Processing of copper alloys
Assignee: Materion Brush Inc
•
Filing: 1985-02-25
•
Granted: 1986-07-08
•
Expires: 2005-02-25
Abstract
Abstract This invention is directed to the treatment of copper beryllium alloys, and to articles and parts made therefrom, containing special small amounts of beryllium and nickel, e.g., about 0.05% to about 0.5% beryllium and about 0.05% to about 1% nickel where cobalt may be substituted for up to about one-half of said nickel content at a substitution ratio of about 1 part by weight cobalt for about 2 parts by weight nickel, which imparts to these alloys a superior combination of stress relaxation resistance, formability, ductility, conductivity and strength by the process of solution annealing, cold working at least about 50% or at least about 70% or 90% or more and age hardening.
Inventors
- 👤 Nathan L. Church
- 👤 W. Raymond Cribb
- 👤 John C. Harkness
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 15:54
CPC Classifications
C; C22; C22F; C22F1/00; C22F1/08; B; B23; B23K; B23K35/00; B23K35/40; B23K35/402
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
170 words
An article made from wrought copper-beryllium alloy material consisting essentially of about 0.05% to about 0.5% beryllium, about 0.05% to about 1% nickel where cobalt may be substituted for up to one-half of said nickel content at a substitution ratio of about 1 part by weight cobalt for about 2 parts by weight nickel, and the balance essentially copper by solution treating said alloy in wrought intermediate form at a temperature between about 1600° F. (870° C.) and about 1850° F. (1000° C.) for a time sufficient to effect recrystallization and solid solution of that portion of the alloying elements capable of contributing to precipitation hardening, subjecting said solution treated alloy to a final cold reduction of at least about 50% and aging said cold worked alloy at a temperature in the range of about 600° F. (315° C.) to about 1000° F. (540° C.) for less than one to about 8 hours to effect precipitation hardening with accompanying substantial increase in stress relaxation resistance, formability, ductility, conductivity and strength.
Claim 2
Dependent Claim
170 words
An article made from wrought copper-beryllium alloy material consisting essentially of about 0.05% to about 0.5% beryllium, about 0.05% to about 1% nickel where cobalt may be substituted for up to one-half of said nickel content at a substitution ratio of about 1 part by weight cobalt for about 2 parts by weight nickel, and the balance essentially copper by solution treating said alloy in wrought intermediate form at a temperature between about 1600° F. (870° C.) and about 1850° F. (1000° C.) for a time sufficient to effect recrystallization and solid solution of that portion of the alloying elements capable of contributing to precipitation hardening, subjecting said solution treated alloy to a final cold reduction of at least about 50% and aging said cold worked alloy at a temperature in the range of about 600° F. (315° C.) to about 1000° F. (540° C.) for less than one to about 8 hours to effect precipitation hardening with accompanying substantial increase in stress relaxation resistance, formability, ductility, conductivity and strength.
Claim 3
Dependent Claim
112 words
An article in accordance with claim 1 wherein said copper-beryllium alloy material consists essentially of at least about 0.15% beryllium and at least 0.2% nickel and has in said cold reduced and aged condition a "stress-remaining" value of at least about 80% in the stress relaxation test for 500 hours at 300° F. (150° C.) and an initial stress of 75% of the 0.2% offset yield strength, a yield strength (0.2% offset) of at least about 70 ksi (480 MPa) to about 120 ksi (900 MPa), a formability value R/t of no more than 3.5 longitudinal and no more than about 9.0 transverse, and a conductivity of at least about 35% I.A.C.S.
Claim 4
Dependent Claim
31 words
An article in accordance with claim 1 comprising a contact element characterized in use by high resistance to stress relaxation upon exposure to temperatures up to about 300° F. (150° C.).
Claim 5
Dependent Claim
57 words
An article in accordance with claim 1 comprising a lead frame or similar device made from material consisting essentially of no more than about 0.2% beryllium and no more than about 0.2% nickel and characterized by an electrical conductivity exceeding about 60% IACS and an 0.2% offset yield strength of at least about 50 ksi (345 MPa).
Claim 6
Dependent Claim
53 words
An article in accordance with claim 1 in the form of at least one shape from the group consisting of strip, wire, rod, bar and tubing, said shape being made of an alloy having a beryllium content of about 0.2% to about 0.5% and a nickel content of about 0.2% to about 1%.
References Cited (Backward Citations)
US2169190A
Cited
US2289593A
Cited
JPS53112222A
Cited
US4179314A
Cited
JPS56122155A
Cited
US4377424A
Cited
US4425168A
Cited
JPS5961154A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-07-07 | 1990-01-06 | 1990-07-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-07-07 | 1994-01-06 | 1994-07-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-07-07 | 1998-01-06 | 1998-07-08 | $7700.00 | Window Closed / Lapsed |