Polymer composition of olefin/carboxylic acid copolymer and elastomer

Claim 2

A polymer composition comprising (A) 88 to 95 parts by weight of a copolymer containing olefin units and unsaturated carboxylic acid compound units and having an intrinsic viscosity [η] of 0.5 to 10 dl/g and a crystallinity of at least 20%, and (B) 12 to 5 parts by weight of a thermoplastic elastomer selected from the group consisting of polyisobutylene and polyhexene-1 having an initial modulus of not more than 100 kg/cm 2 , a glass transition temperature of not more than 0° C. and a weight average molecular weight (Mw) of at least 400,000, said elastomer being dispersed in the form of particles having an average circle equivalent diameter of 0.1 to 5 microns in a matrix of the copolymer (A).

Claim 3

The composition of claim 1 wherein the elastomer is dispersed in the form of particles having an average circle equivalent diameter of 0.3 to 4 microns.

Claim 4

The composition of claim 1 wherein the copolymer (A) has an intrinsic viscosity [η] of 0.7 to 7 dl/g and a crystallinity of at least 25%.

Claim 5

The composition of claim 1 wherein the ratio of the weight average molecular weight (Mw) of the copolymer (A) to its number average molecular weight (Mn), Mw/Mn, is from 1 to 40.

Claim 6

The composition of claim 1 wherein the copolymer (A) contains the unsaturated carboxylic acid compound units in an amount of 10 -6 to 5×10 -3 gram-equivalent, per gram of the copolymer (A).

Claim 7

The composition of claim 1 wherein the olefin units are ethylene units.

Claim 8

The composition of claim 1 wherein the unsaturated carboxylic acid compound units are units derived from acrylic acid, methacrylic acid or maleic anhydride.

Claim 9

The composition of claim 1 wherein the elastomer (B) has a glass transition temperature (Tg) of -130° to -20° C.

Claim 10

An adhesive composed of the composition of claim 1.

Claim 11

The composition of claim 1 wherein the copolymer (A) is selected from the group consisting of ethylene/acrylic acid copolymer, ethylene/methacrylic acid copolymer, ethylene/propylene/(meth)acrylic acid copolymer, ethylene/(meth)acrylic acid/vinyl acetate copolymer, ethylene/(meth)acrylic acid/(meth)acrylate copolymer, ethylene/(meth)acrylic acid/ethyl(meth)acrylate copolymer, ethylene/(meth)acrylic acid/n-butyl(meth)acrylate copolymer, ethylene/(meth)acrylate acid/isobutyl(meth)acrylate copolymer, ethylene/(meth)acrylic acid/hexyl(meth)acrylate copolymer, ethylene/methacrylic acid/2-hydroxyethyl(meth)acrylate copolymer, ethylene/(meth)-acrylic acid/carbon monoxide copolymer, ethylene/propylene/10-undecylenic acid copolymer, ethylene/maleic anhydride/methyl(meth)acrylate, ethylene/maleic anhydride/ethyl(meth)acrylate copolymer, propylene/acrylic acid copolymer, propylene/10-undecylenic acid copolymer, 1-butene/10-undecylenic acid copolymer, 4-methyl-1-pentene/10-undecylenic acid copolymer, and 3-methyl-1-pentene/10-undecylenic acid copolymer.

Claim 12

The composition of claim 4 wherein the ratio Mw/Mn is from 1 to 30.

Claim 13

The composition of claim 5 wherein the copolymer (A) contains the unsaturated carboxylic acid compound units in an amount of 5×10 -6 to 3×10 -3 gram-equivalent, per gram of the copolymer (A).

Claim 14

The composition of claim 8 wherein the elastomer (B) has an initial modulus of not more than 80 kg/cm 2 and a weight average molecular weight (Mw) of at least 500,000.

Claim 15

The composition of claim 13 wherein the elastomer (B) has a crystallinity of not more than 25%.

Claim 16

A polymer composition having adhesion to polar materials comprising (A) 88 to 95 parts by weight of a copolymer of ethylene with from 10 -6 to 5×10 -3 gram-equivalent, per gram of the copolymer (A) of an unsaturated carboxylic acid compound selected from the group consisting of acrylic acid, methacrylic acid, and maleic anhydride, said copolymer having an intrinsic viscosity [η] of 0.7 to 7 dl/g and a crystallinity of at least 25%, and (B) 12 to 5 parts by weight of a thermoplastic elastomer having an initial modulus of not more than 80 kg/cm 2 , a glass transition temperature of from -130° to -20° C. and a weight average molecular weight (Mw) of at least 500,000, said elastomer (B) being dispersed in the form of particles having an average circle equivalent diameter of 0.1 to 5 microns in a matrix of the copolymer (A).

Claim 17

A polymer composition having adhesion to polar materials comprising (A) 88 to 95 parts by weight of a copolymer of ethylene with from 10 -6 to 5×10 -3 gram-equivalent, per gram of the copolymer (A) of an unsaturated carboxylic acid compound selected from the group consisting of acrylic acid, methacrylic acid, and maleic anhydride, said copolymer having an intrinsic viscosity [η] of 0.7 to 7 dl/g and a crystallinity of at least 25%, and (B) 12 to 5 parts by weight of a thermoplastic elastomer having an initial modulus of not more than 80 kg/cm 2 , a glass transition temperature of from -130° to -20° C. and a weight average molecular weight (Mw) of at least 500,000, said elastomer (B) being dispersed in the form of particles having an average circle equivalent diameter of 0.1 to 5 microns in a matrix of the copolymer (A).

Claim 18

The composition of claim 15 wherein the thermoplastic elastomer is polyisobutylene or polyhexene-1.