Lithium-containing neutron target particle
Assignee: General Atomics Corp
•
Filing: 1983-10-12
•
Granted: 1986-07-01
•
Expires: 2003-10-12
Abstract
Abstract To provide a lithium-containing neutron target particle for breeding tritium within the core of a nuclear reactor, including a central core formed of a stable lithium-containing compound, a surrounding buffer layer, and an outer tritium-impermeable silicon carbide coating, the core is initially sealed with an inner sealing layer of pyrolytic carbon and an outer sealing layer of stoichiometric zirconium carbide. The pyrocarbon seal protects the lithium within the core from attack from the zirconium carbide coating atmosphere, and the zirconium carbide layer prevents loss of lithium from the core when the silicon carbide coating is deposited at elevated temperatures.
Inventors
- 👤 James L. Kaae
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 13:31
CPC Classifications
H; H05; H05H; H05H6/00
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
68 words
A neutron target particle for breeding tritium comprising a central generally spherical core formed of a lithium-containing compound which is stable under coating conditions and conditions within the core of a nuclear reactor, a pyrocarbon seal layer covering said core, a zirconium carbide seal layer covering said pyrocarbon seal layer, a porous pyrocarbon buffer layer surrounding said seal layers, and a silicon carbide coating surrounding said buffer layer.
Claim 2
Dependent Claim
68 words
A neutron target particle for breeding tritium comprising a central generally spherical core formed of a lithium-containing compound which is stable under coating conditions and conditions within the core of a nuclear reactor, a pyrocarbon seal layer covering said core, a zirconium carbide seal layer covering said pyrocarbon seal layer, a porous pyrocarbon buffer layer surrounding said seal layers, and a silicon carbide coating surrounding said buffer layer.
Claim 3
Dependent Claim
19 words
A particle according to claim 1 wherein said core is between about 300 and about 1000 microns in diameter.
Claim 4
Dependent Claim
28 words
A particle according to claim 1 wherein said core is formed of a compound selected from the group consisting of LiAlO 2 and LiAl 5 O 8 .
Claim 5
Dependent Claim
22 words
A particle according to claim 1 wherein said core has a density between about 70 and about 100 percent of theoretical density.
Claim 6
Dependent Claim
33 words
A particle according to claim 1 wherein said pyrocarbon seal layer has a density of between about 1.8 and about 2.0 gm/cm 3 and a thickness between about 30 and about 40 microns.
Claim 7
Dependent Claim
91 words
A neutron target particle for breeding tritium comprising a central generally spherical core formed of a lithium-containing compound which is stable under coating conditions and conditions within the core of a nuclear reactor, a pyrocarbon seal layer covering said core, a zirconium carbide seal layer at least about 10 microns thick covering said pyrocarbon seal layer, said zirconium carbide having the formula ZrC x where x is between about 0.9 and about 1.0, a porous pyrocarbon buffer layer surrounding said seal layers, and a silicon carbide coating surrounding said buffer layer.
Claim 8
Dependent Claim
91 words
A neutron target particle for breeding tritium comprising a central generally spherical core formed of a lithium-containing compound which is stable under coating conditions and conditions within the core of a nuclear reactor, a pyrocarbon seal layer covering said core, a zirconium carbide seal layer at least about 10 microns thick covering said pyrocarbon seal layer, said zirconium carbide having the formula ZrC x where x is between about 0.9 and about 1.0, a porous pyrocarbon buffer layer surrounding said seal layers, and a silicon carbide coating surrounding said buffer layer.
Claim 9
Dependent Claim
22 words
A particle according to claim 6 wherein said zirconium carbide layer has a thickness of between about 10 and about 30 microns.
Claim 10
Dependent Claim
33 words
A particle according to claim 1 wherein said buffer layer has a density of between about 0.9 and about 1.2 gram/cm 3 and a thickness of between about 30 and about 100 microns.
Claim 11
Dependent Claim
20 words
A particle according to claim 1 wherein said SiC coating has a density of above about 98% of theoretical density.
