Production of improved pellets from melt-processable polymer which is capable of forming and anisotropic melt
Assignee: Celanese Corp
•
Filing: 1984-10-09
•
Granted: 1986-04-08
•
Expires: 2004-10-09
Abstract
Abstract Improved pellets comprising a melt-processable thermotropic liquid crystalline polymer (e.g., a wholly aromatic polyester) are provided. The molten anisotropic melt-forming polymer, while present as a thin film of the specified thickness at an appropriate temperature, is subjected to reduced pressure conditions whereby residual volatiles are evolved and removed, and the polymer thereby is densified to the specified degree prior to pellet formation. The resulting densified polymer next is melt-extruded and is cut to form pellets while at an appropriate temperature. It surprisingly has been found to be of prime importance that the resulting pellets possess a density of at least 95 percent of the theoretical maximum (e.g., a polymer density of approximately 1.35 to 1.4 gram/cc.) if the advantages of the present invention are to be fully realized. These pellets have been found to be capable of undergoing melt processing to form shaped articles having improved physical properties. For instance, such shaped articles exhibit markedly smoother surface characteristics and can be used at elevated temperatures for extended periods of time while better retaining the desired surface characteristics.
Inventors
- 👤 Sunil K. Garg
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 23:31
CPC Classifications
B; B29; B29B; B29B9/00; B29B9/02; B29B9/06; B29K; B29K2067/00; B29K2069/00; B29K2077/00
Claims Analysis
Total Claims: 44
Claim 1
Independent Claim
178 words
An improved process for producing pellets from a melt-processable thermotropic polymer which is capable of forming an anisotropic melt phase, which pellets are capable of undergoing melt-processing to form shaped articles having improved physical properties when compared to shaped articles prepared from conventionally prepared pellets which lack the densification treatment of the present invention, comprising: (a) subjecting said melt-processable polymer which is capable of forming an anisotropic melt phase while in the molten state at a temperature below the threshold temperature for further polymerization and present as a thin film in a thickness of no more than approximately 10 mm. to reduced pressure conditions of approximately 0 to 100 mm. of mercury whereby residual volatiles present therein are substantially evolved and removed from said molten polymer whereby said polymer is densified, (b) extruding said resulting densified polymer while molten and at a temperature below its threshold temperature for further polymerization into a quench zone, and (c) cutting the extrudate to form improved solid pellets therefrom having a pellet density of at least 95 percent of the theoretical maximum.
Claim 2
Dependent Claim
178 words
An improved process for producing pellets from a melt-processable thermotropic polymer which is capable of forming an anisotropic melt phase, which pellets are capable of undergoing melt-processing to form shaped articles having improved physical properties when compared to shaped articles prepared from conventionally prepared pellets which lack the densification treatment of the present invention, comprising: (a) subjecting said melt-processable polymer which is capable of forming an anisotropic melt phase while in the molten state at a temperature below the threshold temperature for further polymerization and present as a thin film in a thickness of no more than approximately 10 mm. to reduced pressure conditions of approximately 0 to 100 mm. of mercury whereby residual volatiles present therein are substantially evolved and removed from said molten polymer whereby said polymer is densified, (b) extruding said resulting densified polymer while molten and at a temperature below its threshold temperature for further polymerization into a quench zone, and (c) cutting the extrudate to form improved solid pellets therefrom having a pellet density of at least 95 percent of the theoretical maximum.
Claim 3
Dependent Claim
49 words
An improved process for producing pellets according to claim 1 wherein said melt-processable thermotropic polymer which is capable of forming an anisotropic melt phase is selected from the group consisting of wholly aromatic polyesters, aromatic-aliphatic polyesters, wholly aromatic poly(ester-amides), aromatic-aliphatic poly(ester-amides), aromatic polyester carbonates, and mixtures of the foregoing.
