Clear silicone coated fabric
Assignee: Dow Silicones Corp
•
Filing: 1985-09-20
•
Granted: 1986-05-06
•
Expires: 2005-09-20
Abstract
Abstract The method of this invention produces a silicone coated glass fabric which is translucent or transparent as desired and which has a smooth dry surface. The coated glass fabric is useful in producing air-supported and tension-supported roofs for structures such as greenhouses. A glass fabric is first coated with a polydiorganosiloxane, in which the organo radicals are methyl and phenyl radicals in a ratio of from 0.25 to 3.7, in an amount sufficient to impregnate the fibers in the yarns of the fabric, but leaving the interstices of the fabric open. This first layer is then followed by coating with a polydimethylsiloxane elastomer to give a continuous layer, then coating with an elastoplastic organopolysiloxane resin to give a smooth, dry surface on the glass fabric reinforced sheet.
Inventors
- 👤 Beth I. Gutek
- 👤 Bernard Van Wert
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:59
CPC Classifications
D; D06; D06M; D06M15/00; D06M15/19; D06M15/37; D06M15/39; D06M15/423; D06M15/43; A; A01; A01G; A01G9/00; A01G9/14; A01G9/1438; B; B29; B29B; B29B15/00; B29B15/08; B29B15/10; B29B15/12; B29B15/122; B32; B32B; B32B7/00; B32B7/04; B32B7/08; D06M15/643; D06N; D06N3/00; D06N3/0002; D06N3/0015; D06N3/0022; D06N3/12; D06N3/128; E; E04; E04H; E04H15/00; E04H15/32; E04H15/54; A01G2009/1453; A01G2009/1461; Y; Y02; Y02A; Y02A40/00; Y02A40/10; Y02A40/25; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31551; Y10T428/31609; Y10T428/31612; Y10T428/31652; Y10T428/31663; Y10T442/00; Y10T442/20; Y10T442/2041; Y10T442/2098; Y10T442/2926; Y10T442/2992
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
84 words
A transparent or translucent silicone coated glass fabric comprising a first layer of polydiorganosiloxane, in which the organo radicals are methyl and phenyl radicals in a ratio of from 0.25 to 3.7, impregnating and coating the yarns of the glass fabric but not filling in the interstices of the glass fabric; a second layer of silicone elastomer covering the first layer and filling in the interstices of the glass fabric; and a third layer of elastoplastic organopolysiloxane resin to give a smooth, dry surface.
Claim 2
Dependent Claim
84 words
A transparent or translucent silicone coated glass fabric comprising a first layer of polydiorganosiloxane, in which the organo radicals are methyl and phenyl radicals in a ratio of from 0.25 to 3.7, impregnating and coating the yarns of the glass fabric but not filling in the interstices of the glass fabric; a second layer of silicone elastomer covering the first layer and filling in the interstices of the glass fabric; and a third layer of elastoplastic organopolysiloxane resin to give a smooth, dry surface.
Claim 3
Dependent Claim
19 words
The silicone coated glass fabric of claim 1 in which the polydiorganosiloxane forming the first layer is an elastomer.
Claim 4
Dependent Claim
27 words
The silicone coated glass fabric of claim 1 in which the polydiorganosiloxane forming the first layer has a methyl to phenyl ratio of from 0.6 to 1.5.
Claim 5
Dependent Claim
19 words
The silicone coated glass fabric of claim 3 in which the polydiorganosiloxane forming the first layer is an elastomer.
Claim 6
Dependent Claim
155 words
The silicone coated glass fabric of claim 4 in which the second layer of silicone elastomer and the third layer of elastoplastic organopolysiloxane resin form an interface which is an adhesive bond derived from a combination comprising (i) polydiorganosiloxane of the formula X(R 2 SiO) a SiR 2 Y where R is a monovalent hydrocarbon radical containing no more than 6 carbon atoms, X is a condensable endblocking group and a has a value such that the polydiorganosiloxane has a viscosity of greater than 1 Pa·s at 25° C., (ii) a hydroxyl radical containing, solid, benzene soluble resin copolymer consisting essentially of R 3 SiO 1/2 units and SiO 4/2 units where R is as defined above, there being from 0.6 to 0.9 inclusive R 3 SiO 1/2 units for every SiO 4/2 unit, at least 95 percent of all R radicals in (ii) being methyl, and (iii) a condensation catalyst for (i) and (ii).
Claim 7
Independent Claim
127 words
A method of producing a transparent or translucent silicone coated glass fabric comprising (A) applying to a glass fabric a first layer consisting essentially of a polydiorganosiloxane in which the organo radicals are methyl and phenyl radicals in a ratio of from 0.25 to 3.7 in sufficient amount to impregnate and coat the yarns of the glass fabric, but not filling the interstices of the glass fabric, then (B) applying a second layer consisting essentially of a silicone elastomer in sufficient amount to cover the first layer and to fill in the interstices of the glass fabric, then (C) applying a third layer consisting essentially of an elastoplastic organopolysiloxane resin, to yield a transparent or translucent sheet having a glass fiber reinforcement and a smooth, dry surface.
Claim 8
Independent Claim
127 words
A method of producing a transparent or translucent silicone coated glass fabric comprising (A) applying to a glass fabric a first layer consisting essentially of a polydiorganosiloxane in which the organo radicals are methyl and phenyl radicals in a ratio of from 0.25 to 3.7 in sufficient amount to impregnate and coat the yarns of the glass fabric, but not filling the interstices of the glass fabric, then (B) applying a second layer consisting essentially of a silicone elastomer in sufficient amount to cover the first layer and to fill in the interstices of the glass fabric, then (C) applying a third layer consisting essentially of an elastoplastic organopolysiloxane resin, to yield a transparent or translucent sheet having a glass fiber reinforcement and a smooth, dry surface.
Claim 9
Dependent Claim
14 words
The method of claim 6 in which the polydiorganosiloxane of (A) is an elastomer.
Claim 10
Dependent Claim
22 words
The method of claim 7 in which the polydiorganosiloxane of (A) has a methyl to phenyl ratio of from 0.6 to 1.5.
Claim 11
Dependent Claim
150 words
The method of claim 8 in which the silicone elastomer of (B) and the elastoplastic organopolysiloxane resin of (C) form an interface which is an adhesive bond derived from a combination comprising (i) polydiorganosiloxane of the formula X(R 2 SiO) a SiR 2 Y where R is a monovalent hydrocarbon radical containing no more than 6 carbon atoms, X is a condensable endblocking group and a has a value such that the polydiorganosiloxane has a viscosity of greater than 1 Pa·s at 25° C., (ii) a hydroxyl radical containing, solid, benzene soluble resin copolymer consisting essentially of R 3 SiO 1/2 units and SiO 4/2 units where R is as defined above, there being from 0.6 to 0.9 inclusive R 3 SiO 1/2 units for every SiO 4/2 unit, at least 95 percent of all R radicals in (ii) being methyl, and (iii) a condensation catalyst for (i) and (ii).
References Cited (Backward Citations)
US3373053A
Cited
US4489127A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-05-05 | 1989-11-04 | 1990-05-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-05-05 | 1993-11-04 | 1994-05-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-05-05 | 1997-11-04 | 1998-05-06 | $7700.00 | Window Closed / Lapsed |