Automated chemical milling process
Assignee: Grumman Corp
•
Filing: 1983-02-10
•
Granted: 1986-04-29
•
Expires: 2003-02-10
Abstract
Abstract The specification discloses an automated chemical milling process for metal articles. The metal article is first coated with an etchant resist coating. In one embodiment the area to be etched is digitized to define the x,y coordinate values for the perimeter line around the area. A CPU is used to control a flat bed drafting table with a tangially controlled scribing tool to cut through the resist coating along the perimeter line. If plural etching steps are used, each perimeter line is digitized and scribed or cut in a similar manner. All but one of the perimeter lines are recoated and marked and the resist coating within the remaining perimeter line is removed. The metal part is then etched as desired. If plural etching steps are used the resist coating for each separate area is removed between sequential etching baths. In a second embodiment, the x,y,z point coordinate values for a perimeter line on a three dimensional work piece are defined, and the scribing operation is done by a robotic device controlled by a CPU. In a third embodiment, new template or mask geometry is created on a CRT and digitized for subsequent control of the plotting table or other robotic device. Digital signals are used to define the x,y or x,y,z point coordinates values while analogue signals are used to control the scribing tool.
Inventors
- 👤 Herbert R. Jaffe
- 👤 Irwin Mitzelman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 21:06
CPC Classifications
C; C23; C23F; C23F1/00; C23F1/02; C23F1/04
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
111 words
An automated chemical milling process for metals, said process comprising the steps of: a. coating the metal to be etched with a resist coating; b. digitizing the area(s) to be etched to define x,y coordinate values for the perimeter of the area(s) to be etched; c. automatically scribing the metal and coating with a scribing tool, said scribing tool cutting through said coating along the perimeter defined by the x,y coordinate values; d. removing the resist coating from the area(s) to be etched; and e. immersing said partially coated metal into an etching solution for a predetermined period of time to remove a predetermined amount of metal from the uncoated area(s);
Claim 2
Dependent Claim
111 words
An automated chemical milling process for metals, said process comprising the steps of: a. coating the metal to be etched with a resist coating; b. digitizing the area(s) to be etched to define x,y coordinate values for the perimeter of the area(s) to be etched; c. automatically scribing the metal and coating with a scribing tool, said scribing tool cutting through said coating along the perimeter defined by the x,y coordinate values; d. removing the resist coating from the area(s) to be etched; and e. immersing said partially coated metal into an etching solution for a predetermined period of time to remove a predetermined amount of metal from the uncoated area(s);
Claim 3
Dependent Claim
87 words
An automated chemical milling process as claimed in claim 1, which further includes the steps of: a. separately scribing more than one area to be etched for each metal part; b. recoating the cut scribed lines for all but one of the areas to be etched; c. sequentially removing the resist coating from each of the areas to be etched between separate additional immersions in said etching solution; whereby each of the defined areas to be etched is immersed in said solution for differing cumulative time periods.
Claim 4
Dependent Claim
59 words
An automated chemical milling process for metals as claimed in claims 1 or 2, which further includes the step of marking the perimeter(s) of the area(s) cut by said scribing tool with a visible marker, said marker marking said coating along the perimeter line(s) defined by the x,y coordinate values, said marking occurring before said resist coating is removed.
Claim 5
Dependent Claim
29 words
An automated chemical milling process for metals as claimed in claim 2, wherein the recoating step utilizes a visable sealant to simultaneously reseal and mark the cut scribe lines.
Claim 6
Dependent Claim
46 words
An automated chemical milling process for metals as claimed in claims 1 or 2, which further includes the step of nesting the perimeter lines of each of the areas to be etched when more than one part is to be etched from a single metal plate.
Claim 7
Dependent Claim
40 words
An automated chemical milling process for metals as claimed in claim 1, which further includes the step of applying a predetermined constant downward force on the scribing tool as it moves along a line defined by two x,y point values.
Claim 8
Dependent Claim
52 words
An automated chemical milling process for metals as claimed in claim 6, which further includes the step of raising the scribing tool whenever a line or curve described by a future set of x,y values from a line or curve scribed from a previous set of x,y values by more than 7°.
Claim 9
Dependent Claim
36 words
An automated chemical milling process for metals as claimed in claims 1 or 2 or 6 or 7, in which the metal is aluminum or its alloys, and the etching bath is an alkali metal hydroxide.
Claim 10
Dependent Claim
35 words
An automated chemical milling process for metals as claimed in claims 1 or 2 or 6 or 7, in which the metal is titanium or its alloys, and the etching bath is a hydrohalic acid.
Claim 11
Dependent Claim
27 words
An automated chemical milling process for metals as claimed in claims 1 or 2 or 6 or 7, wherein said resist coating is a butadiene styrene copolymer.
Claim 12
Dependent Claim
32 words
An automated chemical milling process for metals as claimed in claims 1 or 2 or 6 or 7, which further includes the scribing and etching of registration marks in a metal plate.
Claim 13
Dependent Claim
22 words
An automated chemical milling process for metals as claimed in claim 11 wherein tooling holes are subsequently formed from said registration marks.