Claim 4
Dependent Claim
40 words
An improved process for producing pellets according to claim 1 wherein said melt-processable thermotropic polymer which is capable of forming an anisotropic melt phase is wholly aromatic in the sense that each moiety present contributes at least one aromatic ring.
Claim 5
Dependent Claim
29 words
An improved process for producing pellets according to claim 1 wherein said melt-processable thermotropic polymer which is capable of forming an anisotropic melt phase is a wholly aromatic polyester.
Claim 6
Dependent Claim
29 words
An improved process for producing pellets according to claim 1 wherein said melt-processable thermotropic polymer which is capable of forming an anisotropic melt phase is a wholly aromatic poly(ester-amide).
Claim 7
Dependent Claim
40 words
An improved process for producing pellets according to claim 1 wherein said melt-processable thermotropic polymer which is capable of forming an anisotropic melt phase includes not less than about 10 mole percent of recurring units which include a naphthalene moiety.
Claim 8
Dependent Claim
57 words
An improved process for producing pellets according to claim 1 wherein said melt-processable thermotropic polymer which is capable of forming an anisotropic melt phase includes not less than about 10 mole percent of recurring units which include a naphthalene moiety selected from the group consisting of 6-oxy-2-naphthoyl moiety, 2,6-dioxynaphthalene moiety, 2,6-dicarboxynaphthalene moiety, and mixtures of the foregoing.
Claim 9
Dependent Claim
49 words
An improved process for producing pellets according to claim 1 wherein said melt-processable thermotropic polymer which is capable of forming an anisotropic melt phase exhibits an inherent viscosity of approximately 0.8 to 15.0 dl./gm. when dissolved in a concentration of 0.1 percent by weight in pentafluorophenol at 60° C.
Claim 10
Dependent Claim
62 words
An improved process for producing pellets according to claim 1 wherein said melt-processable thermotropic polymer which is capable of forming an anisotropic melt phase is a wholly aromatic polyester which consists essentially of moieties I and II wherein: ##STR6## wherein said polyester comprises approximately 10 to 90 mole percent of moiety I, and approximately 10 of 90 mole percent of moiety II.
Claim 11
Dependent Claim
136 words
An improved process for producing pellets according to claim 1 wherein said melt-processable thermotropic polymer which is capable of forming an anisotropic melt phase is a wholly aromatic poly(ester-amide) which consists essentially of moieties I, II, III, and optionally IV, wherein in each instance Ar comprises at least one aromatic ring, and wherein: I is ##STR7## II is ##STR8## III is --Y--Ar--Z-- where Y is 0, NH, or NR, and Z is NH or NR where R is an alkyl group of 1 to 6 carbon atoms or an aryl group, and IV is --O--Ar--O-- wherein said poly(ester-amide) comprises approximately 10 to 90 mole percent of moiety I, approximately 5 to 45 mole percent of moiety II, approximately 5 to 45 mole percent of moiety III, and approximately 0 to 40 mole percent of moiety IV.
Claim 12
Dependent Claim
29 words
An improved process for producing pellets according to claim 1 wherein said melt-processable thermotropic polymer which is capable of forming an anisotropic melt phase was formed via an acidolysis-polymerization.
Claim 13
Dependent Claim
30 words
An improved process for producing pellets according to claim 1 wherein said melt-processable thermotropic polymer which is capable of forming an anisotropic melt phase was formed via a melt-polymerization technique.
Claim 14
Dependent Claim
30 words
An improved process for producing pellets according to claim 1 wherein said melt-processable thermotropic polymer which is capable of forming a anisotropic melt phase was formed via a slurry-polymerization technique.
Claim 15
Dependent Claim
24 words
An improved process for producing pellets according to claim 1 wherein said thin film thickness in step (a) is approximately 1 to 5 mm.
Claim 16
Dependent Claim
34 words
An improved process for producing pellets according to claim 1 wherein said reduced pressure conditions produce a partial vacuum on the surface of said thin film of approximately 0 to 60 mm. of mercury.
