Hydrotreating catalysts

Claim 2

A process for preparing a composition of matter comprising the steps of: (A) mixing (a) at least one molybdenum and oxygen containing compound, (b) at least one compound of divalent copper, (c) at least one phosphorus and oxygen containing compound, and (d) water, in such amounts and under such conditions as to obtain a solution; (B) mixing the solution obtained in step (A) with an alumina-containing material; (C) heating the mixture obtained in step (B) at a first temperature under such conditions as to at least partially dry said mixture; and (D) heating the at least partially dried mixture obtained in step (C) at a second temperature in the range of from about 200° C. to about 600° C., which is higher than said first temperature, under such conditions as to activate said mixture.

Claim 3

A process in accordance with claim 1, wherein said molybdenum and oxygen containing compound (a) is selected from the group consisting of molybdenum oxides and hydroxides, molybdenum blue, molybdic acids, ammonium and alkali metal orthomolybdates, ammonium and alkali metal dimolybdates, and alkali metal ammonium heptamolybdates, ammonium and alkali metal isomolybdates, phosphomolybdic acid and ammonium salts thereof; said copper compound (b) is selected from the group consisting of copper(II) carbonate, basic copper(II) carbonate, copper(II) hydrogen carbonate, copper(II) oxalate, copper(II) nitrate, copper(II) sulfate, copper(II) halides, copper(II) monocarboxylates containing 1-12 carbon atoms; and said phosphorus and oxygen containing compound is selected from the group consisting of H 3 PO 4 , H 4 P 2 O 7 , (HPO 3 ) n , NH 4 H 2 PO 4 , LiH 2 PO 4 , NaH 2 PO 4 , KH 2 PO 4 , CsH 2 PO 4 , (NH 4 ) 2 HPO 4 , Li 2 HPO 4 , Na 2 HPO 4 , K 2 HPO 4 , Cs 2 HPO 4 , Rb 2 HPO 4 , (NH 4 ) 3 PO 4 , Na 3 PO 4 , K 3 PO.sub. 4, Cs 3 PO 4 , Rb 3 PO 4 , ammonium and alkali metal pyrophosphates, ammonium and alkali metal metaphosphates, H 3 PO 3 , ammonium and alkali metal phosphites.

Claim 4

A process in accordance with claim 1, wherein said solution obtained in step (A) comprises about 0.002-1.0 mole/l Mo, about 0.001-0.5 mole/l Cu and about 0.005-5.0 mole/l P.

Claim 5

A process in accordance with claim 1, wherein said heating in step (C) is carried out at a temperature ranging from about 25° to about 200° C. and said heating in step (D) is carried out in a non-reducing gas atmosphere at a temperature ranging from about 300° C. to about 600° C.

Claim 6

A process in accordance with claim 1, wherein said molybdenum and oxygen containing compound is MoO 3 , said copper compound (b) is basic copper(II) carbonate, and the phosphorus compound is H 3 PO 4 .

Claim 7

A process in accordance with claim 5, wherein the amounts dissolved in 1 liter of said solution comprises about 0.005-0.5 mole/l Mo, about 0.002-0.2 mole/l Cu and about 0.005-1.0 mole/l P.

Claim 8

A process in accordance with claim 1, wherein said alumina-containing support material has a surface area ranging from about 20 m 2 /g to about 350 m 2 /g.

Claim 9

A composition of matter, suitable as a catalyst composition, having been prepared by a process comprising the steps of: (A) mixing (a) at least one molybdenum and oxygen containing compound, (b) at least one compound of divalent copper, (c) at least one phosphorus and oxygen containing compound, and (d) water, in such amounts and under such conditions as to obtain a solution; (B) mixing the solution obtained in step (A) with an alumina-containing material; (C) heating the mixture obtained in step (B) at a first temperature under such conditions as to at least partially dry said mixture; and (D) heating the at least partially dried mixture obtained in step (C) at a second temperature in the range of from about 200° C. to about 600° C., which is higher than said first temperature, under such conditions as to activate said mixture.

