Aqueous emulsion laminating adhesive
Assignee: DeSoto Inc
•
Filing: 1985-02-11
•
Granted: 1986-05-13
•
Expires: 2005-02-11
Abstract
Abstract A method of forming an aqueous emulsion laminating adhesive having an extended pot life is disclosed in which monoethylenically unsaturated monomers are polymerized to form a copolymer having a glass transition temperature in the range of about -10° C. to about -50° C. The polymerization is carried out in aqueous emulsion in the presence of emulsified epoxy resin in an amount of from about 2% to about 60%, based on the weight of the monomers which are copolymerized. An aqueous emulsion of amine-functional resin is then mixed into aqueous emulsion containing copolymer and epoxy resin formed by the aqueous emulsion copolymerization to provide a weight ratio of amino hydrogen atoms to oxirane groups of from about 0.1 to about 1.0.
Inventors
- 👤 Ralph L. Minnis
- 👤 Elias P. Moschovis
- 👤 James J. Killeen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 23:17
CPC Classifications
C; C08; C08J; C08J5/00; C08J5/12; C08J5/124; C08J5/127; C08G; C08G59/00; C08G59/18; C08G59/40; C08G59/50; C08J2323/00; C08J2323/02; C08J2323/10; C08J2323/12; Y; Y10; Y10S; Y10S524/00; Y10S524/906
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
123 words
A method of forming an aqueous emulsion adhesive comprising polymerizing monoethylenically unsaturated monomers in aqueous emulsion in the presence of an emulsified epoxy resin to form an aqueous emulsion copolymer, the copolymer of said monoethylenically unsaturated monomers having a glass transition temperature in the range of about -10° C. to about -50° C. and said epoxy resin being present in an amount of from about 2% to about 60%, based on the weight of the monomers which are copolymerized, and then mixing the aqueous emulsion of copolymer and epoxy resin formed by said copolymerization with an aqueous emulsion of amine-functional resin in an amount to supply a weight ratio of amino hydrogen atoms to oxirane groups of from about 0.1 to about 1.0.
Claim 2
Independent Claim
123 words
A method of forming an aqueous emulsion adhesive comprising polymerizing monoethylenically unsaturated monomers in aqueous emulsion in the presence of an emulsified epoxy resin to form an aqueous emulsion copolymer, the copolymer of said monoethylenically unsaturated monomers having a glass transition temperature in the range of about -10° C. to about -50° C. and said epoxy resin being present in an amount of from about 2% to about 60%, based on the weight of the monomers which are copolymerized, and then mixing the aqueous emulsion of copolymer and epoxy resin formed by said copolymerization with an aqueous emulsion of amine-functional resin in an amount to supply a weight ratio of amino hydrogen atoms to oxirane groups of from about 0.1 to about 1.0.
Claim 3
Dependent Claim
44 words
A method as recited in claim 1 in which said epoxy resin is a diglycidyl ether of a bisphenol having a molecular weight in the range of about 350 to about 3,000, and is emulsified in water with the aid of a nonionic surfactant.
Claim 4
Dependent Claim
47 words
A method as recited in claim 2 in which said epoxy resin is a diglycidyl ether of bisphenol A which is liquid at room temperature and which is present in an amount of from 3% to 40% based on the weight of the monomers which are copolymerized.
Claim 5
Dependent Claim
30 words
A method as recited in claim 2 in which said mixture of monoethylenically unsaturated monomers provides a copolymer having a glass transition temperature of from -15° C. to -30° C.
Claim 6
Dependent Claim
23 words
A method as recited in claim 4 in which said mixture of monomers includes from 1% to 5% of acrylic or methacrylic acid.
Claim 7
Dependent Claim
32 words
A method as recited in claim 5 in which said mixture of monomers includes from 1% to 5% of an hydroxyalkyl monomer in which the alkyl group contains from 2-4 carbon atoms.
Claim 8
Dependent Claim
15 words
A method as recited in claim 6 in which said hydroxyalkyl monomer is 2-hydroxyethyl acrylate.
