Method of forming a glass sheet with a ceramic paint thereon
Assignee: Ford Motor Co
•
Filing: 1985-04-29
•
Granted: 1986-06-24
•
Expires: 2005-04-29
Abstract
Abstract This specification is directed to a method of forming a glass sheet with a ceramic paint thereon, the method having the following steps. A ceramic paint is applied to the glass sheet. The ceramic paint includes normal ceramic paint components along with, as a new component thereof, a metal oxide having at least a low valence oxidation state and a high valence oxidation state. The metal oxide is in its low valence state when applied in the ceramic paint to the glass sheet. The glass sheet is heated to a temperature which softens the glass sheet sufficiently so that the glass sheet can be formed. The glass sheet and the ceramic paint thereon are engaged with a fiberglass covered forming die to form the heated glass sheet to a desired shape. The forming die is removed from engagement with the glass sheet. The metal oxide addition to the ceramic paint in its low valence state is credited with being effective to prevent sticking of any of the ceramic paint to the forming die. The glass sheet is cooled to obtain a formed glass sheet with a ceramic paint thereon.
Inventors
- 👤 Premakaran T. Boaz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 09:43
CPC Classifications
C; C03; C03C; C03C8/00; C03C8/14; C03B; C03B23/00; C03B23/02; C03B23/023; C03B23/03
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
154 words
A method of forming a glass sheet with a ceramic paint thereon, which method comprises the steps of: applying a ceramic paint to said glass sheet, said ceramic paint including a metal oxide powder having at least a low valence oxidation state and a high valence oxidation state, said metal oxide powder being in its low valence state when applied; heating said glass sheet to a temperature which softens said glass sheet sufficiently so that said glass can be formed; engaging said glass sheet and said ceramic paint thereon with a fiberglass covered forming die to form said heated glass sheet to a desired shape; removing said forming die from engagement with said glass sheet, said metal oxide addition to said ceramic paint being effective to prevent sticking of any of said ceramic paint to said forming die; and cooling said glass sheet to obtain a formed glass sheet with a ceramic paint thereon.
Claim 2
Independent Claim
154 words
A method of forming a glass sheet with a ceramic paint thereon, which method comprises the steps of: applying a ceramic paint to said glass sheet, said ceramic paint including a metal oxide powder having at least a low valence oxidation state and a high valence oxidation state, said metal oxide powder being in its low valence state when applied; heating said glass sheet to a temperature which softens said glass sheet sufficiently so that said glass can be formed; engaging said glass sheet and said ceramic paint thereon with a fiberglass covered forming die to form said heated glass sheet to a desired shape; removing said forming die from engagement with said glass sheet, said metal oxide addition to said ceramic paint being effective to prevent sticking of any of said ceramic paint to said forming die; and cooling said glass sheet to obtain a formed glass sheet with a ceramic paint thereon.
Claim 3
Dependent Claim
140 words
The method of claim 1, wherein said ceramic paint comprises: a mixture of metal oxides which together act as a coloring agent for the ceramic paint, said metal oxides being nonreactive with one another and nonreactive with any elements or compounds they come in contact with while being heated to temperatures in a range up to 1300° F.; a low melting point glass frit; a metal oxide powder having at least a low valence oxidation state and a high valence oxidation state, said metal oxide being in its low valence oxidation state when formed into the ceramic paint; and a vehicle mixed with said metal oxides, low melting point glass frit, and metal oxide powder having at least two valence states to form all of said mentioned materials into a ceramic paint which can be applied to a glass surface.
Claim 4
Dependent Claim
28 words
The method of claim 2, wherein no vehicle is used in said ceramic paint composition and wherein an electrostatic deposition operaion is used to apply said ceramic paint.
Claim 5
Dependent Claim
155 words
The method of claim 1, wherein said ceramic paint composition, comprises: 8-25% by weight of a mixture of metal oxides which together act as a coloring agent for the ceramic paint, said metal oxides being nonreactive with one another and nonreactive with any elements or compounds they come in contact with while being heated to temperatures in a range up to 1300° F.; 30-50% by weight of a low melting point glass frit; 5-25% of a metal oxide powder having at least a low valence oxidation state and a high valence oxidation state, said metal oxide being in its low valence oxidation state when formed into the ceramic paint; and 0-35% by weight of a vehicle mixed with said metal oxides, low melting point glass frit, and metal oxide powder having at least two valence stales to form all of said mentioned materials into a ceramic paint which can be applied to a glass surface.
Claim 6
Dependent Claim
54 words
The method of claim 4, wherein in said ceramic paint composition said mixtre of metal oxides is present in an amount of 10-20% by weight, said low melting point glass frit is present in a range of 35-45% by weight, and said metal oxide powder is present in a range of 10-20% by weight.
Claim 7
Dependent Claim
13 words
The method of claim 5, wherein said metal oxide powder is stannous oxide.
Claim 8
Dependent Claim
52 words
The method of claim 4, wherein in said composition said mixture of metal oxides is present in an amount of 16% by weight, said low melting point glass frit is present in a range of 42% by weight, and said metal oxide powder is present in a range of 17% by weight.
Claim 9
Dependent Claim
13 words
The method of claim 7, wherein said metal oxide powder is stannous oxide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-06-23 | 1989-12-23 | 1990-06-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-06-23 | 1993-12-23 | 1994-06-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-06-23 | 1997-12-23 | 1998-06-24 | $7700.00 | Window Closed / Lapsed |