Method for making rare-earth element containing permanent magnets
Assignee: VAC MAGNETICS Corp
•
Filing: 1984-04-09
•
Granted: 1986-04-29
•
Expires: 2004-04-09
Abstract
Abstract A method for making rare earth-permanent magnets wherein a molten mass of a rare earth magnet alloy is produced such as by induction melting and while in a protective atmosphere is introduced in the form of a stream into a chamber having a protective atmosphere and a bottom portion containing a cooling medium, such as a cryogenic liquid which may be liquid argon. After cooling and solidification, the alloy is collected from the chamber and comminuted to produce particles. The particles are formed into a magnet body. Alternately, the stream may be atomized, as by striking the same with a jet of inert gas, to produce discrete droplets, which droplets are directed to the cooling medium at the chamber bottom for cooling, solidification and collection.
Inventors
- 👤 Kalatur S. V. L. Narasimhan
- 👤 Edward J. Dulis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 09:37
CPC Classifications
B; B22; B22F; B22F9/00; B22F9/02; B22F9/06; B22F9/08; B22F9/082; H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/032; H01F1/04; H01F1/047; H01F1/053; H01F1/055; H01F1/057; H01F1/0571; H01F1/0574; H01F1/0575; H01F1/0576; B22F2009/086
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
86 words
A method for making rare-earth permanent magnets, said method comprising producing a molten mass of a rare-earth magnet alloy, maintaining said molten mass in a protective atmosphere while introducing said molten mass into a chamber having a protective atmosphere and a bottom portion containing a cryogenic liquid cooling medium, cooling and collecting said molten mass in said bottom portion to form a solidified mass, removing said solidified mass from said chamber, comminuting said solidified mass to produce particles and compacting said particles into a magnet body.
Claim 2
Independent Claim
86 words
A method for making rare-earth permanent magnets, said method comprising producing a molten mass of a rare-earth magnet alloy, maintaining said molten mass in a protective atmosphere while introducing said molten mass into a chamber having a protective atmosphere and a bottom portion containing a cryogenic liquid cooling medium, cooling and collecting said molten mass in said bottom portion to form a solidified mass, removing said solidified mass from said chamber, comminuting said solidified mass to produce particles and compacting said particles into a magnet body.
Claim 3
Dependent Claim
20 words
The method of claim 1 wherein said molten mass of said rare-earth magnet alloy is produced by vacuum induction melting.
Claim 4
Dependent Claim
19 words
The method of claim 1 wherein said cryogenic liquid is liquid argon and said chamber has an argon atmosphere.
Claim 5
Dependent Claim
18 words
The method of claim 1 wherein said particles are within the size range of 1 to 5 microns.
Claim 6
Independent Claim
88 words
A method for making rare-earth permanent magnets, said method comprising producting a molten mass of a rare-earth magnet alloy, maintaining said molten mass in a protective atmosphere while introducing a stream of said molten mass into a chamber having a protective atmosphere and a bottom portion containing a cryogenic liquid cooling medium, atomizing said stream with an inert gas to form droplets, cooling and collecting said droplets in said bottom portion to produce particles, removing said particles from said chamber and compacting said particles into a magnet body.
Claim 7
Independent Claim
88 words
A method for making rare-earth permanent magnets, said method comprising producting a molten mass of a rare-earth magnet alloy, maintaining said molten mass in a protective atmosphere while introducing a stream of said molten mass into a chamber having a protective atmosphere and a bottom portion containing a cryogenic liquid cooling medium, atomizing said stream with an inert gas to form droplets, cooling and collecting said droplets in said bottom portion to produce particles, removing said particles from said chamber and compacting said particles into a magnet body.
Claim 8
Dependent Claim
11 words
The method of claim 5 wherein said inert gas is argon.
Claim 9
Dependent Claim
20 words
The method of claim 6 wherein said molten mass of said rare-earth magnet alloy is produced by vacuum induction melting.
Claim 10
Dependent Claim
19 words
The method of claim 5 wherein said cryogenic liquid is liquid argon and said chamber has an argon atmosphere.