Claim 9
Dependent Claim
50 words
A method as recited in claim 1 in which said monomers are emulsified in the aqueous polymerization medium in a proportion of from 25% to 55% using a nonionic surfactant together with an anionic surfactant, and the polymerization is carried out below the boiling point of water using a persulfate.
Claim 10
Dependent Claim
29 words
A method as recited in claim 8 in which the catalyst is ammonium persulfate, no reducing agent is present, and the polymerization is carried out at about 80° C.
Claim 11
Dependent Claim
32 words
A method as recited in claim 1 in which said amine-functional resin is emulsified in water with a nonionic surfactant to provide an emulsion containing from 8% to 20% of amine-functional resin.
Claim 12
Dependent Claim
18 words
A method as recited in claim 10 in which said amine-functional resin is a dimer fatty acid diamine.
Claim 13
Dependent Claim
30 words
A method as recited in claim 10 in which said amine-functional resin is present in a weight ratio of amino hydrogen atoms to oxirane groups of from 0.25 to 0.6.
Claim 14
Independent Claim
169 words
A method of forming an aqueous emulsion adhesive comprising polymerizing monoethylenically unsaturated monomers including from 1% to 5% of acrylic or methacrylic acid and from 1% to 5% of an hydroxyalkyl monomer in which the alkyl group contains from 2-4 carbon atoms in aqueous emulsion in the presence of an emulsified epoxy resin which is a diglydicyl ether of a bisphenol having a molecular weight in the range of about 350 to about 3,000 to form an aqueous emulsion copolymer, the copolymer of said monoethylenically unsaturated monomers having a glass transition temperature in the range of -15° C. to -30° C. and said epoxy resin being present in an amount of from 3% to 40%, based on the weight of the monomers which are copolymerized, and then mixing the aqueous emulsion of copolymer and epoxy resin formed by said copolymerization with an aqueous emulsion of dimer fatty acid diamine in an amount to supply a weight ratio of amino hydrogen atoms to oxirane groups of from 0.25 to 0.6.
Claim 15
Independent Claim
169 words
A method of forming an aqueous emulsion adhesive comprising polymerizing monoethylenically unsaturated monomers including from 1% to 5% of acrylic or methacrylic acid and from 1% to 5% of an hydroxyalkyl monomer in which the alkyl group contains from 2-4 carbon atoms in aqueous emulsion in the presence of an emulsified epoxy resin which is a diglydicyl ether of a bisphenol having a molecular weight in the range of about 350 to about 3,000 to form an aqueous emulsion copolymer, the copolymer of said monoethylenically unsaturated monomers having a glass transition temperature in the range of -15° C. to -30° C. and said epoxy resin being present in an amount of from 3% to 40%, based on the weight of the monomers which are copolymerized, and then mixing the aqueous emulsion of copolymer and epoxy resin formed by said copolymerization with an aqueous emulsion of dimer fatty acid diamine in an amount to supply a weight ratio of amino hydrogen atoms to oxirane groups of from 0.25 to 0.6.
Claim 16
Dependent Claim
51 words
A method as recited in claim 13 in which said monomers are emulsified in the aqueous polymerization medium in a proportion of from 25% to 55% using a nonionic surfactant together with an anionic surfactant, and the polymerization is carried out at about 80° C. in the presence of ammonium persulfate.
Claim 17
Dependent Claim
8 words
The product of the method of claim 1.
Claim 18
Dependent Claim
8 words
The product of the method of claim 13.
References Cited (Backward Citations)
JPS5323399A
Cited
US4308183A
Cited
US4418166A
Cited
GB2108976A
Cited
US4444923A
Cited
JPS59145211A
Cited
US4503173A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-05-12 | 1989-11-11 | 1990-05-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-05-12 | 1993-11-11 | 1994-05-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-05-12 | 1997-11-11 | 1998-05-13 | $7700.00 | Window Closed / Lapsed |