US4585535A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Electrophoretic method of producing high-density magnetic recording media
Assignee: HP Indigo BV
•
Filing: 1985-03-11
•
Granted: 1986-04-29
•
Expires: 2005-03-11
Abstract
Abstract A magnetic recording medium having a coating of magnetic particles deposited thereon by electrophoresis. Magnetic particles are encapsulated by dry milling in a thermoplastic binder which is insoluble at ambient or room temperatures and is softenable at temperatures higher than 70° C. A charge director for producing functional sites in the binder is incorporated in the encapsulating polymer during the dry-milling step. The encapsulated mass is comminuted or pulverized and then wet-milled with a major amount of a low-boiling aliphatic hydrocarbon liquid. A suspension is then formed with additional hydrocarbon liquid. Additional charge director may be added, either during the wet-milling step or during the suspension-forming step. The suspension is then used as a bath from which the coating is deposited by electrophoresis. The magnetic particles are oriented by the application of a magnetic field, either during the depositing step or subsequent thereto. If subsequent, the binder is heated to soften the same. The final coating is then cured by any appropriate means, such as an electron beam.
Inventors
- 👤 Arden Sher
- 👤 Karen Sabo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 21:31
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/44; C09D5/448; G; G11; G11B; G11B5/00; G11B5/62; G11B5/68; G11B5/70; G11B5/712
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
108 words
A method of making a composition adapted to deposit a magnetic coating by electrophoresis on a carrier medium including the steps of dry-milling a major amount of magnetic particles with a minor amount of a binder and a minor amount of charge director to produce a solid chip of encapsulated magnetic particles, comminuting said chip into small pieces, wet-milling a minor amount of said chip pieces with a major amount of a low-boiling aliphatic hydrocarbon liquid to produce a suspension, depositing encapsulated magnetic particles from said suspension on a carrier medium by electrophoresis, orienting said magnetic particles, and then curing the binder to produce a magnetic recording medium.
Claim 2
Independent Claim
108 words
A method of making a composition adapted to deposit a magnetic coating by electrophoresis on a carrier medium including the steps of dry-milling a major amount of magnetic particles with a minor amount of a binder and a minor amount of charge director to produce a solid chip of encapsulated magnetic particles, comminuting said chip into small pieces, wet-milling a minor amount of said chip pieces with a major amount of a low-boiling aliphatic hydrocarbon liquid to produce a suspension, depositing encapsulated magnetic particles from said suspension on a carrier medium by electrophoresis, orienting said magnetic particles, and then curing the binder to produce a magnetic recording medium.
Claim 3
Dependent Claim
20 words
A method as in claim 1 in which additional charge director is added in the process before the depositing step.
Claim 4
Dependent Claim
17 words
A method as in claim 2 in which additional charge director is added in the wet-milling step.
Claim 5
Independent Claim
121 words
A method of making a composition adapted to deposit a magnetic coating by electrophoresis on a carrier medium including the steps of dry-milling a major amount of ferriferous particles with a minor amount of a binder and a minor amount of a charge director adapted to produce functional sites to form a solid chip of encapsulated ferriferous particles, reducing the chip to a powder in a micropulverizing step, wet-milling a minor amount of said powder with a major amount of a low-boiling aliphatic hydrocarbon liquid and a charge director to produce a suspension, depositing encapsulated ferriferous particles from said suspension on a carrier medium by electrophoresis, orienting said ferriferous particles, and then curing the binder to produce a magnetic recording medium.
Claim 6
Independent Claim
121 words
A method of making a composition adapted to deposit a magnetic coating by electrophoresis on a carrier medium including the steps of dry-milling a major amount of ferriferous particles with a minor amount of a binder and a minor amount of a charge director adapted to produce functional sites to form a solid chip of encapsulated ferriferous particles, reducing the chip to a powder in a micropulverizing step, wet-milling a minor amount of said powder with a major amount of a low-boiling aliphatic hydrocarbon liquid and a charge director to produce a suspension, depositing encapsulated ferriferous particles from said suspension on a carrier medium by electrophoresis, orienting said ferriferous particles, and then curing the binder to produce a magnetic recording medium.
Claim 7
Dependent Claim
49 words
A method as in claim 4 in which said carrier medium is metal and in which the thickness of the deposit during the electrophoretic depositing step is controlled by an application of voltage between 400 volts and 1000 volts for a period of between 0.001 second and 1 second.
Claim 8
Dependent Claim
22 words
A method as in claim 4 in which said micropulverizing step forms a powder having an average particle size of 200 microns.
Claim 9
Dependent Claim
25 words
A method as in claim 4 in which said wet-milling step is carried on with sufficient low-boiling aliphatic hydrocarbon liquid to produce 40 percent solids.
Claim 10
Dependent Claim
24 words
A method as in claim 4 in which said suspension is diluted to 20 percent solids in order to enable storage of the composition.
Claim 11
Dependent Claim
26 words
A method as in claim 4 in which said suspension is diluted to between 1 percent solids to 5 percent solids before practicing the depositing step.
Claim 12
Dependent Claim
30 words
A method as in claim 4 in which said carrier medium is an insulator and the applied voltage during the electrophoretic depositing step is between 2000 volts and 5000 volts.
Claim 13
Dependent Claim
23 words
A method as in claim 4 in which there are a plurality of magnetic particles present in powder form during the micropulverizing step.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-04-28 | 1989-10-28 | 1990-04-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-04-28 | 1993-10-28 | 1994-04-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-04-28 | 1997-10-28 | 1998-04-29 | $7700.00 | Window Closed / Lapsed |