Abstract A vinyl repair compound and two step vinyl repair method provide an exceptionally strong and long wearing repair. The repair compound includes vinyl resins, a solvent, a plasticizer and silica filler, has a paste-like consistency and air dries. The repair process entails the following: trimming away the damaged material, placing backing material behind the damaged area if necessary, filling the repair area flush with the surface of the surrounding material with the repair compound and allowing it to air dry. Due to shrinkage of the compound as it dries, a depression is formed which is then filled with a conventional heat curable plastisol vinyl repair compound. If necessary, smooth or grained release paper is placed over the repair area, heat is applied to cure the plastisol compound and the repair is allowed to cool.
A composition for repairing vinyl and similar materials comprising: a mixture of between 40 and 60 percent dry powder vinyl resins, between 25 and 35 percent methylisobutylketone solvent, about 10 to 20 percent silica filler and about 2 to 5 percent plasticizer.
Claim 2
Dependent Claim
42 words
A composition for repairing vinyl and similar materials comprising: a mixture of between 40 and 60 percent dry powder vinyl resins, between 25 and 35 percent methylisobutylketone solvent, about 10 to 20 percent silica filler and about 2 to 5 percent plasticizer.
Claim 3
Dependent Claim
40 words
The vinyl repair composition of claim 1 wherein said 40 to 60 percent of dry powder vinyl resins includes at least two distinct resins, two of said at least two distinct resins each comprising approximately 26 percent of said composition.
Claim 4
Dependent Claim
18 words
The vinyl repair composition of claim 1 wherein said methylisobutylketone solvent comprises approximately 30 percent of said compound.
Claim 5
Dependent Claim
18 words
The vinyl repair composition of claim 1 wherein said silica filler comprises approximately 15 percent of said compound.
Claim 6
Dependent Claim
17 words
The vinyl repair composition of claim 1 wherein said plasticizer comprises approximately 3 percent of said compound.
Claim 7
Dependent Claim
42 words
A composition for repairing vinyl and similar materials comprising: a mixture of between 45 and 55 percent dry powder vinyl resins, between 28 and 32 percent methylisobutyliketone solvent, between 13 and 17 percent silica filler and between 3 and 4 percent plasticizer.
Claim 8
Dependent Claim
42 words
A composition for repairing vinyl and similar materials comprising: a mixture of between 45 and 55 percent dry powder vinyl resins, between 28 and 32 percent methylisobutyliketone solvent, between 13 and 17 percent silica filler and between 3 and 4 percent plasticizer.