Claim 12
Dependent Claim
40 words
A particle according to claim 1 having a pyrocarbon layer with a density of between about 1.7 and about 2.0 gm/cm 3 and a thickness between about 35 and about 45 microns between said buffer layer and said SiC coating.
Claim 13
Dependent Claim
37 words
A particle according to claim 1 having a pyrocarbon layer with a density of between about 1.7 and about 2.0 gm/cm 3 and a thickness of between about 35 and about 45 microns around said SiC coating.
Claim 14
Independent Claim
147 words
A method of forming a neutron target particle comprising, forming a generally spherical core from a lithium-containing compound, sealing said core by depositing pyrocarbon on said core at a temperature below about 1300° C. to a thickness of at least about 10 microns, and a density of at least about 1.8 grams/cm 3 , further sealing said core by pyrolytically depositing on said pyrocarbon seal layer, at a temperature below about 1320° C., zirconium carbide to a thickness of at least about 10 microns, depositing on said zirconium carbide layer a porous pyrocarbon buffer layer having a thickness of between about 30 and about 100 microns and a density of between about 0.9 and about 1.2 gram/cm 3 , and pyrolytically coating said particle with SiC to a thickness of at least about 35 microns and a density of at least about 98 percent of theoretical density.
Claim 15
Independent Claim
147 words
A method of forming a neutron target particle comprising, forming a generally spherical core from a lithium-containing compound, sealing said core by depositing pyrocarbon on said core at a temperature below about 1300° C. to a thickness of at least about 10 microns, and a density of at least about 1.8 grams/cm 3 , further sealing said core by pyrolytically depositing on said pyrocarbon seal layer, at a temperature below about 1320° C., zirconium carbide to a thickness of at least about 10 microns, depositing on said zirconium carbide layer a porous pyrocarbon buffer layer having a thickness of between about 30 and about 100 microns and a density of between about 0.9 and about 1.2 gram/cm 3 , and pyrolytically coating said particle with SiC to a thickness of at least about 35 microns and a density of at least about 98 percent of theoretical density.
Claim 16
Dependent Claim
35 words
A mehod according to claim 12 wherein said ZrC layer is deposited by pyrolytic decomposition of a mixture of a zirconium halide and a hydrocarbon selected from the group consisting of acetylene, propane and propylene.
Claim 17
Dependent Claim
39 words
A method according to claim 12 wherein depositing said zirconium carbide is carried out using a gas mixture and temperature appropriate to form zirconium carbide having the formula ZrC x where x is between about 0.9 and about 1.0.
Claim 18
Dependent Claim
22 words
A particle according to claim 1 wherein said zirconium carbide layer has a thickness of between about 10 and about 30 microns.
Claim 19
Dependent Claim
19 words
A particle according to claim 6 wherein said core is between about 300 and about 1000 microns in diameter.
Claim 20
Dependent Claim
28 words
A particle according to claim 6 wherein said core is formed of a compound selected from the group consisting of LiAlO 2 and LiAl 5 O 8 .
Claim 21
Dependent Claim
22 words
A particle according to claim 6 wherein said core has a density between about 70 and about 100 percent of theoretical density.
Claim 22
Dependent Claim
33 words
A particle according to claim 6 wherein said pyrocarbon seal layer has a density of between about 1.8 and about 2.0 gm/cm 3 and a thickness between about 30 and about 40 microns.
Claim 23
Dependent Claim
20 words
A particle according to claim 6 wherein said SiC coating has a density of above about 98% of theoretical density.
References Cited (Backward Citations)
US3089785A
Cited
US3151037A
Cited
US3122595A
Cited
US3312597A
Cited
US3276968A
Cited
US3301763A
Cited
US3669832A
Cited
US3649452A
Cited
US3554783A
Cited
US3907948A
Cited
US3650896A
Cited
US3736169A
Cited
US3804664A
Cited
US3846154A
Cited
US3798123A
Cited
US3878041A
Cited
US3992258A
Cited
US4077838A
Cited
US4267019A
Cited
US4405595A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-06-30 | 1989-12-30 | 1990-07-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-06-30 | 1993-12-30 | 1994-07-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-06-30 | 1997-12-30 | 1998-07-01 | $7700.00 | Window Closed / Lapsed |