Foaming and curing polyimide resins by application of microwave energy
Assignee: IMI-TECH Corp ELK GROVE ILL A CORP OF
•
Filing: 1985-11-19
•
Granted: 1986-07-08
•
Expires: 2005-11-19
Abstract
Abstract Methods of foaming and fully curing polyimide resins entirely by the application of microwave energy. Foamable polyimide resins may be prepared by esterifying a suitable dianhydride, reacting the product with a suitable diamine, drying the resulting product and heating to spontaneously form a foam. In the past, such materials could be foamed but could not be satisfactorily cured to a resilient foam entirely by microwave energy. Post-foaming direct application of thermal energy was required to produce a satisfactory foam. We have found that adding a suitable oxoimine, such as caprolactam, to the reaction mixture results in a foam material which is fully and completely cured entirely by the application of microwave energy, considerably simplifying the process and reducing costs.
Inventors
- 👤 John Gagliani
- 👤 John V. Long
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 18:26
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/02; C08J2379/00; C08J2379/04; C08J2379/08
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
121 words
The method of making a resilient, flame resistant modified polyimide foam which comprises the steps of: reacting an aromatic dianhydride with an oximine having the general formula: ##STR6## wherein "X" is an integer from 2 to 4, in a mole ratio of oxoimine to dianhydride between about 1.5:1 and about 0.05:1 to produce an N-substituted aliphatic imide; dissolving said imide in a reactive solvent esterifying agent to esterify said imide; adding thereto a diamine; drying the resulting solution; and exposing the dried material to microwave energy at a level of from about 5 to 80 KW for from 5 to 60 minutes to cause said material to spontaneously foam and cure, whereby a resilient foam having good flame resistance is produced.
Claim 2
Independent Claim
121 words
The method of making a resilient, flame resistant modified polyimide foam which comprises the steps of: reacting an aromatic dianhydride with an oximine having the general formula: ##STR6## wherein "X" is an integer from 2 to 4, in a mole ratio of oxoimine to dianhydride between about 1.5:1 and about 0.05:1 to produce an N-substituted aliphatic imide; dissolving said imide in a reactive solvent esterifying agent to esterify said imide; adding thereto a diamine; drying the resulting solution; and exposing the dried material to microwave energy at a level of from about 5 to 80 KW for from 5 to 60 minutes to cause said material to spontaneously foam and cure, whereby a resilient foam having good flame resistance is produced.
Claim 3
Dependent Claim
20 words
The method according to claim 1 wherein said drying is accomplished by spray drying to produce a substantially uniform powder.
Claim 4
Dependent Claim
21 words
The method according to claim 1 wherein said microwave energy is applied for about 10 minutes at about 10 KW (optimum).
Claim 5
Dependent Claim
22 words
The method according to claim 1 wherein said aromatic dianhydride is pyromellitic dianhydride, 3, 3', 4,4'-benzophenone tetracarboxylic acid dianhydride or mixtures thereof.
Claim 6
Dependent Claim
11 words
The method according to claim 1 wherein said oxoimine is caprolactam.
Claim 7
Dependent Claim
13 words
The method according to claim 1 wherein said reactive solvent is methyl alcohol.
Claim 8
Dependent Claim
12 words
The method according to claim 1 wherein said diamine is 4,4'-diaminophenyl methane.
Claim 9
Dependent Claim
24 words
The method according to claim 1 wherein said diamine comprises at least two different diamines, at least one of which is an aromatic diamine.
Claim 10
Dependent Claim
29 words
The method according to claim 1 further including the step of adding from about 0.01 to about 2 wt. % of a surfactant to the solution prior to drying.
Claim 11
Dependent Claim
22 words
The method according to claim 1 further including the step of adding fillers or reinforcing materials to the solution prior to drying.
