US4039697A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for forming a film composed of plastic-coated inorganic powder particles
Assignee: Fujikura Cable Works Ltd
•
Filing: 1974-08-21
•
Granted: 1977-08-02
•
Expires: 1994-08-21
Abstract
Abstract A uniform, thick film is formed by applying a powdered metal, alloy, sulfide of metal or glass each particle of which is coated with plastics 1-15% by weight, preferably the particle surfaces having been treated with an aliphatic acid or a silane-type surface-treating agent and the plastics including an organic peroxide, to a substrate by electrostatic powder spraying, fluidized bed coating, electrophoretic deposition, or by electrostatic fluidization, and fixing the layer thus provided on the substrate with heating to such extent that the plastic ingredient is fused or volatilized, to finally produce the desired film. The materials having such films fixed thereon have a wide application for interior building and glass-lining and as material of bearings.
Inventors
- 👤 Kazuo Isawa
- 👤 Masatsugu Maejima
- 👤 Hideo Nagasaka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 22:39
CPC Classifications
C; C23; C23D; C23D5/00; C23D5/04; C23C; C23C24/00; C23C24/08
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
119 words
A process of forming a uniform film at least 200μ thick on a substrate which comprises surface-treating an inorganic substance having a particle size range from 0.1 to 500 microns with a surface-treating agent to render its surface compatible with plastics, said surface-treating agent being selected from the group consisting of stearic acid, palmitic acid, gamma-methacryloxypropyltrimethoxy silane, gamma-glycidoxypropyltrimethoxy silane, and beta-ethyltrimethoxy silane, coating each surface-treated particles with plastic in an amount equal to 1 to 15% by weight of the particle, drying the coated particles, applying said dried coated particles to the substrate, and heating and fixing the layer thus provided on the substrate surface at a temperature between the melting point and the volatilizing point of the plastic.
Claim 2
Dependent Claim
119 words
A process of forming a uniform film at least 200μ thick on a substrate which comprises surface-treating an inorganic substance having a particle size range from 0.1 to 500 microns with a surface-treating agent to render its surface compatible with plastics, said surface-treating agent being selected from the group consisting of stearic acid, palmitic acid, gamma-methacryloxypropyltrimethoxy silane, gamma-glycidoxypropyltrimethoxy silane, and beta-ethyltrimethoxy silane, coating each surface-treated particles with plastic in an amount equal to 1 to 15% by weight of the particle, drying the coated particles, applying said dried coated particles to the substrate, and heating and fixing the layer thus provided on the substrate surface at a temperature between the melting point and the volatilizing point of the plastic.
Claim 3
Dependent Claim
28 words
The process according to claim 1 wherein the inorganic powdered substance is selected from the group consisting of metals, alloys, sulfides of metals, carbon fluoride, ceramics, and glass.
Claim 4
Dependent Claim
44 words
The process according to claim 2 wherein the metals are copper, aluminum, titanium, and nickel; the alloys are brass and bronze; the sulfides of metals are disulfide molybdenum and disulfide tungsten; glass is silicate glass, soda-lime glass, potassium-lime glass, lead glass, and borate-silicate glass.
Claim 5
Dependent Claim
23 words
The process according to claim 1 wherein the application of the plastic-coated inorganic particles to the substrate is conducted by electrostatic powder spraying.
Claim 6
Dependent Claim
23 words
The process according to claim 1 wherein the application of the dried plastic-coated inorganic particles to the substrate is conducted by electrophoretic deposition.
Claim 7
Dependent Claim
22 words
The process according to claim 1 wherein the application of the plastic-coated inorganic particles to the substrate is conducted by electrostatic fluidization.
Claim 8
Dependent Claim
23 words
The process according to claim 1 wherein the application of the plastic-coated inorganic particles to the substrate is conducted by fluidized bed coating.
Claim 9
Dependent Claim
34 words
The process according to claim 1 wherein the plastic is selected from the group consisting of polyethylene resin, polystyrene resin, epoxy resin, polymethylmethacrylate resin, polyvinyl chloride resin, polyvinyl alcohol resin, polyester resin and ethylcellulose.
Claim 10
Dependent Claim
15 words
The process according to claim 1 wherein an organic peroxide is added to the plastic.
Claim 11
Dependent Claim
25 words
The process according to claim 1 wherein the layer provided on the substrate surface is heated to such extent that the plastic ingredient is fused.
Claim 12
Dependent Claim
25 words
The process according to claim 1 wherein the layer provided on the substrate surface is heated to such extent that the plastic ingredient is volatilized.
References Cited (Backward Citations)
US3093511A
Cited
US3464906A
Cited
US3616388A
Cited
US3575900A
Cited
US3844919A
Cited
US3928668A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-01 | 1981-01-31 | 1981-08-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-01 | 1985-01-31 | 1985-08-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-01 | 1989-01-31 | 1989-08-02 | $7700.00 | Window Closed / Lapsed |