Abstract
Abstract A refractory material consists of a zircon matrix with zirconia particles dispersed in it. The zirconia particles comprise from 5 to 30 percent (by weight) of the material. A method of making this material involves milling zircon sand particles and zirconia particles until they have a respective predetermined particle size distribution, adding a fugitive binder, moulding a green ware, firing the green ware at a temperature in the range from 1400° C. to 1800° C., and furnace cooling the fired ware. Preferably the ware is held at the firing temperature for one hour.
Inventors
- 👤 Ronald C. Garvie
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 22:08
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/48; C04B35/481
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
232 words
A method of making a refractory ceramic material having a porosity of about 10% consisting essentially of a matrix of zircon containing from 5 to 30 wt percent of zirconia, said method comprising the steps of: (a) milling a zircon sand having a purity of at least 97 percent until the milled zircon sand has a means particle diameter in the range from about 0.5 micrometer to about 20 micrometers; (b) milling zirconia particles having a purity of at least 97 percent until the milled particles have a mean particle diameter in the range from about 2.4 micrometers to about 95 micrometers; (c) forming an admixture of the milled zircon sand and the milled zirconia particles, said admixture containing from about 5 wt percent to about 30 wt percent of zirconia; (d) adding a fugitive binder to said admixture and mixing until the fugitive binder and zirconia particles are uniformly distributed in the admixture; (e) moulding the product admixture of step (d) into a desired shape to form a green ware; (f) heating the green ware to a firing temperature in the range from about 1400° C. to about 1800° C. at a rate of heating which ensures that the ware does not crack; (g) holding the firing temperature for a period in the range of 1 to 5 hours; and (h) allowing the fired ware to furnace cool to ambient temperature.
Claim 2
Independent Claim
232 words
A method of making a refractory ceramic material having a porosity of about 10% consisting essentially of a matrix of zircon containing from 5 to 30 wt percent of zirconia, said method comprising the steps of: (a) milling a zircon sand having a purity of at least 97 percent until the milled zircon sand has a means particle diameter in the range from about 0.5 micrometer to about 20 micrometers; (b) milling zirconia particles having a purity of at least 97 percent until the milled particles have a mean particle diameter in the range from about 2.4 micrometers to about 95 micrometers; (c) forming an admixture of the milled zircon sand and the milled zirconia particles, said admixture containing from about 5 wt percent to about 30 wt percent of zirconia; (d) adding a fugitive binder to said admixture and mixing until the fugitive binder and zirconia particles are uniformly distributed in the admixture; (e) moulding the product admixture of step (d) into a desired shape to form a green ware; (f) heating the green ware to a firing temperature in the range from about 1400° C. to about 1800° C. at a rate of heating which ensures that the ware does not crack; (g) holding the firing temperature for a period in the range of 1 to 5 hours; and (h) allowing the fired ware to furnace cool to ambient temperature.
Claim 3
Independent Claim
242 words
A method of making a refractory ceramic material having a porosity of about 10% consisting essentially of a matrix of zircon containing from 5 to 30 wt percent of zirconia, said method comprising the steps of (a) milling a zircon sand having a purity of at least 97 percent until the milled zircon sand has a mean particle diameter in the range from about 0.5 micrometer to about 20 micrometers; (b) adding zirconia particles having a purity of at least 97 percent to the zircon sand during the course of the milling thereof, to form an admixture of zircon sand and zirconia, and milling the admixture until the zircon sand particles have the said mean particle diameter and the zirconia particles have a mean particle diameter in the range from about 2.4 micrometers to about 95 micrometers; (c) adding a fugitive binder to the milled admixture of zircon sand and zirconia particles, and mixing until the fugitive binder is uniformly distributed in the admixture; (d) moulding the product admixture of step (c) into a desired shape to form a green ware; (e) heating the green ware to a firing temperature in the range from about 1400° C. to about 1800° C. at a rate of heating which ensures that the ware does not crack; (f) holding the firing temperature for a period in the range of 1 to 5 hours; and (g) allowing the fired ware to furnace cool to ambient temperature.
