Solderable conductive compositions having high adhesive strength
Assignee: National Starch and Chemical Investment Holding Corp
•
Filing: 1984-07-18
•
Granted: 1986-06-17
•
Expires: 2004-07-18
Abstract
Abstract This invention provides conductive compositions that are directly solderable and that can be bonded directly to substrates. The compositions are made of silver exclusively in the form of flake and a resin system, said resin system comprising phenolic resin, acrylic resin, polyurethane resin, vinyl chloride/vinyl acetate copolymer, epoxy resin and epoxy hardner. By making a mixture of such a complex vehicle system a composition is produced that displays outstanding solderability and adhesion. Also provided is a method of making these compositions.
Inventors
- 👤 Frank St. John
- 👤 Samson Shahbazi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 05:29
CPC Classifications
B; B23; B23K; B23K35/00; B23K35/22; B23K35/36; B23K35/362; C; C08; C08K; C08K3/00; C08K3/02; C08K3/08; H; H01; H01B; H01B1/00; H01B1/20; H01B1/22; H05; H05K; H05K1/00; H05K1/02; H05K1/09; H05K1/092; H05K1/095; Y; Y10; Y10S; Y10S428/00; Y10S428/901
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
134 words
A directly solderable conductive composition consisting essentially of, in combination, from about 80% to about 85% by weight silver and a resin system consisting essentially of from about 0.6% to about 1.6% by weight phenolic resin, from about 0.8% to about 1.6% by weight acrylic resin, from about 0.4% to about 0.8% by weight polyurethane resin, from about 1.2% to about 3.5% by weight vinyl chloride/vinyl acetate copolymer, from about 1.0% to about 3.0% by weight epoxy resin and from about 2.5% to about 4.0% by weight epoxy hardener; said silver being 100% in the form of flake having an average particle size from about 0.5 to about 50 microns, and said vinyl chloride/vinyl acetate copolymer having a number average molecular weight from about 14,000 to about 35,000 and containing no carboxylic acid groups.
Claim 2
Dependent Claim
134 words
A directly solderable conductive composition consisting essentially of, in combination, from about 80% to about 85% by weight silver and a resin system consisting essentially of from about 0.6% to about 1.6% by weight phenolic resin, from about 0.8% to about 1.6% by weight acrylic resin, from about 0.4% to about 0.8% by weight polyurethane resin, from about 1.2% to about 3.5% by weight vinyl chloride/vinyl acetate copolymer, from about 1.0% to about 3.0% by weight epoxy resin and from about 2.5% to about 4.0% by weight epoxy hardener; said silver being 100% in the form of flake having an average particle size from about 0.5 to about 50 microns, and said vinyl chloride/vinyl acetate copolymer having a number average molecular weight from about 14,000 to about 35,000 and containing no carboxylic acid groups.
Claim 3
Dependent Claim
21 words
The composition of claim 1 wherein the ratio of vinyl chloride to vinyl acetate is from about 80:20 to about 90:10.
Claim 4
Dependent Claim
26 words
The method of claim 1 wherein the ratio of silver flake to the first solution to the second solution is from about 65:20:15 to about 80:10:10.
Claim 5
Dependent Claim
43 words
The method of claim 1 wherein the ratio of total resin to solvent in the first solution is from about 1:1 to about 1:2 and the ratio of total resin to solvent in the second solution is from about 3:1 to about 9:1.
Claim 6
Dependent Claim
70 words
The method of claim 1 wherein the silver flake is present in an amount of from about 65% to about 80%, by weight, of the total composition, the first solution is present in an amount of from about 10% to about 20%, by weight, of the total composition and the second solution is present in an amount of from about 10% to about 15%, by weight, of the total composition.
Claim 7
Dependent Claim
19 words
The method of claim 1 additionally comprising applying the mixture to a substrate, then drying and curing the mixture.
Claim 8
Dependent Claim
13 words
The method of claim 6 wherein the substrate is a printed circuit board.
Claim 9
Dependent Claim
32 words
The method of claim 6 wherein the mixture is dried and cured at a temperature of from about 125° C. to about 180° C. for about 15 minutes to about 120 minutes.
Claim 10
Dependent Claim
22 words
A method of applying a conductive composition to a substrate comprising bonding the conductive composition of claim 1 directly to the substrate.
Claim 11
Dependent Claim
22 words
The method of claim 9 wherein the force required to remove the conductive composition from the substrate is greater than 1000 p.s.i.
Claim 12
Dependent Claim
13 words
The method of claim 9 wherein the substrate is a printed circuit board.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-06-16 | 1989-12-16 | 1990-06-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-06-16 | 1993-12-16 | 1994-06-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-06-16 | 1997-12-16 | 1998-06-17 | $7700.00 | Window Closed / Lapsed |