Abstract Improved encapsulating compositions for inductive devices are provided. The composition has a polybutadiene base and contains an initiator, an inhibitor and a co-agent for improving the curing of the composition under the influence of the initiator. Certain compositions are usable at higher temperatures than prior polybutadiene base encapsulating compounds based on a conditioning of the composition during cure at or near the projected use temperature. When combined with high temperature conductor insulation coatings, such as polyimides, a high temperature encapsulating system is achieved. Certain compositions are usable to provide a soft cure encapsulation from which an encapsulated inductive device may be liberated without damage to the device. For such compositions, soft curable polybutadienes are employed and particularly those having high trans and cis components.
As an article of manufacture, an inductive device, said device being encapsulated in a cured encapsulant composition, said encapsulant composition prior to its being cured comprising: (a) elastomeric polybutadiene of 100 parts consisting of about 54 to about 66 weight percent trans-1,4 polybutadiene, about 16 to about 24 weight percent cis-1,4 polybutadiene, and about 16 to about 24 weight percent vinyl-1,2-polybutadiene; (b) vinyl toluene of 0 to 40 parts; (c) trimethylol propane trimethacrylate of 0 to 10 parts; (d) peroxide crosslinking agent of 2.5 to 5 parts; (e) inhibitor of not substantially in excess of 0.9 parts.
Claim 2
Dependent Claim
97 words
As an article of manufacture, an inductive device, said device being encapsulated in a cured encapsulant composition, said encapsulant composition prior to its being cured comprising: (a) elastomeric polybutadiene of 100 parts consisting of about 54 to about 66 weight percent trans-1,4 polybutadiene, about 16 to about 24 weight percent cis-1,4 polybutadiene, and about 16 to about 24 weight percent vinyl-1,2-polybutadiene; (b) vinyl toluene of 0 to 40 parts; (c) trimethylol propane trimethacrylate of 0 to 10 parts; (d) peroxide crosslinking agent of 2.5 to 5 parts; (e) inhibitor of not substantially in excess of 0.9 parts.
Claim 3
Dependent Claim
25 words
The article of claim 1 in which the cured encapsulant is soft enough to permit the inductive device to be liberated without significant damage thereto.
Claim 4
Dependent Claim
20 words
The article of claim 1 in which the encapsulant has been cured at a temperature proximate the end use temperature.
Claim 5
Dependent Claim
22 words
The article of claim 1 or 3 in which the article is rated for a high temperature operating capability of 220° C.
Claim 6
Dependent Claim
38 words
The article of claims 1, 2 or 3 in which the range of vinyl toluene and trimethylol propane trimethacrylate is as follows: ______________________________________
INGREDIENT PARTS
______________________________________
vinyl toluene 17 to 25
trimethylol propane 4 to 8
trimethacrylate
______________________________________