Polyester film primed with crosslinked vinyl acetate polymers
Assignee: CNA Holdings LLC
•
Filing: 1983-12-12
•
Granted: 1986-06-03
•
Expires: 2003-12-12
Abstract
Abstract An oriented polyester film coated on one or both sides with a crosslinked vinyl acetate polymer composition which renders the polyester film surface receptive to additional reprographic or matte coatings applied thereto, and to film containing the reclamation product of such coated film.
Inventors
- 👤 Grover L. Farrar
- 👤 E. C. Culbertson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 20:48
CPC Classifications
B; B44; B44D; B44D3/00; B44D3/18; C; C08; C08J; C08J7/00; C08J7/12; C08J7/16; C08J7/18; C08J7/04; C08J7/042; C08J7/043; G; G03; G03C; G03C1/00; G03C1/76; G03C1/91; G03C1/93; C08J2367/00; C08J2423/00; C08J2423/02; C08J2431/00; C08J2431/02; C08J2431/04; Y; Y10; Y10T; Y10T428/00; Y10T428/26; Y10T428/31504; Y10T428/31786; Y10T428/31797
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
149 words
An oriented self-supporting polyester film having a continuous cross-linked primer coating on one or both sides thereof, said polyester film prepared by melt extruding a substantially amorphous polyester film and thereafter orienting the film by stretching in one or two directions and heat setting the film, said primer coating being applied to said film from an aqueous medium prior to stretching in one direction or subsequent to stretching in one direction but prior to stretching in a mutually perpendicular direction, said primer coating consisting essentially of a substantially halogen-free copolymer of at least about 50 percent by weight of polymerized vinyl acetate, from about 1 to about 15% by weight of a copolymerized N-methylol functional group-containing comonomer which in the copolymerized state is capable of inter-molecular crosslinking by the application of heat, and from about 0 to 49% by weight of one or more halogen-free monoethylenically unsaturate copolymerized monomers.
Claim 2
Dependent Claim
149 words
An oriented self-supporting polyester film having a continuous cross-linked primer coating on one or both sides thereof, said polyester film prepared by melt extruding a substantially amorphous polyester film and thereafter orienting the film by stretching in one or two directions and heat setting the film, said primer coating being applied to said film from an aqueous medium prior to stretching in one direction or subsequent to stretching in one direction but prior to stretching in a mutually perpendicular direction, said primer coating consisting essentially of a substantially halogen-free copolymer of at least about 50 percent by weight of polymerized vinyl acetate, from about 1 to about 15% by weight of a copolymerized N-methylol functional group-containing comonomer which in the copolymerized state is capable of inter-molecular crosslinking by the application of heat, and from about 0 to 49% by weight of one or more halogen-free monoethylenically unsaturate copolymerized monomers.
Claim 3
Dependent Claim
21 words
The film of claim 1 wherein said functional group-containing comonomer is selected from the group consisting of N-methylol acrylamide and N-methylolmethacrylamide.
Claim 4
Dependent Claim
23 words
The film is claim 2 wherein said monoethylenically unsaturated monomer is present at a level of from about 5 to 45% by weight.
Claim 5
Dependent Claim
13 words
The film of claim 3 wherein said monoethylenically unsaturated monomer is methyl methacrylate.
Claim 6
Dependent Claim
21 words
The film of claim 2 said functional group-containing comonomer is present at a level of about 5 to 10% by weight.
Claim 7
Dependent Claim
38 words
The film of claim 5 wherein said primer coating comprises a copolymer of about 50 to 90% by weight vinyl acetate, about 5 to 45% by weight methylmethacrylate, and from about 5 to 10% by weight N-methylol acrylamide.
Claim 8
Dependent Claim
24 words
The film of claim 1 wherein said primer coating has a dry thickness within the range of about 10 -7 to 10 -5 inch.
Claim 9
Dependent Claim
17 words
The film of claim 7 wherein said self supporting polyester film is biaxially oriented polyethylene terephthalate film.
Claim 10
Dependent Claim
74 words
A biaxially oriented polyester film comprising an intimate mixture of from about 30 to 95% by weight of fresh polyester and corresponding about 70 to 5% by weight of the coated film of claim 8, said coated film characterized in that said coated film is comminuted, melted at a temperature within the range of about 270° C. to about 310° C., and mixed with fresh polyester prior to extruding and biaxially orienting said film.
Claim 11
Dependent Claim
17 words
The film of claim 9 containing from about 0.01 to about 1.0% by weight of said coating.
Claim 12
Dependent Claim
126 words
The oriented self supporting polyester film of claim 10 which is itself primer coated with a continuous cross-linked coating on one or both sides thereof, said coating being applied to said film from an aqueous medium prior to stretching in one direction or subsequent to stretching in one direction but prior to stretching in a mutually perpendicular direction, said coating consisting essentially of a substantially halogen-free copolymer of at least about 50 percent by weight of polymerized vinyl acetate, from about 1 to about 15% by weight of a copolymerized N-methylol functional group-containing comonomer which in the copolymerized state is capable of inter-molecular crosslinking by the application of heat, and from about 0 to 49% by weight of one or more halogen-free monoethylenically unsaturated copolymerized monomers.
Claim 13
Dependent Claim
24 words
The film of claim 11 wherein said primer coating has a dry thickness within the range of about 10 -7 to 10 -5 inch.
Claim 14
Dependent Claim
17 words
The film of claim 12 wherein said self supporting polyester film is biaxially oriented polyethylene terephthalate film.
Claim 15
Dependent Claim
31 words
A light-sensitive film comprising the film of claim 13 having a light-sensitive layer comprising a resinous binder containing or impregnated with a light-sensitive diazonium salt applied directly to said primer coating.
Claim 16
Dependent Claim
29 words
A graphic film comprising the film of claim 13 having a matte layer comprising a resinous binder containing a finely divided particulate material applied directly to said primer coating.
Claim 17
Dependent Claim
21 words
The film of claim 13 having a printing ink composition applied directly to at least a portion of said primer coating.
Claim 18
Dependent Claim
21 words
The film of claim 11 wherein said functional group-containing comonomer is selected from the group consisting of N-methylol acrylamide and N-methylol-methacrylamide.
Claim 19
Dependent Claim
22 words
The film of claim 17 wherein said functional group-containing comonomer is present at a level of about 5 to 10% by weight.
Claim 20
Dependent Claim
23 words
The film of claim 17 wherein said monoethylenically unsaturated monomer is present at a level of from about 5 to 45% by weight.
Claim 21
Dependent Claim
19 words
The film of claim 19 wherein said primer coating contains about 5 to 10% by weight of N-methylol acrylamide.
Claim 22
Dependent Claim
13 words
The film of claim 19 wherein said monoethylenically unsaturated monomer is methyl methacrylate.
References Cited (Backward Citations)
US3624021A
Cited
US3506445A
Cited
US3720539A
Cited
US3674531A
Cited
US3819773A
Cited
US4066820A
Cited
GB1497656A
Cited
GB1497658A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-06-02 | 1989-12-02 | 1990-06-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-06-02 | 1993-12-02 | 1994-06-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-06-02 | 1997-12-02 | 1998-06-03 | $7700.00 | Window Closed / Lapsed |