Method of manufacturing permanent magnet alloys
Assignee: Namiki Precision Jewel Co Ltd
•
Filing: 1980-02-29
•
Granted: 1983-01-18
•
Expires: 2000-02-29
Abstract
Abstract This invention relates to a process for manufacturing R 2 Co 17 system permanent magnet alloys of rare earth(R)-cobalt(Co) intermetallic compounds. Sm 2 Co 17 alloy, in which R is samarium (Sm) with respect to intermetallic compounds whose stoichiometric composition is R 2 Co 17 , possesses high saturation magnetization and high Curie temperature making it possible to obtain a high energy product. However, its permanent magnetization has not been practiced much at all because coercive force could not be obtained. This invention practices heat aging for 0.5-200 hours at 700°-800° C. in the heat treatment process of the sintered material of R 2 (Co,Fe,M) 17 system (M is one or more than one elements of Ti, Cr, Mn, Ni, Cu, Zr, Nb, Hf, Ta, and W) and the coercive force is increased by carrying out this process in a magnetic field to achieve permanent magnetization.
Inventors
- 👤 Imaizumi Nobuo
- 👤 Aoe Masahiro
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 06:29
CPC Classifications
H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/032; H01F1/04; H01F1/047; H01F1/053; H01F1/055; H01F1/0555; H01F1/0557; C; C22; C22F; C22F1/00; C22F1/10
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
125 words
A process for manufacturing permanent magnet alloys characterized by the fact that an alloy of R(Co 1-x-y Fe x M y ) z (R is one or more than one elements of Y, Ce, Nd, Pr, Sm, Eu, and M.M.; and M consists of one or more than one elements of Ti, Cr, Mn, Ni, Cu, Zr, Nb, Hf, Ta, and W; where M.M. is misch metal; 0.02≦×≦0.5, 0.01≦y≦0.3, 8.3≦z≦9.0) is finely powdered and compression-molded in a magnetic field or without impressing a magnetic field; and the molded powder is sintered at a temperature of 1100°-1250° C. in vacuum or in an inert atmosphere; solid solution treated and, heat aged for 0.5-200 hours in the temperature range of 700°-800° C. in a further magnetic field.
Claim 2
Dependent Claim
125 words
A process for manufacturing permanent magnet alloys characterized by the fact that an alloy of R(Co 1-x-y Fe x M y ) z (R is one or more than one elements of Y, Ce, Nd, Pr, Sm, Eu, and M.M.; and M consists of one or more than one elements of Ti, Cr, Mn, Ni, Cu, Zr, Nb, Hf, Ta, and W; where M.M. is misch metal; 0.02≦×≦0.5, 0.01≦y≦0.3, 8.3≦z≦9.0) is finely powdered and compression-molded in a magnetic field or without impressing a magnetic field; and the molded powder is sintered at a temperature of 1100°-1250° C. in vacuum or in an inert atmosphere; solid solution treated and, heat aged for 0.5-200 hours in the temperature range of 700°-800° C. in a further magnetic field.
Claim 3
Dependent Claim
21 words
A process for manufacturing permanent magnet alloys as in claim 1, where said further magnetic field is more than 0.5 Koe.
Claim 4
Dependent Claim
40 words
A process for manufacturing permanent magnet alloys as in claims 1 or 2 where the direction of said further magnetic field matches the direction of orientation of the permanent magnet alloy in the case of an anisotropic permanent magnet alloy.
Claim 5
Dependent Claim
44 words
A process for manufacturing permanent magnet alloys as in claim 1 where the solution treated, molded powder is cooled to room temperature after the sintering and solid solution treatment and heat aged by reheating for 0.5-200 hours in the temperature range of 700°-800° C.
Claim 6
Dependent Claim
52 words
A process for manufacturing permanent magnet alloys as in claim 1 where the solution treated, molded powder is cooled to room temperature after heat aging by gradual cooling for 0.5-200 hours in the temperature range of 700°-800° C. during the cooling process to room temperature, after the sintering and solid solution treatment.
Claim 7
Dependent Claim
55 words
A process for manufacturing permanent magnet alloys as in claim 1 where the solution treated, molded powder is cooled to room temperature after heat aging by soaking it for 0.5-200 hours at a constant temperature in the range of 700°-800° C. during the cooling process to room temperature, after the sintering and solid solution treatment.
Claim 8
Dependent Claim
17 words
A process as in claim 1, where the finely powdered alloy has particle diameters of 0.5-5 μm.
Claim 9
Dependent Claim
16 words
A process as in claim 2 wherein said further magnetic field is at least 1 KOe.
Claim 10
Dependent Claim
41 words
A process as in claim 4 where the alloy has the composition Sm 0 .7 Y 0 .3 (Co 0 .73 Fe 0 .16 Cu 0 .08 Zr 0 .03) 8 .6, and said further magnetic field is about 5 KOe.
References Cited (Backward Citations)
US3560200A
Cited
US3982971A
Cited
US4082582A
Cited
US4116726A
Cited
US4047982A
Cited
US4135953A
Cited
US4131495A
Cited
US4210471A
Cited
US4213803A
Cited
US4221613A
Cited
US4213802A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-01-17 | 1986-07-19 | 1987-01-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-01-17 | 1990-07-19 | 1991-01-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-01-17 | 1994-07-19 | 1995-01-18 | $7700.00 | Window Closed / Lapsed |