Methods of forming denuded zone in wafer by intrinsic gettering and forming bipolar transistor therein
Assignee: Fujitsu Ltd
•
Filing: 1984-04-12
•
Granted: 1986-07-01
•
Expires: 2004-04-12
Abstract
Abstract A variety of methods are applicable to production of semiconductor devices in which the active layer is produced in a denuded zone which is thin and free of defects. This denuded zone in combination with a high concentration of crystalline defects contained in a deep layer of the semiconductor device, allows the semiconductor device to enjoy the function of the intrinsic gettering effect. A variety of improvements, including a decrease in the overall production time, removal of limitations due to the oxygen concentration of a wafer, etc. is realized by introducing an idea that the annealing temperature is increased and/or decreased gradually at a predetermined rate. A variety of such improved annealing processes being combined with each other and/or to a variety of conventional annealing processes, aiming at a higher magnitude of the intrinsic gettering effect. This improvement is further modified to be combined with epitaxy to diversify the uses of a denuded zone.
Inventors
- 👤 Kazunori Imaoka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 12:00
CPC Classifications
H; H10; H10P; H10P95/00; H10P95/90; H10D; H10D62/00; H10D62/80; H10D62/83; H10D62/834; H10P36/00; H10P36/20
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
136 words
A method for producing a semiconductor device on a silicon wafer utilizing the function of the intrinsic gettering effect or a silicon wafer having a shallow or surface zone which is a denuded zone and a having deep or internal region containing a high concentration of crystalline defects which are large in size, comprising the step of annealing the silicon wafer at an annealing temperature selected from a range of 500° through 1300° C. by heating the silicon wafer such that the annealing temperature corresponds to a first temperature selected from a range of 500° through 900° C., and increasing the annealing temperature to a second temperature selected from a range of 950° through 1300° C., the annealing temperature being increased from the first temperature to the second temperature at a rate not exceeding 14° C./min.
Claim 2
Independent Claim
136 words
A method for producing a semiconductor device on a silicon wafer utilizing the function of the intrinsic gettering effect or a silicon wafer having a shallow or surface zone which is a denuded zone and a having deep or internal region containing a high concentration of crystalline defects which are large in size, comprising the step of annealing the silicon wafer at an annealing temperature selected from a range of 500° through 1300° C. by heating the silicon wafer such that the annealing temperature corresponds to a first temperature selected from a range of 500° through 900° C., and increasing the annealing temperature to a second temperature selected from a range of 950° through 1300° C., the annealing temperature being increased from the first temperature to the second temperature at a rate not exceeding 14° C./min.
Claim 3
Dependent Claim
67 words
A method for producing a semiconductor device, utilizing the function of the intrinsic gettering effect, as defined in claim 1, wherein said annealing step comprises increasing the annealing temperature from the first temperature to the second temperature at a rate selected from a range of 5° through 14° C./min, and wherein the silicon wafer contains a concentration of oxygen in excess of 1.5×10 18 /cm 3 .
Claim 4
Dependent Claim
61 words
A method for producing a semiconductor device, utilizing the function of the intrinsic gettering effect, as defined in claim 1, wherein said annealing step comprises increasing the annealing temperature from the first temperature to the second temperature at a rate not exceeding 5° C./min, and wherein the silicon wafer contains a concentration of oxygen not exceeding 15×10 18 /cm 3 .
Claim 5
Independent Claim
144 words
A method for producing a semiconductor device employing a silicon wafer having a shallow region which is a denuded zone and having a deep region containing a high concentration of crystalline defects which are large in size, comprising the steps of: (a) annealing the silicon wafer by heating the silicon wafer such that the annealing temperature corresponds to a first temperature selected from a range of 500° through 900° C.; (b) annealing the silicon wafer at a second temperature selected from a range of 950° through 1300° C.; and (c) decreasing the annealing temperature from the second temperature to the first temperature, said annealing steps (a) and (b) including increasing the first temperature to the second temperature and decreasing the second temperature to the first temperature, both the rate of increase and decrease in temperature being selected from a rate not exceeding 14° C./min.
Claim 6
Independent Claim
144 words
A method for producing a semiconductor device employing a silicon wafer having a shallow region which is a denuded zone and having a deep region containing a high concentration of crystalline defects which are large in size, comprising the steps of: (a) annealing the silicon wafer by heating the silicon wafer such that the annealing temperature corresponds to a first temperature selected from a range of 500° through 900° C.; (b) annealing the silicon wafer at a second temperature selected from a range of 950° through 1300° C.; and (c) decreasing the annealing temperature from the second temperature to the first temperature, said annealing steps (a) and (b) including increasing the first temperature to the second temperature and decreasing the second temperature to the first temperature, both the rate of increase and decrease in temperature being selected from a rate not exceeding 14° C./min.
