Method for pouring molten metal
Assignee: Nippon Steel Corp
•
Filing: 1984-06-19
•
Granted: 1986-04-22
•
Expires: 2004-06-19
Abstract
Abstract This invention relates to a method for pouring molten metal, that is applied when molten metal is poured into a vessel or a mold from a pouring apparatus provided with a nozzle having a sliding portion adjustable of an extent of opening, such as a sliding nozzle. The extent of opening of the nozzle is changed periodically with a preset extent of opening as the center of the change. The method enables to prevent that molten metal gets into and solidifies in a gap of the sliding portion of the nozzle, and always to control a pouring amount of molten metal with a stable accuracy. Also, the sliding resistance of the sliding portion of the nozzle is detected, and the extent of opening of nozzle is changed with a vibration width corresponding to the resistance. The method enables to drop off the molten metal adhering and solidifying around the sliding portion of the nozzle, or to maintain a stable control accuracy even when the heat of molten metal causes distortion at the nozzle to change the sliding resistance.
Inventors
- 👤 Yoshii Hasegawa
- 👤 Takeshi Tsuruta
- 👤 Takao Kohgo
- 👤 Masahiro Nakamura
- 👤 Tohru Kishida
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 08:17
CPC Classifications
B; B22; B22D; B22D11/00; B22D11/16; B22D11/18; B22D11/181
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
105 words
A method for pouring molten metal into a vessel and maintaining the level of molten metal at a predetermined level comprising the steps of: providing a pouring nozzle having a sliding member to vary the extent of opening of the nozzle, periodically changing the extent of opening of the nozzle at a predetermined frequency in response to an excitation signal, measuring the level of molten metal and comparing the measured level to the predetermined level to provide a control signal, indicative of the differences between the levels, superimposing the control signal on said excitation signal to adjust the width of movement of said sliding member.
Claim 2
Independent Claim
105 words
A method for pouring molten metal into a vessel and maintaining the level of molten metal at a predetermined level comprising the steps of: providing a pouring nozzle having a sliding member to vary the extent of opening of the nozzle, periodically changing the extent of opening of the nozzle at a predetermined frequency in response to an excitation signal, measuring the level of molten metal and comparing the measured level to the predetermined level to provide a control signal, indicative of the differences between the levels, superimposing the control signal on said excitation signal to adjust the width of movement of said sliding member.
Claim 3
Dependent Claim
35 words
A method for pouring molten metal as set forth in claim 1, wherein a width of the periodical movement in the extent of opening of said nozzle is from 1 mm to 20 mm inclusive.
Claim 4
Dependent Claim
35 words
A method for pouring molten metal as set forth in claim 1, wherein the frequency of the periodical movement in the extent of opening of said nozzle is from 0.2 Hz to 1.2 Hz inclusive.
Claim 5
Dependent Claim
35 words
A method for pouring molten metal as set forth in claim 2, wherein the frequency of the periodical movement in the extent of opening of said nozzle is from 0.2 Hz to 1.2 Hz inclusive.
Claim 6
Independent Claim
131 words
A method for pouring molten metal into a vessel and maintaining the level of the molten metal in the vessel at an optimum level comprising the steps of: providing a pouring nozzle having a sliding member to vary the extent of opening of the nozzle, periodically changing the extent of opening of the nozzle at a predetermined frequency in response to an excitation signal, measuring the level of molten metal and comparing the measured level to the predetermined level to provide a control signal, indicative of the differences between the levels, measuring the sliding resistance of the sliding member, making the amplitude of said control signal larger when the sliding resistance becomes larger, superimposing the control signal on said excitation signal to adjust the width of movement of said sliding member.
Claim 7
Independent Claim
131 words
A method for pouring molten metal into a vessel and maintaining the level of the molten metal in the vessel at an optimum level comprising the steps of: providing a pouring nozzle having a sliding member to vary the extent of opening of the nozzle, periodically changing the extent of opening of the nozzle at a predetermined frequency in response to an excitation signal, measuring the level of molten metal and comparing the measured level to the predetermined level to provide a control signal, indicative of the differences between the levels, measuring the sliding resistance of the sliding member, making the amplitude of said control signal larger when the sliding resistance becomes larger, superimposing the control signal on said excitation signal to adjust the width of movement of said sliding member.
Claim 8
Independent Claim
114 words
A method for pouring molten metal into a vessel and maintaining the level of molten metal at a predetermined level comprising the steps of: providing a pouring nozzle having a sliding portion to vary the extent of opening of the nozzle, periodically changing the extent of opening of the nozzle, measuring the level of molten metal and comparing the measured level to the predetermined level to provide a control signal, indicative of the differences between the levels, making the amplitude of said excitation signal larger when said difference of the level of molten metal becomes larger, superimposing the control signal on said excitation signal to adjust the width of movement of said sliding member.
Claim 9
Independent Claim
114 words
A method for pouring molten metal into a vessel and maintaining the level of molten metal at a predetermined level comprising the steps of: providing a pouring nozzle having a sliding portion to vary the extent of opening of the nozzle, periodically changing the extent of opening of the nozzle, measuring the level of molten metal and comparing the measured level to the predetermined level to provide a control signal, indicative of the differences between the levels, making the amplitude of said excitation signal larger when said difference of the level of molten metal becomes larger, superimposing the control signal on said excitation signal to adjust the width of movement of said sliding member.
Claim 10
Dependent Claim
35 words
A method of pouring molten metal as set forth in claim 5, wherein a width of the periodical change in the extent of opening of said nozzle is from 1 mm to 20 mm inclusive.
Claim 11
Dependent Claim
35 words
A method of pouring molten metal as set forth in claim 5, wherein the frequency of the periodical change in the extent of opening of said nozzle is from 0.2 Hz to 1.2 Hz inclusive.
Claim 12
Dependent Claim
35 words
A method of pouring molten metal as set forth in claim 7, wherein the frequency of the periodical change in the extent of opening of said nozzle is from 0.2 Hz to 1.2 Hz inclusive.
Claim 13
Dependent Claim
35 words
A method of pouring molten metal as set forth in claim 6, wherein a width of the periodical change in the extent of opening of said nozzle is from 1 mm to 2 mm inclusive.
Claim 14
Dependent Claim
35 words
A method of pouring molten metal as set forth in claim 6, wherein the frequency of the periodical change in the extent of opening of said nozzle is from 0.2 Hz to 1.2 Hz inclusive.
Claim 15
Dependent Claim
35 words
A method of pouring molten metal as set forth in claim 10, wherein the frequency of the periodical change in the extent of opening of said nozzle is from 0.2 Hz to 1.2 Hz inclusive.
References Cited (Backward Citations)
US4077457A
Cited
US4019562A
Cited
US3990614A
Cited
GB2001154A
Cited
US4355787A
Cited
JPS574369A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-04-21 | 1989-10-21 | 1990-04-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-04-21 | 1993-10-21 | 1994-04-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-04-21 | 1997-10-21 | 1998-04-22 | $7700.00 | Window Closed / Lapsed |