Tough Si3 N4 composite ceramics
Assignee: Boeing North American Inc
•
Filing: 1985-08-30
•
Granted: 1986-06-24
•
Expires: 2005-08-30
Abstract
Abstract A tough Si 3 N 4 ceramic composite is provided by incorporating a ternary oxide additive containing hafnia, titania and zirconia. The ternary oxide additive consists essentially of 60 to 85 mole percent hafnia, 10 to 30 mole percent titania and 10 to 30 mole percent zirconia, and is added to the Si 3 N 4 in a proportion ranging from about 10 to about 50%, by volume of ternary oxide additive, based on the overall composition. The ceramic composites are prepared by providing a mixture of the Si 3 N 4 and the ternary oxide additive, forming the mixture into a predetermined shape, e.g. by cold pressing, and sintering the shape at an appropriate temperature, to solidify and densify the shape.
Inventors
- 👤 Harry W. Carpenter
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 12:31
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/584; C04B35/593
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
91 words
A composition for producing a tough Si 3 N 4 ceramic composite, which comprises a powder mixture of (a) about 50% or more by volume of Si 3 N 4 and (b) a ternary oxide additive containing 60 or more mole percent hafina, 10 to 30 mole percent titania and 10 to 30 mole percent zirconia, said oxide additive having a lower coefficient of thermal expansion than Si 3 N 4 , said composition containing about 10% to about 50% by volume of ternary oxide additive based on the overall composition.
Claim 2
Dependent Claim
91 words
A composition for producing a tough Si 3 N 4 ceramic composite, which comprises a powder mixture of (a) about 50% or more by volume of Si 3 N 4 and (b) a ternary oxide additive containing 60 or more mole percent hafina, 10 to 30 mole percent titania and 10 to 30 mole percent zirconia, said oxide additive having a lower coefficient of thermal expansion than Si 3 N 4 , said composition containing about 10% to about 50% by volume of ternary oxide additive based on the overall composition.
Claim 3
Dependent Claim
24 words
The composition of claim 1, said composition containing about 15% to about 30% by volume of ternary oxide additive based on the overall composition.
Claim 4
Dependent Claim
18 words
A tough Si 3 N 4 composite ceramic produced by forming and sintering the composition of claim 1.
Claim 5
Dependent Claim
18 words
A tough Si 3 N 4 composite ceramic produced by forming and sintering the composition of claim 2.
Claim 6
Independent Claim
119 words
A method for fabricating a tough Si 3 N 4 ceramic composite which comprises providing a powder mixture of (a) about 50% or more by volume of Si 3 N 4 and (b) a ternary oxide additive containing 60 or more mole percent hafnia, 10 to 30 mole percent titania and 10 to 30 mole percent zirconia, said oxide additive having a lower coefficient of thermal expansion than Si 3 N 4 , said composition containing about 10 to about 50% by volume of ternary oxide additive, based on the overall composition, forming said mixture into a predetermined shape, and sintering said shape to solidify and densify same as high as 98% of theoretical density or near theoretical density.
Claim 7
Independent Claim
119 words
A method for fabricating a tough Si 3 N 4 ceramic composite which comprises providing a powder mixture of (a) about 50% or more by volume of Si 3 N 4 and (b) a ternary oxide additive containing 60 or more mole percent hafnia, 10 to 30 mole percent titania and 10 to 30 mole percent zirconia, said oxide additive having a lower coefficient of thermal expansion than Si 3 N 4 , said composition containing about 10 to about 50% by volume of ternary oxide additive, based on the overall composition, forming said mixture into a predetermined shape, and sintering said shape to solidify and densify same as high as 98% of theoretical density or near theoretical density.
Claim 8
Dependent Claim
20 words
The method of claim 5, including forming said shape by cold pressing, isostatic pressing, extrusion, injecting molding or slip casting.
Claim 9
Dependent Claim
24 words
The method of claim 5, said composition containing about 15% to about 30% by volume of ternary oxide additive, based on the overall composition.
Claim 10
Dependent Claim
117 words
The method of claim 5, including the steps prior to forming said mixture into a predetermined shape, of providing an initial aqueous multiphase dispersion containing said hafnia, titania and zirconia components of said ternary oxide additive in the aforesaid proportions. removing particles greater than 1 micron size in said dispersion, filtering said dispersion, drying the filtered powder, forming said powder into a predetermined shape, heating said powder to form a solid solution of the three oxide components, crushing the resulting solid solution powder, forming an aqueous dispersion of said solid solution powder, mixing Si 3 N 4 of micron or submicron particle size in said aqueous dispersion, filtering said aqueous dispersion, and drying the resulting filtered powder.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-06-23 | 1989-12-23 | 1990-06-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-06-23 | 1993-12-23 | 1994-06-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-06-23 | 1997-12-23 | 1998-06-24 | $7700.00 | Window Closed / Lapsed |