US4597958A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of producing hydrated iron oxide
Assignee: Mitsui Kinzoku Co Ltd
•
Filing: 1984-09-17
•
Granted: 1986-07-01
•
Expires: 2004-09-17
Abstract
Abstract In a method of producing a hydrated iron oxide as a starting material for a magnetic powder by aging a suspension of a ferric hydroxide prepared by reacting a ferric salt with an aqueous solution of alkali, the aging temperature is controlled between 20 DEG and 100 DEG C. and pH is controlled between 1 and 6 for the first 5 to 240 minutes while nuclei of hydrated iron oxide crystals generate, and then the aqueous solution of alkali is added again to adjust the pH value to 10 to 13.5 to make the crystals grow. This production method is capable of producing an acicular hydrated iron oxide having a reduced particle-size distribution range and also capable of controlling the length of the crystals as desired.
Inventors
- 👤 Nobuo Takagi
- 👤 Masakazu Konno
- 👤 Takeo Kobayashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 05:44
CPC Classifications
C; C01; C01G; C01G49/00; C01G49/02; C01G49/06; G; G11; G11B; G11B5/00; G11B5/62; G11B5/68; G11B5/70; G11B5/706; G11B5/70626; G11B5/70642; G11B5/70652; C01P; C01P2004/00; C01P2004/01; C01P2004/03; C01P2004/10; C01P2004/54; C01P2004/60; C01P2004/62
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
157 words
A method for the production of acicular iron oxide hydroxide which comprises: (a) forming an aqueous solution having a pH in the range of 2.5 to 4 from a ferric salt and an alkali by adding an aqueous solution of the alkali to an aqueous solution of the ferric salt; (b) maintaining said solution at said pH under conditions of continouos agitation at a temperature in the range of 20° to 100° C. for a period of time in the range of 5 to 240 minutes to effect formation of a suspension of nuclei crystals of an iron oxide hydroxide; (c) thereafter adjusting the pH of the suspension to a value within the range of 10 to 13.5 by the addition of an alkali and aging the suspension for a period of about four hours at a temperature in the range of 20° to 100° C. to effect the growth of acicular crystals of iron oxide hydroxide.
Claim 2
Independent Claim
157 words
A method for the production of acicular iron oxide hydroxide which comprises: (a) forming an aqueous solution having a pH in the range of 2.5 to 4 from a ferric salt and an alkali by adding an aqueous solution of the alkali to an aqueous solution of the ferric salt; (b) maintaining said solution at said pH under conditions of continouos agitation at a temperature in the range of 20° to 100° C. for a period of time in the range of 5 to 240 minutes to effect formation of a suspension of nuclei crystals of an iron oxide hydroxide; (c) thereafter adjusting the pH of the suspension to a value within the range of 10 to 13.5 by the addition of an alkali and aging the suspension for a period of about four hours at a temperature in the range of 20° to 100° C. to effect the growth of acicular crystals of iron oxide hydroxide.
Claim 3
Dependent Claim
19 words
A method according to claim 1 wherein the pH of the aqueous solution in step (a) is about 2.9.
Claim 4
Dependent Claim
25 words
A method according to claim 1 wherein the pH of the crystal growth suspension in step (c) is in the range of 11 to 13.
Claim 5
Dependent Claim
25 words
A method according to claim 1, wherein said ferric salt is selected from the group consisting of a ferric sulfate, ferric chloride and ferric nitrate.
Claim 6
Dependent Claim
16 words
A method according to claim 1, wherein said iron oxide hydroxide is an α-FeOOH or β-FeOOH.
Claim 7
Dependent Claim
20 words
A method according to claim 1 wherein said ferric salt is prepared by oxidizing a ferrous salt by hydrogen peroxide.
Claim 8
Dependent Claim
27 words
A method according to claim 1, wherein said alkali is selected from the group consisting of sodium hydroxide, potassium hydroxide, sodium carbonate, sodium bicarbonate and ammonium carbonate.
Claim 9
Dependent Claim
21 words
A method according to claim 1 wherein said iron oxide hydroxide has an average particle size between 0.1 and 0.5 μ.
Claim 10
Dependent Claim
21 words
A method according to claim 1 wherein said iron oxide hydroxide has a particle-size distribution ranging from 0.05 to 1 μ.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-06-30 | 1989-12-30 | 1990-07-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-06-30 | 1993-12-30 | 1994-07-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-06-30 | 1997-12-30 | 1998-07-01 | $7700.00 | Window Closed / Lapsed |