Claim 7
Independent Claim
166 words
A method for producing a semiconductor device on a silicon wafer utilizing the function of the intrinsic gettering effect, or a silicon wafer having a shallow or surface region which is a denuded zone and having a deep or internal region containing a high concentration of crystalline defects which are large in size, comprising the steps of: (a) annealing the silicon wafer at an annealing temperature selected from a range of 500° through 1300° C. by heating the silicon wafer such that the annealing temperature corresponds to a first temperature selected from a range of 500° through 900° C. and increasing the annealing temperature to a second temperature selected from a range of 950° through 1300° C., the annealing temperature being increased from the first temperature to the second temperature at a rate not exceeding 14° C./min.; and (b) growing a silicon epitaxial layer on the silicon wafer, the silicon epitaxial layer comprising at least one impurity and having a thickness between 2 and 27 micrometers.
Claim 8
Independent Claim
166 words
A method for producing a semiconductor device on a silicon wafer utilizing the function of the intrinsic gettering effect, or a silicon wafer having a shallow or surface region which is a denuded zone and having a deep or internal region containing a high concentration of crystalline defects which are large in size, comprising the steps of: (a) annealing the silicon wafer at an annealing temperature selected from a range of 500° through 1300° C. by heating the silicon wafer such that the annealing temperature corresponds to a first temperature selected from a range of 500° through 900° C. and increasing the annealing temperature to a second temperature selected from a range of 950° through 1300° C., the annealing temperature being increased from the first temperature to the second temperature at a rate not exceeding 14° C./min.; and (b) growing a silicon epitaxial layer on the silicon wafer, the silicon epitaxial layer comprising at least one impurity and having a thickness between 2 and 27 micrometers.
Claim 9
Dependent Claim
35 words
A method for producing a semiconductor device utilizing the function of the intrinsic gettering effect as defined in claim 5, wherein the annealing temperature of said annealing step (a) is increased to approximately 1,100° C.
Claim 10
Dependent Claim
53 words
A method for producing a semiconductor device, utilizing the function of the intrinsic gettering effect, as defined in claim 5 or 6, wherein said annealing step (a) comprises the substeps of: increasing the temperature at a first rate; and increasing the temperature at a second rate greater than that of the first rate.
Claim 11
Independent Claim
255 words
A method for producing a bipolar transistor on a silicon wafer utilizing the function of the intrinsic gettering effect, or a silicon wafer having a shallow or surface region which is a denuded zone and having a deep or internal region containing a high concentration of crystalline defects which are large in size, comprising the steps of: (a) annealing the silicon wafer at an annealing temperature selected from a range of 500° through 1300° C. by heating the silicon wafer such that the annealing temperature corresponds to a first temperature selected from a range of 500° through 900° C., and increasing the annealing temperature to a second temperature selected from a range of 950° through 1300° C., the annealing temperature being increased from the first temperature to the second temperature at a rate not exceeding 14° C./min.; (b) growing, on the silicon wafer, a thin silicon epitaxial layer having a top portion and comprising at least one impurity; (c) introducing a high concentration of at least one impurity into a selected portion of the top portion of the thin silicon epitaxial layer for forming a buried layer; (d) growing, on the buried layer and the top portion of the thin silicon epitaxial layer, a thick silicon epitaxial layer comprising at least one impurity and having a thickness between 2 and 27 micrometers; and (e) forming base, emitter and collector regions in the thick silicon epitaxial layer, the impurity concentration of the buried layer being higher than the impurity concentration of the thick silicon epitaxial layer.
Claim 12
Independent Claim
255 words
A method for producing a bipolar transistor on a silicon wafer utilizing the function of the intrinsic gettering effect, or a silicon wafer having a shallow or surface region which is a denuded zone and having a deep or internal region containing a high concentration of crystalline defects which are large in size, comprising the steps of: (a) annealing the silicon wafer at an annealing temperature selected from a range of 500° through 1300° C. by heating the silicon wafer such that the annealing temperature corresponds to a first temperature selected from a range of 500° through 900° C., and increasing the annealing temperature to a second temperature selected from a range of 950° through 1300° C., the annealing temperature being increased from the first temperature to the second temperature at a rate not exceeding 14° C./min.; (b) growing, on the silicon wafer, a thin silicon epitaxial layer having a top portion and comprising at least one impurity; (c) introducing a high concentration of at least one impurity into a selected portion of the top portion of the thin silicon epitaxial layer for forming a buried layer; (d) growing, on the buried layer and the top portion of the thin silicon epitaxial layer, a thick silicon epitaxial layer comprising at least one impurity and having a thickness between 2 and 27 micrometers; and (e) forming base, emitter and collector regions in the thick silicon epitaxial layer, the impurity concentration of the buried layer being higher than the impurity concentration of the thick silicon epitaxial layer.