Claim 17
Dependent Claim
22 words
An improved process for producing pellets according to claim 1 wherein said step (a) is carried out in a thin film extruder.
Claim 18
Dependent Claim
23 words
An improved process for producing pellets according to claim 1 wherein said step (a) is carried out in a disk pack apparatus .
Claim 19
Dependent Claim
40 words
An improved process for producing pellets according to claim 1 wherein said melt-processable thermotropic polymer is provided in steps (a) and (b) at a temperature in the range of approximately 280° to 325° C. prior to quenching in step (b).
Claim 20
Dependent Claim
36 words
An improved process for producing pellets according to claim 1 wherein during said step (b) said extruded densified polymer is subjected to a drawdown of about 1:1 to 3:1 prior to solidification in said quench zone.
Claim 21
Dependent Claim
20 words
An improved process for producing pellets according to claim 1 wherein said resulting pellets possess a substantially cylindrical cross-sectional configuration.
Claim 22
Dependent Claim
25 words
An improved process for producing pellets according to claim 1 wherein the polymer density of said resulting improved solid pellets is at least 1.35 gram/cc.
Claim 23
Dependent Claim
26 words
An improved process for producing pellets according to claim 1 wherein the polymer density of said resulting improved solid pellets is approximately 1.35 to 1.4 gram/cc.
Claim 24
Dependent Claim
25 words
An improved process for producing improved solid pellets according to claim 1 wherein the polymer density of said resulting pellets is at least 1.39 gram/cc.
Claim 25
Dependent Claim
26 words
An improved process for producing pellets according to claim 1 wherein the polymer density of said resulting improved solid pellets is approximately 1.39 to 1.40 gram/cc.
Claim 26
Dependent Claim
36 words
An improved process for producing pellets according to claim 1 wherein the resulting pellets additionally include a solid particulate filler and/or reinforcing agent incorporated therein in a concentration of up to approximately 60 percent by weight.
Claim 27
Dependent Claim
78 words
An improved pellet comprising a melt-processable thermotropic polymer which is capable of forming an anisotropic melt phase and which pellet is capable of undergoing melt-processing to form shaped articles having improved physical properties when compared to shaped articles prepared from conventionally prepared pellets of lesser density, wherein said pellet has a width of approximately 0.0625 to 0.25 inch, a length of approximately 0.0625 to 0.25 inch, and a pellet density of at least 95 percent of theoretical maximum.
Claim 28
Dependent Claim
78 words
An improved pellet comprising a melt-processable thermotropic polymer which is capable of forming an anisotropic melt phase and which pellet is capable of undergoing melt-processing to form shaped articles having improved physical properties when compared to shaped articles prepared from conventionally prepared pellets of lesser density, wherein said pellet has a width of approximately 0.0625 to 0.25 inch, a length of approximately 0.0625 to 0.25 inch, and a pellet density of at least 95 percent of theoretical maximum.
Claim 29
Dependent Claim
46 words
An improved pellet according to claim 26 wherein said melt-processable thermotropic polymer which is capable of forming an anisotropic melt phase is selected from the group consisting of wholly aromatic polyesters, aromatic-aliphatic polyesters, wholly aromatic poly(ester-amides), aromatic-aliphatic poly(ester-amides), aromatic polyester carbonates, and mixtures of the foregoing.
Claim 30
Dependent Claim
37 words
An improved pellet according to claim 26 wherein said melt-processable thermotropic polymer which is capable of forming an anisotropic melt phase is wholly aromatic in the sense that each moiety present contributes at least one aromatic ring.
Claim 31
Dependent Claim
26 words
An improved pellet according to claim 26 wherein said melt-processable thermotropic polymer which is capable of forming an anisotropic melt phase is a wholly aromatic polyester.
Claim 32
Dependent Claim
26 words
An improved pellet according to claim 26 wherein said melt-processable thermotropic polymer which is capable of forming an anisotropic melt phase is a wholly aromatic poly(ester-amide).
