Method for producing a thermoplastic polymeric sheet
Assignee: Toray Industries Inc
•
Filing: 1984-03-13
•
Granted: 1986-06-10
•
Expires: 2004-03-13
Abstract
Abstract The present invention relates to a method for producing a thermoplastic polymeric sheet, wherein a molten thermoplastic polymer is extruded from an extrusion die in the form of a sheet onto a moving quenching member, with an electric potential difference being established between the surface of the moving quenching member and the extrusion die, whereby the polymer is caused to electrostatically solidify and adhered to the surface of the quenching member. The contact area of the polymeric sheet with the moving quenching member is held in an atmosphere of a gas which posesses better insulating properties than standard air. Thus the present invention provides a useful method that can produce, at higher speeds than conventional method, polymer sheets of high surface quality which avoid the operational problems encountered in the conventional methods.
Inventors
- 👤 Satoru Hagiwara
- 👤 Ichiro Ishizuka
- 👤 Kazuo Okabe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 15:53
CPC Classifications
B; B29; B29C; B29C48/00; B29C48/25; B29C48/88; B29C48/911; B29C48/9135; B29C48/9175; B29C48/914; B29C48/915; B29C48/9165; B29C48/917; B29C48/03; B29C48/07; B29C48/08
Claims Analysis
Total Claims: 35
Claim 1
Independent Claim
95 words
A method for producing a thermoplastic polymeric sheet comprising: extruding a molten thermoplastic polymer in the form of a sheet from an extrusion die onto a moving quenching member; maintaining the contact area of the molten thermoplastic polymer in the form of a sheet with the moving quenching member in a gaseous atmosphere more insulating than that of air; and electrically adhering the molten thermoplastic polymer in the form of a sheet to the quenching member and solidifying the sheet with an electric potential difference applied between the extrusion die and the moving quenching member.
Claim 2
Independent Claim
95 words
A method for producing a thermoplastic polymeric sheet comprising: extruding a molten thermoplastic polymer in the form of a sheet from an extrusion die onto a moving quenching member; maintaining the contact area of the molten thermoplastic polymer in the form of a sheet with the moving quenching member in a gaseous atmosphere more insulating than that of air; and electrically adhering the molten thermoplastic polymer in the form of a sheet to the quenching member and solidifying the sheet with an electric potential difference applied between the extrusion die and the moving quenching member.
Claim 3
Dependent Claim
40 words
The method of claim 1 wherein an auxiliary electrode is disposed on the non-contact side of the polymeric sheet with the moving quenching member and an electric potential difference is established between said auxiliary electrode and the moving quenching member.
Claim 4
Dependent Claim
39 words
The method of claim 1 wherein the electric potential difference established between the extrusion die and the surface of the moving quenching member is a potential difference generated by D.C. with less than 1% variation in the voltage rate.
Claim 5
Dependent Claim
43 words
The method of claim 2 wherein the electric potential difference established between the extrusion die and the auxiliary electrode, and the surface of the moving quenching member is a potential difference generated by D.C. with less than 1% variation in the voltage rate.
Claim 6
Dependent Claim
46 words
The method of claim 1 wherein the gas which is more insulating than air is a gas with more than 1.3 times the insulating quality of the air in terms of the dielectric break down voltage as measured by the method specified in ASTM D 2477.
Claim 7
Dependent Claim
72 words
The method of claim 1 wherein the gas which is more insulating than air is a gas selected from the group consisting of halogenated hydrocarbons having a molecular weight larger than 100 and having a gaseous state at a room temperature, sulfur fluoride having a molecular weight larger than 100 and having a gaseous state at a room temperature, a mixture of these materials and a mixture of these materials and air.
Claim 8
Dependent Claim
19 words
The method of claim 2 wherein said auxiliary electrode is a wire, a needle, a knife or a band.
Claim 9
Dependent Claim
30 words
The method of claim 1 wherein the electric potential difference (E 1 ) established between the extrusion die and the moving quenching member is from 8 KV to 60 KV.
Claim 10
Dependent Claim
61 words
The method of claim 2 wherein the electric potential difference (E 1 ) established between the extrusion die and the moving quenching member is from 8 KV to 60 KV, while the electric potential difference (E 2 ) established between the auxiliary electrode and the moving quenching member is less than E 1 and ranges from 5 KV to 15 KV.
Claim 11
Dependent Claim
18 words
The method of claim 1 wherein the moving quenching member is a cooling roller or a cooling belt.
Claim 12
Dependent Claim
29 words
The method of claim 1 wherein the moving quenching member, on at least its surface, comprises an electrically conductive material of less than 10 8 Ω.cm in volume resistivity.
Claim 13
Dependent Claim
29 words
The method of claim 1 wherein the moving quenching member, on at least its surface, comprises an electrically conductive material of less than 10 -3 Ω.cm in volume resistivity.