Claim 13
Dependent Claim
35 words
A method for producing a bipolar transistor, utilizing the function of the intrinsic gettering effect, as defined in claim 8, wherein the annealing temperature of said annealing step (a) is increased to approximately 1,100° C.
Claim 14
Dependent Claim
52 words
A method for producing a bipolar transistor, utilizing the function of the intrinsic gettering effect, as defined in claim 8 or 9, wherein said annealing step (a) comprises the substeps of: increasing the temperature at a first rate; increasing the temperature at a second rate greater than that of the first rate.
Claim 15
Independent Claim
132 words
A method for producing a semiconductor device on a silicon wafer utilizing the function of the intrinsic gettering effect or a silicon wafer having a shallow or surface region which is a denuded zone and having a deep or internal region containing a high concentration of large cyrstalline defects, comprising the step of annealing the silicon wafer at an annealing temperature selected from a range of 500° through 1300° C. by heating the silicon wafer so that the annealing temperature corresponds to a first temperature selected from a range of 500° to 900° C., and increasing the annealing temperature toward a second temperature selected from a range of 950° to 1300° C., the annealing temperature being increased from the first temperature toward the second temperature at a rate not exceeding 14° C./min.
Claim 16
Independent Claim
132 words
A method for producing a semiconductor device on a silicon wafer utilizing the function of the intrinsic gettering effect or a silicon wafer having a shallow or surface region which is a denuded zone and having a deep or internal region containing a high concentration of large cyrstalline defects, comprising the step of annealing the silicon wafer at an annealing temperature selected from a range of 500° through 1300° C. by heating the silicon wafer so that the annealing temperature corresponds to a first temperature selected from a range of 500° to 900° C., and increasing the annealing temperature toward a second temperature selected from a range of 950° to 1300° C., the annealing temperature being increased from the first temperature toward the second temperature at a rate not exceeding 14° C./min.
Claim 17
Dependent Claim
66 words
A method for producing a semiconductor device, utilizing the function of the intrinsic gettering effect, as defined in claim 11, wherein said annealing step comprises increasing the annealing temperature from the first temperature toward the second temperature at a rate selected from a range of 5° to 14° C./min., and wherein the silicon wafer contains a concentration of oxygen greater than 1.5×10 18 /cm 3 .
Claim 18
Dependent Claim
61 words
A method for producing a semiconductor device, utilizing the function of the intrinsic gettering effect, as defined in claim 11, wherein said annealing step comprises increasing the annealing temperature from the first temperature toward the second temperature at a rate not exceeding 5° C./min., and wherein the silicon wafer contains a concentration of oxygen not exceeding 1.5×10 18 /cm 3 .
Claim 19
Independent Claim
175 words
A method for producing a semiconductor device on a silicon wafer utilizing the function of the intrinsic gettering effect or a silicon wafer having a shallow or surface region which is a denuded zone and having a deep or internal region containing a high concentration of large crystalline defects, comprising the steps of: (a) annealing the silicon wafer, at an annealing temperature selected from a range of 500° through 1300° C. by heating the silicon wafer, such that the annealing temperature corresponds to a first annealing temperature selected within the range of 950° C. through 1300° C., for a period of time from 10 minutes to 10 hours; (b) annealing the silicon wafer by heating the silicon wafer at a second annealing temperature selected within the range of 500° C. through 900° C.; and (c) increasing the annealing temperature toward a third annealing temperature selected within the range of 950° C. through 1300° C., the annealing temperature increased from the second annealing temperature toward the third annealing temperature at a rate not exceeding 14° C./min.
Claim 20
Independent Claim
175 words
A method for producing a semiconductor device on a silicon wafer utilizing the function of the intrinsic gettering effect or a silicon wafer having a shallow or surface region which is a denuded zone and having a deep or internal region containing a high concentration of large crystalline defects, comprising the steps of: (a) annealing the silicon wafer, at an annealing temperature selected from a range of 500° through 1300° C. by heating the silicon wafer, such that the annealing temperature corresponds to a first annealing temperature selected within the range of 950° C. through 1300° C., for a period of time from 10 minutes to 10 hours; (b) annealing the silicon wafer by heating the silicon wafer at a second annealing temperature selected within the range of 500° C. through 900° C.; and (c) increasing the annealing temperature toward a third annealing temperature selected within the range of 950° C. through 1300° C., the annealing temperature increased from the second annealing temperature toward the third annealing temperature at a rate not exceeding 14° C./min.
Claim 21
Dependent Claim
42 words
A method for producing a semiconductor device, utilizing the function of the intrinsic gettering effect, as defined in claim 14, wherein said increasing step (c) comprises increasing the annealing temperature from the second annealing temperature at a rate not exceeding 5° C./min.
