Refractory metal borides and composites containing them
Assignee: ELTECH SYSTEMS Ltd A CORP OF BERMUDA
•
Filing: 1982-12-30
•
Granted: 1986-06-17
•
Expires: 2002-12-30
Abstract
Abstract Refractory metal borides, carbides, nitrides and mixtures thereof of the Group IVb, Vb and VIb metals are produced from a glass or microcrystalline gel formed from organo-metallic precursors. Typically TiO 2 .B 2 O 3 glass is produced by hydrolysis of titanium butoxide and trimethyl borate, followed by gelling/drying. The glass may have carbon inclusions or may be mixed with carbon or aluminum powder or a mixture thereof, and reacted. In the case of aluminothermic and carboaluminothermic reduction, there is a residual aluminum-containing phase in the product. Composites can also be produced by including inert materials in the reaction mixture.
Inventors
- 👤 Ajit Y. Sane
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 03:11
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/56; C04B35/5607; C04B35/5611; C01; C01B; C01B21/00; C01B21/06; C01B32/00; C01B32/90; C01B35/00; C01B35/02; C01B35/04; C04B35/58; C04B35/58007; C04B35/58014; C04B35/5805; C04B35/58064; C04B35/58071; C04B35/622; C04B35/64; C04B35/65; C04B41/00; C04B41/009; C04B41/45; C04B41/50; C04B41/51; C04B41/80; C04B41/81; C04B41/85; C04B41/88; C25; C25C; C25C3/00; C25C3/06; C25C3/08; C01B21/0615; C01B21/0617; C01B21/062; C01B21/076; C01P; C01P2004/00; C01P2004/60; C01P2004/61; C01P2004/62
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
151 words
The method of producing titanium diboride or a mixture thereof with a carbide and/or a nitride of the Group IVb, Vb, or VIb metals, comprising: (a) preparing a solution of organic compounds comprising alkoxides of titanium and boron wherein the Ti:B molar ratio is at least about 1:2; (b) mixing particulate carbon or a carbon precursor in said solution in an amount to provide a Ti:B:C molar ratio or about 1:2:5; (c) hydrolyzing and gelling the solution to produce a glass or microcrystalline gell of an amorphous or microcrystalline oxide having a grain size up to 200 A and containing particulate carbon up to 500 A; (d) grinding said glass or microcrystalline gel to form a resulting material, optionally adjusting the Ti:B:C molar ratio of the resulting material, and pressing the resulting material into a body; and (e) heating the body to reaction temperature under vacuum, an inert atmosphere or nitrogen.
Claim 2
Independent Claim
151 words
The method of producing titanium diboride or a mixture thereof with a carbide and/or a nitride of the Group IVb, Vb, or VIb metals, comprising: (a) preparing a solution of organic compounds comprising alkoxides of titanium and boron wherein the Ti:B molar ratio is at least about 1:2; (b) mixing particulate carbon or a carbon precursor in said solution in an amount to provide a Ti:B:C molar ratio or about 1:2:5; (c) hydrolyzing and gelling the solution to produce a glass or microcrystalline gell of an amorphous or microcrystalline oxide having a grain size up to 200 A and containing particulate carbon up to 500 A; (d) grinding said glass or microcrystalline gel to form a resulting material, optionally adjusting the Ti:B:C molar ratio of the resulting material, and pressing the resulting material into a body; and (e) heating the body to reaction temperature under vacuum, an inert atmosphere or nitrogen.
Claim 3
Dependent Claim
11 words
The method of claim 1 wherein the heating sinters said body.
Claim 4
Dependent Claim
17 words
The method of claim 2 wherein the heating is a controlled heating providing a self-sustaining porous body.
Claim 5
Dependent Claim
27 words
The method of claim 1 wherein a composite is formed between the titanium diboride and an added inert material which is in mixture therewith before the heating.
Claim 6
Dependent Claim
30 words
The method of claim 1 wherein said solution of organic compounds comprises alkoxides of titanium and boron selected from the group consisting of methoxides, isopropoxides, butoxides, amyloxides and their mixtures.
Claim 7
Dependent Claim
23 words
The method of claim 1 wherein said organic compounds are soluble one with the othwer and said solution is prepared without additional solvent.
Claim 8
Dependent Claim
46 words
A method of producing a body of a composite material of titanium diboride, an aluminum compound and aluminum, characterized by producing a porous composite body of titanium diboride and the aluminum compound by the method of claim 6 and infiltrating the porous body with molten aluminum.
Claim 9
Independent Claim
150 words
A method of producing a composite material of titanium diboride and an aluminum-containing phase or a mixture of titanium diboride with a carbide and/or a nitride of a Group IVb, Vb, or VIb metal and an aluminum-containing phase, comprising: (a) preparing a solution of organic compounds comprising alkoxides of titanium and boron wherein the Ti:B molar ratio is at least about 1:2; (b) hydrolyzing and gelling the solution to produce a glass or microcrystalline gel of amorphous or microcrystalline oxide having a grain size up to 200 A; (c) grinding said glass or microcrystalline gel into a ground material; (d) adding particulate aluminum or an aluminum compound to the ground material of step (c) to form a resulting mixture, (e) forming the resulting mixture of step (d) into a body; and (f) heating the body at elevated temperature under vacuum, an inert atmosphere or nitrogen to react the ground material.
Claim 10
Independent Claim
150 words
A method of producing a composite material of titanium diboride and an aluminum-containing phase or a mixture of titanium diboride with a carbide and/or a nitride of a Group IVb, Vb, or VIb metal and an aluminum-containing phase, comprising: (a) preparing a solution of organic compounds comprising alkoxides of titanium and boron wherein the Ti:B molar ratio is at least about 1:2; (b) hydrolyzing and gelling the solution to produce a glass or microcrystalline gel of amorphous or microcrystalline oxide having a grain size up to 200 A; (c) grinding said glass or microcrystalline gel into a ground material; (d) adding particulate aluminum or an aluminum compound to the ground material of step (c) to form a resulting mixture, (e) forming the resulting mixture of step (d) into a body; and (f) heating the body at elevated temperature under vacuum, an inert atmosphere or nitrogen to react the ground material.
Claim 11
Dependent Claim
24 words
The method of claim 8 wherein finely divided powder of aluminum or aluminum mixed with aluminum nitride is mixed with said glass or gel.
Claim 12
Dependent Claim
16 words
The method of claim 9 wherein during heating the aluminum provides aluminum oxide, nitride and/or oxynitride.
Claim 13
Dependent Claim
16 words
The method of claim 9 wherein excess unreacted aluminum remains at the end of the heating.
Claim 14
Dependent Claim
18 words
The method of claim 11 wherein the excess aluminum is subusequently reacted with nitrogen to form aluminum nitrides.
Claim 15
Dependent Claim
30 words
The method of claim 8 wherein said solution of organic compounds comprise alkoxides of titanium and boron selected from the group consisting of methoxides, isopropoxides, butoxides, amyloxides and their mixture.
References Cited (Backward Citations)
US3106456A
Cited
GB1004585A
Cited
US3379647A
Cited
US3471380A
Cited
US3649314A
Cited
US3692474A
Cited
US3749571A
Cited
US3791808A
Cited
US4282195A
Cited
US4376029A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-06-16 | 1989-12-16 | 1990-06-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-06-16 | 1993-12-16 | 1994-06-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-06-16 | 1997-12-16 | 1998-06-17 | $7700.00 | Window Closed / Lapsed |