Claim 33
Dependent Claim
37 words
An improved pellet according to claim 26 wherein said melt-processable thermotropic polymer which is capable of forming an anisotropic melt phase includes not less than about 10 mole percent of recurring units which include a naphthalene moiety.
Claim 34
Dependent Claim
54 words
An improved pellet according to claim 26 wherein said melt-processable thermotropic polymer which is capable of forming an anisotropic melt phase includes not less than about 10 mole percent of recurring units which include a naphthalene moiety selected from the group consisting of 6-oxy-2-naphthoyl moiety, 2,6-dioxynaphthalene moiety, 2,6-dicarboxynaphthalene moiety, and mixtures of the foregoing.
Claim 35
Dependent Claim
46 words
An improved pellet according to claim 26 wherein said melt-processable thermotropic polymer which is capable of forming an anisotropic melt phase exhibits an inherent viscosity of approximately 0.8 to 15.0 dl./gm. when dissolved in a concentration of 0.1 percent by weight in pentafluorophenol at 60° C.
Claim 36
Dependent Claim
59 words
An improved pellet according to claim 26 wherein said melt-processable thermotropic polymer which is capable of forming an anisotropic melt phase is a wholly aromatic polyester which consists essentially of moieties I and II wherein: ##STR9## wherein said polyester comprises approximately 10 to 90 mole percent of moiety I, and approximately 10 of 90 mole percent of moiety II.
Claim 37
Dependent Claim
133 words
An improved pellet according to claim 26 wherein said melt-processable thermotropic polymer which is capable of forming an anisotropic melt phase is a wholly aromatic poly(ester-amide) which consists essentially of moieties I, II, III, and optionally IV, wherein in each instance Ar comprises at least one aromatic ring, and wherein I is ##STR10## II is ##STR11## III is --Y--Ar--Z-- where Y is 0, NH, or NR, and Z is NH or NR where R is an alkyl group of 1 to 6 carbon atoms or an aryl group, and IV is --O--Ar--O-- wherein said poly(ester-amide) comprises approximately 10 to 90 mole percent of moiety I, approximately 5 to 45 mole percent of moiety II, approximately 5 to 45 mole percent of moiety III, and approximately 0 to 40 mole percent of moiety IV.
Claim 38
Dependent Claim
16 words
An improved pellet according to claim 26 wherein said pellet possesses a substantially cylindrical cross-sectional configuration.
Claim 39
Dependent Claim
29 words
An improved pellet according to claim 26 wherein said pellet possesses a substantially cylindrical cross-sectional configuration and is approximately 0.125 inch in diameter and approximately 0.125 inch in length.
Claim 40
Dependent Claim
16 words
An improved pellet according to claim 26 wherein the polymer density is at least 1.35 gram/cc.
Claim 41
Dependent Claim
17 words
An improved pellet according to claim 26 wherein the polymer density is approximately 1.35 to 1.4 gram/cc.
Claim 42
Dependent Claim
16 words
An improved pellet according to claim 26 wherein the polymer density is at least 1.39 gram/cc.
Claim 43
Dependent Claim
17 words
An improved pellet according to claim 26 wherein the polymer density is approximately 1.39 to 1.4 gram/cc.
Claim 44
Dependent Claim
30 words
An improved pellet according to claim 26 which additionally includes a solid particulate filler and/or reinforcing agent incorporated therein in a concentration of up to approximately 60 percent by weight.
References Cited (Backward Citations)
GB998063A
Cited
US3577360A
Cited
JPS503350A
Cited
US4161470A
Cited
US4447599A
Cited
US4418030A
Cited
US4474938A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-04-07 | 1989-10-07 | 1990-04-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-04-07 | 1993-10-07 | 1994-04-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-04-07 | 1997-10-07 | 1998-04-08 | $7700.00 | Window Closed / Lapsed |