Claim 12
Independent Claim
118 words
The method of making a resilient, flame resistant modified polyimide foam which comprises the steps of: reacting an aromatic dianhydride with an oximine having the general formula: ##STR7## wherein "X" is an integer from 2 to 4, in a mole ratio of oxoimine to dianhydride between about 1.5:1 and about 0.05:1 to produce an N-substituted aliphatic imide; dissolving said imide in reactive solvent esterifying agent to exterify said imide; adding thereto a diamine; adding thereto an effective quantity of a surfactant, spray drying the mixture to produce a dry, free-flowing powder; placing said powder in a microwave oven; subjecting said powder solely to microwave energy for a period sufficient to produce a fully cured, resilient and flexible foam.
Claim 13
Independent Claim
118 words
The method of making a resilient, flame resistant modified polyimide foam which comprises the steps of: reacting an aromatic dianhydride with an oximine having the general formula: ##STR7## wherein "X" is an integer from 2 to 4, in a mole ratio of oxoimine to dianhydride between about 1.5:1 and about 0.05:1 to produce an N-substituted aliphatic imide; dissolving said imide in reactive solvent esterifying agent to exterify said imide; adding thereto a diamine; adding thereto an effective quantity of a surfactant, spray drying the mixture to produce a dry, free-flowing powder; placing said powder in a microwave oven; subjecting said powder solely to microwave energy for a period sufficient to produce a fully cured, resilient and flexible foam.
Claim 14
Dependent Claim
21 words
The method according to claim 11 wherein said aromatic dianhydride is pyromellitic dianhydride, 3,3', 4,4'-benzophenone tetracarboxylic acid dianhydride or mixtures thereof.
Claim 15
Dependent Claim
11 words
The method according to claim 11 wherein said oxoimine is caprolactam.
Claim 16
Dependent Claim
13 words
The method according to claim 11 wherein said reactive solvent is methyl alcohol.
Claim 17
Dependent Claim
12 words
The method according to claim 11 wherein said diamine is 4,4'-diaminophenyl methane.
Claim 18
Dependent Claim
24 words
The method according to claim 11 wherein said diamine comprises at least two different diamines, at least one of which is an aromatic diamine.
Claim 19
Dependent Claim
125 words
In the method of making a resilient, flame resistant modified polyimide foam which comprises the steps of: reacting an aromatic dianhydride with an oximine having the general formula: ##STR8## where "X" is an integer from 2 to 4, to produce an N-substituted aliphatic imide; dissolving said imide in a reactive solvent esterifying agent to esterify said imide; adding thereto a diamine; drying the resulting solution; and heating the dry material to foam and cure the material; the improvement wherein: said solution is dried by spray drying said solution to produce a free flowing dry powder; and said dry material is heated to foam and cure solely by exposing said dry powder to microwave energy for a period sufficient to produce a fully cured, resilient foam.
Claim 20
Dependent Claim
125 words
In the method of making a resilient, flame resistant modified polyimide foam which comprises the steps of: reacting an aromatic dianhydride with an oximine having the general formula: ##STR8## where "X" is an integer from 2 to 4, to produce an N-substituted aliphatic imide; dissolving said imide in a reactive solvent esterifying agent to esterify said imide; adding thereto a diamine; drying the resulting solution; and heating the dry material to foam and cure the material; the improvement wherein: said solution is dried by spray drying said solution to produce a free flowing dry powder; and said dry material is heated to foam and cure solely by exposing said dry powder to microwave energy for a period sufficient to produce a fully cured, resilient foam.
Claim 21
Dependent Claim
24 words
The improvement according to claim 17 wherein an effective quantity of a surfactant is mixed with said solution prior to spray drying said solution.
Claim 22
Dependent Claim
32 words
The improvement according to claim 17 wherein said dry powder is exposed to microwave energy for from about 7 to 10 minutes at an energy level of about 8 to 10 KW.
Claim 23
Dependent Claim
22 words
The improvement according to claim 17 wherein said aromatic dianhydride is 3,3', 4,4' - benzophenonetetracarboxylic acid dianhydride and said oxoimine is caprolactam.
References Cited (Backward Citations)
US31756A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-07-07 | 1990-01-06 | 1990-07-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-07-07 | 1994-01-06 | 1994-07-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-07-07 | 1998-01-06 | 1998-07-08 | $7700.00 | Window Closed / Lapsed |