Claim 10

A composition of matter, suitable as a catalyst composition, having been prepared by a process comprising the steps of: (A) mixing (a) at least one molybdenum and oxygen containing compound, (b) at least one compound of divalent copper, (c) at least one phosphorus and oxygen containing compound, and (d) water, in such amounts and under such conditions as to obtain a solution; (B) mixing the solution obtained in step (A) with an alumina-containing material; (C) heating the mixture obtained in step (B) at a first temperature under such conditions as to at least partially dry said mixture; and (D) heating the at least partially dried mixture obtained in step (C) at a second temperature in the range of from about 200° C. to about 600° C., which is higher than said first temperature, under such conditions as to activate said mixture.

Claim 11

A composition of matter in accordance with claim 8, wherein said molybdenum and oxygen containing compound (a) is selected from the group consisting of molybdenum oxides and hydroxides, molybdenum blue, molybdic acids, ammonium and alkali metal orthomolybdates, ammonium and alkali metal dimolybdates, and alkali metal ammonium heptamolybdates, ammonium and alkali metal isomolybdates, phosphomolybdic acid and ammonium salts thereof; said copper compound (b) is selected from the group consisting of copper(II) carbonate, basic copper(II) carbonate, copper(II) hydrogen carbonate, copper(II) oxalate, copper(II) nitrate, copper(II) sulfate, copper(II) halides, copper(II) monocarboxylates containing 1-12 carbon atoms; and said phosphorus and oxygen containing compound is selected from the group consisting of H 3 PO 4 , H 4 P 2 O 7 , (HPO 3 ) n , NH 4 H 2 PO 4 , LiH 2 PO 4 , NaH 2 PO 4 , KH 2 PO 4 , CsH 2 PO 4 , (NH 4 ) 2 HPO 4 , Li 2 HPO 4 , Na 2 HPO 4 , K 2 HPO 4 , Cs 2 HPO 4 , Rb 2 HPO 4 , (NH 4 ) 3 PO 4 , Na 3 PO 4 , K 3 PO 4 , Cs 3 PO 4 , Rb 3 PO 4 , ammonium and alkali metal pyrophosphates, ammonium and alkali metal metaphosphates, H 3 PO 3 , ammonium and alkali metal phosphites.

Claim 12

A composition of matter in accordance with claim 8, wherein said solution obtained in step (A) comprises about 0.002-1.0 mole/l Mo, about 0.001-0.5 mole/l Cu, and about 0.005-5.0 mole/l P.

Claim 13

A composition of matter in accordance with claim 8, wherein said heating in step (C) is carried out at a temperature ranging from about 25° C. to about 200° C. and said heating in step (D) is carried out in a non-reducing gas atmosphere at a temperature ranging from about 300° C. to about 600° C.

Claim 14

A composition of matter in accordance with claim 8, wherein said molybdenum and oxygen containing compound (a) is MoO 3 , said copper compound (b) is basic copper(II) carbonate, and said phosphorus and oxygen containing compound (c) is H 3 PO 4 .

Claim 15

A composition of matter in accordance with claim 8 comprising from about 0.1 to about 5.0 weight-% Mo, based on the weight of the entire catalyst composition; from about 0.02 to about 2.5 weight-% of Cu, based on the weight of the entire catalyst composition; from about 0.001 to about 10 weight-% P, based on the weight of the entire catalyst composition, and having a surface area ranging from about 20 m 2 /g to about 350 m 2 g.

Claim 16

A composition of matter in accordance with claim 8, comprising from about 0.3 to about 2.0 weight-% Mo, based on the entire catalyst composition; from about 0.05 to about 1.0 weight-% of Cu, based on the entire catalyst composition; from about 0.01 to about 6.0 weight-% P, based on the entire catalyst composition; and having a surface area ranging from about 100 to about 250 m 2 /g.