comprises a mounting bracket for supporting at least one ball bearing roller and said shoe guide comprises a mounting bracket and at least one shoe, said ball bearing roller and said shoe for contacting a workpiece, such workpiece having a cold side on one side of said inductor coil and a hot side on the other side of said inductor coil, said ball bearing roller contacting the cold side and said shoe contacting the hot side of such workpiece, said ball bearing roller and said shoe for adapting to distortions in such workpiece and moving said inductor head so that said inductor coil maintains a uniform gap around such workpiece.
Claim 15
Dependent Claim
48 words
An apparatus as claimed in claim 11 wherein said pivotable connection comprises at least one longitudinal arm rigidly mounted above said inductor head and at least one transverse arm pivotably connected to said carriage assembly, said longitudinal arm and said transverse arm pivotably connected to a connector plate.
Claim 16
Dependent Claim
32 words
An apparatus as claimed in claim 12 wherein said headstock drive assembly is adapted so that said roller guide and said inductor coil can run out over an end of a workpiece.
Claim 17
Dependent Claim
54 words
An apparatus as claimed in claim 13 wherein said means for supporting a workpiece in said apparatus comprises at least one steady rest mounted on said stationary bed, wherein said steady rest has rollers for supporting such workpiece, said rollers being removable to allow for passage of said inductor coil past said steady rest.
Claim 18
Dependent Claim
22 words
An apparatus as claimed in claim 12 wherein said means for supporting a workpiece in said apparatus comprises headstock and tailstock centers.
Claim 19
Dependent Claim
104 words
A process for continuously induction hardening a workpiece to obtain a hardened workpiece with minimum distortion, with said workpiece being a mandrel bar for a tube piercing mill made from class 520 steel, comprising scanning a workpiece with an inductor coil in one direction and adjusting the inductor coil in a plane perpendicular to the scanning direction of the inductor coil so a uniform gap is maintained between the workpiece and the inductor coil, with said workpiece being continuously heated by said inductor coil to a temperature above an upper critical temperature, air cooled, and double tempered to temperatures below a lower critical temperature.
Claim 20
Dependent Claim
104 words
A process for continuously induction hardening a workpiece to obtain a hardened workpiece with minimum distortion, with said workpiece being a mandrel bar for a tube piercing mill made from class 520 steel, comprising scanning a workpiece with an inductor coil in one direction and adjusting the inductor coil in a plane perpendicular to the scanning direction of the inductor coil so a uniform gap is maintained between the workpiece and the inductor coil, with said workpiece being continuously heated by said inductor coil to a temperature above an upper critical temperature, air cooled, and double tempered to temperatures below a lower critical temperature.
Claim 21
Dependent Claim
34 words
A process as claimed in claim 16 wherein said mandrel bar has a surface hardness of 60 Rc and a case hardness of 48 Rc at about 3/16 inch (4.76 mm.) after induction hardening.
References Cited (Backward Citations)
US2364893A
Cited
US3270177A
Cited
US3377214A
Cited
US3562030A
Cited
US3682721A
Cited
US4142923A
Cited
US4459451A
Cited
JPS5739160A
Cited
SU926062A1
Cited
US4394194A
Cited
US4388510A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-07-07 | 1990-01-06 | 1990-07-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-07-07 | 1994-01-06 | 1994-07-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-07-07 | 1998-01-06 | 1998-07-08 | $7700.00 | Window Closed / Lapsed |