Claim 22
Independent Claim
177 words
A method for producing a semiconductor device in a silicon wafer utilizing the function of the intrinsic gettering effect or a silicon wafer having a shallow or surface region which is a denuded zone and having a deep or internal region containing a high concentration of large crystalline defects, comprising the steps of: (a) annealing the silicon wafer at an annealing temperature selected from a range of 500° through 1300° C. by heating the silicon wafer such that the annealing temperature corresponds to a first temperature selected from a range of 950° through 1300° C., for a period of time from 10 minutes to 10 hours; (b) decreasing the annealing temperature from the first annealing temperature; (c) increasing the annealing temperature through a second temperature selected from a range of 500° through 900° C. toward a third temperature selected from a range of 950° through 1300° C., the annealing temperature being increased from the second temperature toward the third temperature at a rate not exceeding 14° C./min.; and (d) annealing the silicon wafer at the third temperature.
Claim 23
Independent Claim
177 words
A method for producing a semiconductor device in a silicon wafer utilizing the function of the intrinsic gettering effect or a silicon wafer having a shallow or surface region which is a denuded zone and having a deep or internal region containing a high concentration of large crystalline defects, comprising the steps of: (a) annealing the silicon wafer at an annealing temperature selected from a range of 500° through 1300° C. by heating the silicon wafer such that the annealing temperature corresponds to a first temperature selected from a range of 950° through 1300° C., for a period of time from 10 minutes to 10 hours; (b) decreasing the annealing temperature from the first annealing temperature; (c) increasing the annealing temperature through a second temperature selected from a range of 500° through 900° C. toward a third temperature selected from a range of 950° through 1300° C., the annealing temperature being increased from the second temperature toward the third temperature at a rate not exceeding 14° C./min.; and (d) annealing the silicon wafer at the third temperature.
Claim 24
Dependent Claim
49 words
A method for producing a semiconductor device on a silicon wafer utilizing the function of the intrinsic gettering effect as set forth in claim 2, wherein said step of increasing the annealing temperature from the first temperature to the second temperature is at a rate not exceeding 14° C./min.
Claim 25
Dependent Claim
49 words
A method for producing a semiconductor device on a silicon wafer utilizing the function of the intrinsic gettering effect as set forth in claim 3, wherein said step of increasing the annealing temperature from the first temperature to the second temperature is at a rate not exceeding 14° C./min.
Claim 26
Dependent Claim
51 words
A method for producing a semiconductor device on a silicon wafer utilizing the function of the intrinsic gettering effect as set forth in claim 4, further comprising the step of employing an oxidizing gas as an atmosphere for producing a gate oxide film on the silicon wafer by a thermal process.
Claim 27
Dependent Claim
40 words
A method for producing a semiconductor device on a silicon wafer utilizing the function of the intrinsic gettering effect as set forth in claim 4, further comprising selecting the temperature increase rate from a range of 5° through 14° C./min.
Claim 28
Dependent Claim
54 words
A method for producing a semiconductor device on a silicon wafer utilizing the function of the intrinsic gettering effect as set forth in claim 1, wherein said annealing step comprises increasing the annealing temperature from the first temperature to the second temperature at a rate selected from a range of 1° through 14° C./min.
Claim 29
Dependent Claim
54 words
A method for producing a semiconductor device on a silicon wafer utilizing the function of the intrinsic gettering effect as set forth in claim 11, wherein said annealing step comprises increasing the annealing temperature from the first temperature to the second temperature at a rate selected from a range of 1° through 14° C./min.
Claim 30
Dependent Claim
52 words
A method for producing a semiconductor device on a silicon wafer utilizing the function of the intrinsic gettering effect as set forth in claim 14, wherein said step (c) comprises increasing the second annealing temperature toward the third annealing temperature at a rate selected from the range of 1° through 5° C./min.
Claim 31
Dependent Claim
53 words
A method for producing a semiconductor device on a silicon wafer utilizing the function of the intrinsic gettering effect as set forth in claim 15, wherein said step (c) further comprises increasing the second annealing temperature toward the third annealing temperature at a rate selected from the range of 1° through 5° C./min.
Claim 32
Dependent Claim
50 words
A method for producing a semiconductor device on a silicon wafer utilizing the function of the intrinsic gettering effect as set forth in claim 16, wherein said step (c) comprises increasing the second temperature toward the third temperature at a rate selected from the range of 1° through 5° C./min.
References Cited (Backward Citations)
US4116719A
Cited
US4144099A
Cited
US4149905A
Cited
US4220483A
Cited
US4314595A
Cited
US4332627A
Cited
US4231809A
Cited
JPS5640250A
Cited
JPS5649532A
Cited
US4376657A
Cited
US4437922A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-06-30 | 1989-12-30 | 1990-07-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-06-30 | 1993-12-30 | 1994-07-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-06-30 | 1997-12-30 | 1998-07-01 | $7700.00 | Window Closed / Lapsed |