Claim 14
Dependent Claim
24 words
The method of claim 1 wherein at least the extrusion die or the moving quenching member is electrically insulated in relation to the ground.
Claim 15
Dependent Claim
13 words
The method of claim 1 wherein the gas is supplied through a nozzle.
Claim 16
Dependent Claim
37 words
The method of claim 1 wherein said polymeric sheet is a single sheet or a laminated sheet of a material selected from the group consisting of polyolefines, polyesters, polyamides, polymides, vinyl polymers, copolymers thereof and mixtures thereof.
Claim 17
Dependent Claim
25 words
The method of claim 1 wherein said polymeric sheet is either a polyester sheet or a laminated sheet of a polyester and another thermoplastic polymer.
Claim 18
Dependent Claim
46 words
The method of claim 2 wherein the gas which is more insulating than air is a gas with more than 1.3 times the insulating quality of the air in terms of the dielectric break down voltage as measured by the method specified in ASTM D 2477.
Claim 19
Dependent Claim
72 words
The method of claim 2 wherein the gas which is more insulating than air is a gas selected from the group consisting of halogenated hydrocarbons having a molecular weight larger than 100 and having a gaseous state at a room temperature, sulfur fluoride having a molecular weight larger than 100 and having a gaseous state at a room temperature, a mixture of these materials and a mixture of these materials and air.
Claim 20
Dependent Claim
18 words
The method of claim 2 wherein the moving quenching member is a cooling roller or a cooling belt.
Claim 21
Dependent Claim
28 words
The method of claim 2 wherein the moving quenching member, on at least its surface, comprises an electrically conductive material of less 10 8 Ω.cm in volume resistivity.
Claim 22
Dependent Claim
31 words
The method of claim 2 wherein the moving quenching member, on at least its surface, is constituted of an electrically conductive material of less than 10 -3 Ω.cm in volume resistivity.
Claim 23
Dependent Claim
24 words
The method of claim 2 wherein at least the extrusion die or the moving quenching member is electrically insulated in relation to the ground.
Claim 24
Dependent Claim
13 words
The method of claim 2 wherein the gas is supplied through a nozzle.
Claim 25
Dependent Claim
37 words
The method of claim 2 wherein said polymeric sheet is a single sheet or a laminated sheet of a material selected from the group consisting of polyolefines, polyesters, polyamides, polyamides, vinyl polymers, copolymers thereof and mixtures thereof.
Claim 26
Dependent Claim
25 words
The method of claim 2 wherein said polymeric sheet is either a polyester sheet or a laminated sheet of a polyester and another thermoplastic polymer.
Claim 27
Dependent Claim
37 words
The method of claim 1 wherein the contact area between the polymeric sheet and the moving quenching member is in the vicinity of the point where the polymeric sheet comes into contact with the moving quenching member.
Claim 28
Dependent Claim
29 words
The method of claim 26 wherein the contact area is completely covered to exclude external air said contact area being supplied with said gaseous atmosphere more insulative than air.
Claim 29
Dependent Claim
18 words
The method of claim 26 wherein the insulating gas is applied to the contact area from a nozzle.
Claim 30
Dependent Claim
23 words
The method of claim 1 wherein the surface of the moving quenching member is below the glass-transition point of the polymer being quenched.
Claim 31
Dependent Claim
12 words
The method of claim 1 wherein the thermoplastic polymer is polyethylene terephthalate.
Claim 32
Dependent Claim
47 words
The metod of claim 1 wherein the surface of the quenching member is provided with an insulating layer which in turn is provided with an electrically conductive layer and an electrical potential difference established between the electrically conductive layer of the quenching member and the extrusion die.
Claim 33
Dependent Claim
36 words
The method of claim 1 wherein the surface of the moving quenching member is electrostatically charged with a potential by a charging electrode disposed on the contact side of the thermoplastic polymer with the quenching member.
Claim 34
Dependent Claim
40 words
The method of claim 31 wherein an auxiliary electrode is disposed on the non-contact side of the polymeric sheet with the moving quenching member and an electric potential difference is established between said auxiliary electrode and the moving quenching member.
Claim 35
Dependent Claim
26 words
The method of claim 33 wherein the auxiliary electrode is grounded via a resister and an auxiliary power supply is connected in parallel to the resister.
References Cited (Backward Citations)
US3223757A
Cited
US3490115A
Cited
US3427686A
Cited
US4310294A
Cited
US3593074A
Cited
US3655307A
Cited
US3660549A
Cited
US3686374A
Cited
US4111625A
Cited
JPS5517559A
Cited
JPS562126A
Cited
US4268464A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-06-09 | 1989-12-09 | 1990-06-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-06-09 | 1993-12-09 | 1994-06-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-06-09 | 1997-12-09 | 1998-06-10 | $7700.00 | Window Closed / Lapsed |