Claim 14
Dependent Claim
129 words
An automated chemical milling process for three-dimensional metal parts, said process comprising the steps of: a. coating the metal to be etched with a resist coating; b. defining a three-dimensional space with three separate x,y,z axes, wherein no two axes are parallel to one another; c. digitizing the x,y,z point coordinate values along a perimeter of the three-dimensional area to be etched; d. automatically scribing the coating and metal with a scribing tool, said scribing tool cutting through said coating along the three-dimensional perimeter defined by said x,y,z point coordinate value; e. removing the resist coating from the area to be etched; f. immersing said partially coated metal into an etching solution for a predetermined period of time to remove a predetermined amount of metal from the uncoated area.
Claim 15
Dependent Claim
129 words
An automated chemical milling process for three-dimensional metal parts, said process comprising the steps of: a. coating the metal to be etched with a resist coating; b. defining a three-dimensional space with three separate x,y,z axes, wherein no two axes are parallel to one another; c. digitizing the x,y,z point coordinate values along a perimeter of the three-dimensional area to be etched; d. automatically scribing the coating and metal with a scribing tool, said scribing tool cutting through said coating along the three-dimensional perimeter defined by said x,y,z point coordinate value; e. removing the resist coating from the area to be etched; f. immersing said partially coated metal into an etching solution for a predetermined period of time to remove a predetermined amount of metal from the uncoated area.
Claim 16
Dependent Claim
86 words
An automated chemical milling process for three-dimensional metal parts, as claimed in claim 13, which further includes the steps of: a. separately scribing more than one area to be etched for a single three-dimensional metal part; b. recoating the cut scribed lines for all but one of the areas to be etched; c. sequentially removing the areas to be etched between separate immersions in the etching solution; whereby each of the defined areas to be etched is immersed in said solution for differing cumulative time periods.
Claim 17
Dependent Claim
32 words
An automated chemical milling process for three-dimensional metal parts as claimed in claim 14, wherein the recoating step utilizes a visable sealant material to simultaneously reseal and mark the cut scribe lines.
Claim 18
Dependent Claim
54 words
An automated chemical milling process for three-dimensional metal parts as claimed in claim 13, which further includes the steps of defining three or more rotational axes for the scribing tool, said scribing tool selecting one or more of said rotational axes as it traverses said three dimensional space defined by said x,y,z coordinate values.
Claim 19
Dependent Claim
59 words
An automated chemical milling process for three-dimensional metal parts as claimed in claims 13 or 14 or 16, which further includes the step of marking the areas cut by said scribing tool with a visible marker, said marker marking said coating along the three-dimensional surface traversed by said scribing tool, said marking occurring before said resist coating is removed.
Claim 20
Dependent Claim
46 words
An automated chemical milling process for three-dimesnional metal parts as claimed in claims 13 or 14 or 15 or 16, which further includes the step of nesting the areas to be etched when more than one part is to be etched from a single metal plate.
Claim 21
Dependent Claim
72 words
An automated chemical milling process for three-dimensional metal parts as claimed in claims 13 or 14 or 16, which further includes the step of applying a predetermined constant force on the scribing tool to force said scribing tool into engagement with said three-dimensional metal part, said force being applied perpendicularly to a plane defined by at least two of said x,y,z coordinate point values for each point traversed by said scribing tool.
Claim 22
Dependent Claim
60 words
An automated chemical milling process for three dimensional metal parts as claimed in claim 16, which further includes a step of raising the scribing tool whenever a line or curve described by a future set of x,y,z point coordinate values varies from a line or curve described from a previous set of x,y,z point coordinate values by more than 7°.
Claim 23
Dependent Claim
39 words
An automated chemical milling process for three dimensional metal parts as claimed in claims 13 or 14 or 15 or 16, in which the metal is aluminum or its alloys, and the etching bath if an alkali metal hydroxide.
Claim 24
Dependent Claim
37 words
An automated chemical milling process for three dimensional metal parts as claimed in claims 13 or 14 or 15 or 16, in which the metal is titanium or its alloys, and the etching bath is hydrohalic acid.
Claim 25
Dependent Claim
30 words
An automated chemical milling process for three dimensional metal parts as claimed in claims 13 or 14 or 15 or 16, wherein said resist coating is a butadiene styrene copolymer.
Claim 26
Dependent Claim
37 words
An automated chemical milling process for three dimensional metal parts as claimed in claims 13 or 14 or 15 or 16, which further includes the step of scribing and etching registration marks in the three-dimensional metal parts.
Claim 27
Dependent Claim
25 words
An automated chemical milling process for three dimensional metal parts as claimed in claim 24 wherein tooling holes are subsequently formed from said registration marks.
References Cited (Backward Citations)
US2888335A
Cited
US3227589A
Cited
US3380863A
Cited
US3555950A
Cited
US3745079A
Cited
US3803960A
Cited
US3805650A
Cited
US3988254A
Cited
US3991636A
Cited
US3895358A
Cited
US4145723A
Cited
US4171657A
Cited
US4137118A
Cited
US4325779A
Cited
US4294649A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-04-28 | 1989-10-28 | 1990-04-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-04-28 | 1993-10-28 | 1994-04-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-04-28 | 1997-10-28 | 1998-04-29 | $7700.00 | Window Closed / Lapsed |