Annealed polydioxanone surgical device and method for producing the same
Assignee: Ethicon Inc
•
Filing: 1985-06-10
•
Granted: 1986-05-27
•
Expires: 2005-06-10
Abstract
Abstract Thermally formed annealed surgical devices made from unoriented polymers of p-dioxanone and methods for manufacturing the same. The preferred device is a ligating clip having good in vivo performance characteristics. The method includes initially drying the thermally formed device followed by heating the device without restraint at specific temperatures for specific time periods.
Inventors
- 👤 Arthur Gertzman
- 👤 Darrell R. Thompson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 15:57
CPC Classifications
A; A61; A61L; A61L17/00; A61L17/14; A61L17/06; A61L17/10; A61L17/105; C; C08; C08G; C08G63/00; C08G63/66; C08G63/664
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
85 words
A method of treating a thermally formed, substantially unoriented surgical device made of a polymer prepared from a monomer having the formula ##STR3## comprising: (a) drying the thermally formed device at a temperature of less than 30° C. to remove substantially all moisture from the device; and (b) heating the dried device without any restraint in a dry, inert atmosphere at a temperature of 50° C. to 90° C. for at least 7 hours whereby the strength and functional integrity of the device are improved.
Claim 2
Independent Claim
85 words
A method of treating a thermally formed, substantially unoriented surgical device made of a polymer prepared from a monomer having the formula ##STR3## comprising: (a) drying the thermally formed device at a temperature of less than 30° C. to remove substantially all moisture from the device; and (b) heating the dried device without any restraint in a dry, inert atmosphere at a temperature of 50° C. to 90° C. for at least 7 hours whereby the strength and functional integrity of the device are improved.
Claim 3
Independent Claim
106 words
A method for treating thermally formed, substantially unoriented surgical devices made from polymers having units of the formula ##STR4## wherein x is the degree of polymerization resulting in a thermally formable polymer comprising; (a) drying the thermally formed device at a temperature of less than 30° C. to remove substantially all the moisture from the device; (b) heating the dried device without any restraint in an inert atmosphere at a temperature of from 50° C. to 90° C. for a sufficient period of time to increase the crystallinity of the device to at least 43% whereby the strength and functional integrity of the device are improved.
Claim 4
Independent Claim
106 words
A method for treating thermally formed, substantially unoriented surgical devices made from polymers having units of the formula ##STR4## wherein x is the degree of polymerization resulting in a thermally formable polymer comprising; (a) drying the thermally formed device at a temperature of less than 30° C. to remove substantially all the moisture from the device; (b) heating the dried device without any restraint in an inert atmosphere at a temperature of from 50° C. to 90° C. for a sufficient period of time to increase the crystallinity of the device to at least 43% whereby the strength and functional integrity of the device are improved.
Claim 5
Dependent Claim
17 words
A method according to claim 2 wherein the dried device is heated for at least 7 hours.
Claim 6
Dependent Claim
15 words
A method according to claim 1 or 2 wherein the device is a ligating clip.
Claim 7
Dependent Claim
24 words
A method according to claim 1 or 2 wherein the dried device is heated to a temperature of from 80° C. to 85° C.
Claim 8
Dependent Claim
20 words
A method according to claim 1 or 2 wherein the inert atmosphere is a nitrogen atmosphere substantially free of moisture.
Claim 9
Dependent Claim
14 words
A method according to claim 6 wherein the device is an injection molded device.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-05-26 | 1989-11-25 | 1990-05-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-05-26 | 1993-11-25 | 1994-05-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-05-26 | 1997-11-25 | 1998-05-27 | $7700.00 | Window Closed / Lapsed |