Blends of a polyglutarimide with a rubber-modified vinyl chloride resin
Assignee: Individual
•
Filing: 1985-05-02
•
Granted: 1986-06-17
•
Expires: 2005-05-02
Abstract
Abstract Thermoplastic blends having high heat distortion temperature and impact strength comprise 10-90 weight percent of a polyglutarimide, and 90-10 weight percent of a rubber-modified vinyl chloride resin prepared by polymerization of vinyl chloride in the presence of 2 to 50 percent of a rubber to form a graft copolymer.
Inventors
- 👤 Kenneth W. Doak
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 05:12
CPC Classifications
C; C08; C08L; C08L33/00; C08L33/24; C08L51/00; C08L51/04
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
111 words
A thermoplastic blend comprising: 10-90 percent by weight of a olyglutarimide prepared by reacting an acrylic polymer with an aminating agent selected from the group consisting of ammonia and an amine selected from the group consisting of alkyl and aryl amines containing 1 to 20 carbon atoms; and 90-100 percent by weight of a rubber-modified vinyl chloride resin prepared by polymerization of vinyl chloride in the presence of 2 to 50 percent, based on the weight of the resin, of a rubber to form a graft copolymer, which rubber-modified vinyl chloride resin contains 0-80 percent by weight of an unmodified vinyl chloride resin, based on the total weight of the resin.
Claim 2
Dependent Claim
111 words
A thermoplastic blend comprising: 10-90 percent by weight of a olyglutarimide prepared by reacting an acrylic polymer with an aminating agent selected from the group consisting of ammonia and an amine selected from the group consisting of alkyl and aryl amines containing 1 to 20 carbon atoms; and 90-100 percent by weight of a rubber-modified vinyl chloride resin prepared by polymerization of vinyl chloride in the presence of 2 to 50 percent, based on the weight of the resin, of a rubber to form a graft copolymer, which rubber-modified vinyl chloride resin contains 0-80 percent by weight of an unmodified vinyl chloride resin, based on the total weight of the resin.
Claim 3
Dependent Claim
19 words
The thermoplastic blend as defined in claim 1 wherein said polyglutarimide is prepared by reacting polymethyl methacrylate with ammonia.
Claim 4
Dependent Claim
20 words
The thermoplastic blend as defined in claim 1 wherein said polyglutarimide is prepared by reacting polymethyl methacrylate with methyl amine.
Claim 5
Dependent Claim
43 words
The thermoplastic blend as defined in claim 1 wherein said polyglutarimide is prepared by reacting a copolymer of methyl methacrylate and a minor amount of an ethylenically unsaturated comonomer with an aminating agent selected from the group consisting of ammonia and methyl amine.
Claim 6
Dependent Claim
30 words
The thermoplastic blend as defined in claim 1 wherein said rubber-modified vinyl chloride resin contains up to 20 percent by weight, of total monomers, of a copolymerizable, ethylenically unsaturated comonomer.
Claim 7
Dependent Claim
33 words
The thermoplastic blend as defined in claim 1 wherein said rubber-modified vinyl chloride resin contains an unmodified vinyl chloride resin in an amount of between 10-70 percent by weight of the total resin.
Claim 8
Dependent Claim
99 words
The thermoplastic blend as defined in claim 1 wherein there is added up to 40 weight percent, based on the weight of the total blend, of a copolymer selected from the group consisting of (a) a copolymer of a vinyl aromatic monomer and 20 to 40 percent by weight of an ethylenically unsaturated nitrile, (b) a copolymer of a vinyl aromatic monomer and 30 to 80 percent by weight of methyl methacrylate; and (c) a copolymer of a vinyl aromatic monomer and 30 to 70 percent by weight of a mixture of an ethylenically unsaturated nitrile and methyl methacrylate.
Claim 9
Dependent Claim
37 words
The thermoplastic blend as defined in claim 7 wherein said copolymer contains up to 60 percent by weight, based on the total weight of the copolymer, of a substrate rubber grafted with a portion of said copolymer.
Claim 10
Dependent Claim
46 words
The thermoplastic blend as defined in claim 1 wherein there is added up to 40 weight percent, based on the weight of the total blend, of a polymer of methyl methacrylate containing 0 to 20 percent by weight of an alkyl acrylate containing 1-8 carbon atoms.
Claim 11
Dependent Claim
37 words
The thermoplastic blend as defined in claim 9 wherein said polymer contains up to 60 percent by weight, based on the total weight of the polymer, of a substrate rubber grafted with a portion of said polymer.
Claim 12
Dependent Claim
46 words
The thermoplastic blend as defined in claim 1 wherein there is added up to 40 weight percent, based, on the weight of the total blend, of a copolymer of methyl methacrylate and up to 20 percent by weight, of the copolymer, of a vinyl aromatic monomer.
Claim 13
Dependent Claim
37 words
The thermoplastic blend as defined in claim 11 wherein said copolymer contains up to 60 percent by weight, based on the total weight of the copolymer, of a substrate rubber grafted with a portion of said copolymer.
Claim 14
Dependent Claim
30 words
The thermoplastic blend as defined in claim 1 wherein there is added up to 15 percent by weight, based on the weight of the total blend, of an ungrafted rubber.
Claim 15
Dependent Claim
66 words
The thermoplastic blend as defined in claim 1 wherein the rubber, in said rubber-modified vinyl chloride resin, is selected from the group consisting of a terpolymer of ethylene, propylene, and a diene termonomer; a copolymer of ethylene and vinyl acetate; a butyl acrylate-based rubber; and a copolymer of ethylene and an alkyl acrylate selected from the group consisting of methyl acrylate, ethyl acrylate and butyl acrylate.
Claim 16
Dependent Claim
44 words
The thermoplastic blend as defined in claim 1 wherein the rubber, in the rubber-modified vinyl chloride resin, is an EPDM rubber, in an amount of up to 20 weight percent, and all of the vinyl chloride is polymerized in the presence of said rubber.
References Cited (Backward Citations)
US3652726A
Cited
US3626033A
Cited
US3925510A
Cited
US4217424A
Cited
US4255322A
Cited
US4458046A
Cited
US4339554A
Cited
US4469845A
Cited
US4469844A
Cited
US4454300A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-06-16 | 1989-12-16 | 1990-06-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-06-16 | 1993-12-16 | 1994-06-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-06-16 | 1997-12-16 | 1998-06-17 | $7700.00 | Window Closed / Lapsed |