Treatment process for removing fluoride impurities from aluminosilicates

Claim 2

The process for treating fluoride-containing aluminosilicates to decrease the amount of insoluble fluoride compounds contained therein comprising treating said fluoride-containing aluminosilicate with an effective amount of a solution of a soluble aluminum compound at an effective temperature and for an effective time whereby the amount of insoluble fluoride compounds associated with said aluminosilicate is decreased.

Claim 3

The process of claim 1 wherein said aluminosilicate has been prepared by inserting silicon atoms as SiO 4 tetrahedra into the crystal lattice of a crystalline aluminosilicate having a SiO 2 /Al 2 O 3 molar ratio of at least 3 and pore diameters of at least 3 Angstroms by contacting said aluminosilicate with a fluorosilicate salt in an amount of at least 0.0075 moles per 100 grams of the aluminosilicate on an anhydrous basis, said fluorosilicate salt being in the form of an aqueous solution having a pH value within the range of 3 to about 7 and brought into contact with the aluminosilicate at a rate sufficiently slow to preserve at least 60 percent of the crystallinity of the starting aluminosilicate.

Claim 4

The process of claim 1 wherein the effective temperature is between about 20° C. and about 95° C.

Claim 5

The process of c-aim 3 wherein the effective temperature is between about 20° C. and about 75° C.

Claim 6

The process of c-aim 3 wherein the effective temperature is between about 20° C. and about 75° C.

Claim 7

The process of claim 1 wherein the fluoride is a fluoroaluminate.

Claim 8

The process of claim 1 wherein the soluble aluminum compound is at least one of aluminum sulfate, aluminum nitrate, aluminum chloride, organic salts and complexes of aluminum, aluminum hydroxide and mixtures thereof.

Claim 9

The process of claim 6 wherein the soluble aluminum compound is provided as a water solution.

Claim 10

The process of claim 7 whereby the fluoride compounds are removed at a rate greater than that obtained by the use of water without the soluble aluminum compounds.

Claim 11

The process of claim 1 wherein the mole ratio of fluoride to aluminum cation in the treatment is less than 3.

Claim 12

The process of claim 9 wherein the mole ratio of fluoride to aluminum cation in the treatment is between about 2.0 and about 2.5.

Claim 13

The process of claim 1 wherein said aluminosilicate comprises a component of a fluoride-containing catalyst.

Claim 14

The process of claim 2 wherein said aluminosilicate comprises a component of a fluoride-containing catalyst.