Claim 11
Dependent Claim
23 words
The method of claim 8 wherein said particles are comminuted to produce finer particles within the size range of 1 to 5 microns.
Claim 12
Independent Claim
106 words
A method for making rare-earth permanent magnets, said method comprising producing a molten mass of a rare-earth magnet alloy of the composition in weight percent 35 to 38 effective neodymium, 60 to 64.8 iron and 0.2 to 2 boron, maintaining said molten mass in a protective atmosphere while introducing said molten mass into a chamber having a protective atmosphere and a bottom portion containing a cryogenic liquid cooling medium, cooling and collecting said molten mass in said cooling medium to form a solidified mass, removing said solidified mass from said chamber, comminuting said solidified mass to produce particles and compacting said particles into a magnet body.
Claim 13
Independent Claim
106 words
A method for making rare-earth permanent magnets, said method comprising producing a molten mass of a rare-earth magnet alloy of the composition in weight percent 35 to 38 effective neodymium, 60 to 64.8 iron and 0.2 to 2 boron, maintaining said molten mass in a protective atmosphere while introducing said molten mass into a chamber having a protective atmosphere and a bottom portion containing a cryogenic liquid cooling medium, cooling and collecting said molten mass in said cooling medium to form a solidified mass, removing said solidified mass from said chamber, comminuting said solidified mass to produce particles and compacting said particles into a magnet body.
Claim 14
Dependent Claim
20 words
The method of claim 10 wherein said molten mass of said rare-earth magnet alloy is produced by vacuum induction melting.
Claim 15
Dependent Claim
19 words
The method of claim 10 wherein said cryogenic liquid is liquid argon and said chamber has an argon atmosphere.
Claim 16
Dependent Claim
18 words
The method of claim 10 wherein said particles are within the size range of 1 to 5 microns.
Claim 17
Independent Claim
108 words
A method for making rare-earth permanent magnets, said method comprising producing a molten mass of a rare-earth magnet alloy of the composition in weight percent 35 to 38 effective neodymium, 60 to 64.8 iron and 0.2 to 2 boron, maintaining said molten mass in a protective atmosphere while introducing a stream of said molten mass into a chamber having a protective atmosphere and a bottom portion containing a cryogenic liquid cooling medium, atomizing said stream with an inert gas to form droplets, cooling and collecting said droplets in said cooling medium to produce particles, removing said particles from said chamber and compacting said particles into a magnet body.
Claim 18
Independent Claim
108 words
A method for making rare-earth permanent magnets, said method comprising producing a molten mass of a rare-earth magnet alloy of the composition in weight percent 35 to 38 effective neodymium, 60 to 64.8 iron and 0.2 to 2 boron, maintaining said molten mass in a protective atmosphere while introducing a stream of said molten mass into a chamber having a protective atmosphere and a bottom portion containing a cryogenic liquid cooling medium, atomizing said stream with an inert gas to form droplets, cooling and collecting said droplets in said cooling medium to produce particles, removing said particles from said chamber and compacting said particles into a magnet body.
Claim 19
Dependent Claim
11 words
The method of claim 14 wherein said inert gas is argon.
Claim 20
Dependent Claim
20 words
The method of claim 15 wherein said molten mass of said rare-earth magnet alloy is produced by vacuum induction melting.
Claim 21
Dependent Claim
19 words
The method of claim 16 wherein said cryogenic liquid is liquid argon and said chamber has an argon atmosphere.
Claim 22
Dependent Claim
23 words
The method of claim 17 wherein said particles are comminuted to produce finer particles within the size range of 1 to 5 microns.
References Cited (Backward Citations)
US1671683A
Cited
US2384892A
Cited
US3424578A
Cited
US3560200A
Cited
US3671230A
Cited
US3646177A
Cited
US3901741A
Cited
US4152178A
Cited
US4369075A
Cited
JPS57141901A
Cited
EP0101552B1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-04-28 | 1989-10-28 | 1990-04-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-04-28 | 1993-10-28 | 1994-04-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-04-28 | 1997-10-28 | 1998-04-29 | $7700.00 | Window Closed / Lapsed |