Catalyst
Assignee: Imperial Chemical Industries Ltd
•
Filing: 1976-12-01
•
Granted: 1978-03-21
•
Expires: 1996-12-01
Abstract
Abstract A catalyst composition for hydrogenative purification of hydrocarbons contains a divalent oxide such as CoO, a polyvalent oxide such as MoO 3 , pseudobohmite and/or pseudogamma alumina and preferably also a clay mineral and is made using a defined procedure in which active components are added before and after shaping by wet granulation or extrusion.
Inventors
- 👤 Thomas Vincent Whittam
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 15:26
CPC Classifications
B; B01; B01J; B01J37/00; B01J37/0009; B01J21/00; B01J21/16; B01J37/04; C; C10; C10G; C10G45/00; C10G45/02; C10G45/04
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
91 words
A catalyst composition comprising pseudobohmite alumina and/or pseudogamma alumina, a clay mineral, an oxide of at least one divalent metal selected from the group of transition metals and metals from Group IIA of the Periodic Table and an oxide of at least one polyvalent metal from Groups VA, VIA or VIIA of the Periodic Table, and being in the form of extrudates or approximately spherical granules of diameter at least 0.5 mm, said clay mineral being present in an amount sufficient to increase the mechanical strength of the extrudates or granules.
Claim 2
Dependent Claim
91 words
A catalyst composition comprising pseudobohmite alumina and/or pseudogamma alumina, a clay mineral, an oxide of at least one divalent metal selected from the group of transition metals and metals from Group IIA of the Periodic Table and an oxide of at least one polyvalent metal from Groups VA, VIA or VIIA of the Periodic Table, and being in the form of extrudates or approximately spherical granules of diameter at least 0.5 mm, said clay mineral being present in an amount sufficient to increase the mechanical strength of the extrudates or granules.
Claim 3
Dependent Claim
29 words
A composition according to claim 1 containing also alumina of a type formed under acid conditions, to the extent of 0.5 to 10% of the pseudobohmite and pseudo-gamma aluminas.
Claim 4
Dependent Claim
25 words
A composition according to claim 1 in which the clay mineral sepiolite is present to the extent of 10 to 25% of the total composition.
Claim 5
Dependent Claim
65 words
A composition according to claim 1 in the form of granules having a largest dimension in the range 2-5 mm, a mean diametrical crushing strength of 3-10 kg, a bulk density in the range 0.3 to 0.8 g/ml and a pore volume in the range 0.5 to 1.5 ml/g, at least 0.03 ml/g of which is in pores of diameter greater than 2000 Angstrom units.
Claim 6
Dependent Claim
73 words
A composition according to claim 1 in the form of cylindrical extrudates having a largest dimension in the range 2-12 mm, a diameter in the range 2-5 mm, a mean diametrical crushing strength of 20-75 kg, a bulk density in the range 0.4 to 1.0 g/ml and a pore volume in the range 0.5 to 1.5 ml/g, at least 0.03 ml/g of which is in pores of diameter greater than 2000 Angstrom units.
Claim 7
Independent Claim
125 words
A method of making a catalyst composition comprising pseudobohmite alumina, pseudogamma alumina or mixtures thereof, 0-80% of a clay mineral, an oxide of at least one divalent metal and an oxide of at least one polyvalent metal from Groups VA, VIA or VIIA of the Periodic Table which comprises the steps: (a) forming a mixture of said alumina with at least one divalent metal oxide or a compound thermally decomposable thereto and a clay mineral if present; (b) shaping said mixture by extrusion or granulation into approximately spherical granules of diameter at least 0.5 mm; (c) adding at least one oxide of a polyvalent metal from Group VA, VIA or VIIA or a compound thermally decomposable thereto; and (d) drying and calcining the resulting product.
Claim 8
Independent Claim
125 words
A method of making a catalyst composition comprising pseudobohmite alumina, pseudogamma alumina or mixtures thereof, 0-80% of a clay mineral, an oxide of at least one divalent metal and an oxide of at least one polyvalent metal from Groups VA, VIA or VIIA of the Periodic Table which comprises the steps: (a) forming a mixture of said alumina with at least one divalent metal oxide or a compound thermally decomposable thereto and a clay mineral if present; (b) shaping said mixture by extrusion or granulation into approximately spherical granules of diameter at least 0.5 mm; (c) adding at least one oxide of a polyvalent metal from Group VA, VIA or VIIA or a compound thermally decomposable thereto; and (d) drying and calcining the resulting product.
Claim 9
Dependent Claim
27 words
A method according to claim 6 in which a strong acid salt of the divalent metal or metals is contacted with the pseudobohmite before the shaping operation.
Claim 10
Dependent Claim
28 words
A method according to claim 6 in which the extrusions or approximate spheres are calcined at 500°-900° C before adding the compounds of the polyvalent metal or metals.
Claim 11
Dependent Claim
66 words
A method according to claim 6 in which the particle diameter distribution of the pseudobohmite is: ______________________________________
Diameter, microns %
______________________________________
over 600 0.0
300 - 600 0 - 15
105 - 300 5 - 45
75 - 105 0 - 20
40 - 75 15 - 30
20 - 40 10 - 30
10 - 20 0 - 30
under 10 0 - 30.
______________________________________
Claim 12
Dependent Claim
29 words
A composition according to claim 1 in which the clay mineral is selected from the group consisting of kaolinites, montmorillonites, attapulgites, sepiolites, illites, allophanes, fuller's earth, chlorite and serpentine.
Claim 13
Dependent Claim
18 words
A composition according to claim 10 wherein said clay mineral is present in an amount of from 10-25%.
Claim 14
Dependent Claim
17 words
A composition according to claim 10 wherein said clay mineral is present in an amount from 25-80%.
Claim 15
Dependent Claim
54 words
A method according to claim 6 in which the particle diameter distribution of the pseudobohmite is ______________________________________
diameter, microns % by weight
______________________________________
over 105 0.0
40 - 105 0.15
20 - 40 15 - 25
10 - 20 20 - 40
under 10 30 - 50
______________________________________ and no clay mineral is present.
Claim 16
Dependent Claim
20 words
A method according to claim 9 in which the clay mineral is mixed with the pseudobohmite before the shaping operation.
Claim 17
Dependent Claim
23 words
A method according to claim 6 in which the clay mineral content is in the range 10 to 25% of the finished composition.
Claim 18
Dependent Claim
23 words
A method according to claim 6 in which the clay mineral content is in the range 45 to 65% of the finished composition.
Claim 19
Dependent Claim
41 words
A method according to claim 6 in which a strong acid or a water-soluble aluminium salt is present during shaping, to the extent of 0.1 to 10% by weight, calculated as equivalent HNO 3 , of the alumina introduced as pseudobohmite.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-03-20 | 1981-09-19 | 1982-03-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-03-20 | 1985-09-19 | 1986-03-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-03-20 | 1989-09-19 | 1990-03-21 | $7700.00 | Window Closed / Lapsed |