Claim 4
Independent Claim
242 words
A method of making a refractory ceramic material having a porosity of about 10% consisting essentially of a matrix of zircon containing from 5 to 30 wt percent of zirconia, said method comprising the steps of (a) milling a zircon sand having a purity of at least 97 percent until the milled zircon sand has a mean particle diameter in the range from about 0.5 micrometer to about 20 micrometers; (b) adding zirconia particles having a purity of at least 97 percent to the zircon sand during the course of the milling thereof, to form an admixture of zircon sand and zirconia, and milling the admixture until the zircon sand particles have the said mean particle diameter and the zirconia particles have a mean particle diameter in the range from about 2.4 micrometers to about 95 micrometers; (c) adding a fugitive binder to the milled admixture of zircon sand and zirconia particles, and mixing until the fugitive binder is uniformly distributed in the admixture; (d) moulding the product admixture of step (c) into a desired shape to form a green ware; (e) heating the green ware to a firing temperature in the range from about 1400° C. to about 1800° C. at a rate of heating which ensures that the ware does not crack; (f) holding the firing temperature for a period in the range of 1 to 5 hours; and (g) allowing the fired ware to furnace cool to ambient temperature.
Claim 5
Dependent Claim
16 words
A method as defined in claim 1, in which the firing temperature is about 1600° C.
Claim 6
Dependent Claim
16 words
A method as defined in claim 2, in which the firing temperature is about 1600° C.
Claim 7
Dependent Claim
75 words
A method as defined in claim 2, in which (a) the milled zircon sand has a mean particle diameter in the range from about 2 micrometers to about 7 micrometers, and at least 95 percent of particles in the milled zircon sand have a diameter of less than 5 micrometers; and (b) the milled zirconia particles all have a diameter less than about 27 micrometers, with the mean zirconia particle diameter being about 13 micrometers.
Claim 8
Dependent Claim
75 words
A method as defined in claim 1, in which (a) the milled zircon sand has a mean particle diameter in the range from about 2 micrometers to about 7 micrometers, and at least 95 percent of particles in the milled zircon sand have a diameter of less than 5 micrometers; and (b) the milled zirconia particles all have a diameter less than about 27 micrometers, with the mean zirconia particle diameter being about 13 micrometers.
Claim 9
Dependent Claim
24 words
A method as defined in claim 1, in which the zirconia concentration consists essentially of about 10 wt per cent of the zircon matrix.
Claim 10
Dependent Claim
19 words
A method as defined in claim 2, in which the zirconia concentration consists essentially of about 10 wt percent.
Claim 11
Dependent Claim
19 words
A method as defined in claim 5, in which the zirconia concentration consists essentially of about 10 wt percent.
Claim 12
Dependent Claim
84 words
A method as defined in claim 2, in which (a) the zircon sand particles in the milled zircon sand and zirconia admixture have a mean particle diameter in the range from about 2 micrometers to about 7 micrometers, and at least 95 percent thereof have a diameter of less than 5 micrometers; and (b) the zirconia particles in the milled zircon sand and zirconia admixture all have a diameter less than about 27 micrometers, and the mean particle diameter thereof is about 13 micrometers.
Claim 13
Dependent Claim
84 words
A method as defined in claim 4, in which (a) the zircon sand particles in the milled zircon sand and zirconia admixture have a means particle diameter in the range from about 2 micrometers to about 7 micrometers, and at least 95 percent thereof have a diameter of less than 5 micrometers; and (b) the zirconia particles in the milled zircon sand and zirconia admixture all have a diameter less than about 27 micrometers, and the mean particle diameter thereof is about 13 micrometers.
Claim 14
Dependent Claim
23 words
A method as defined in claim 2, in which the zirconia concentration consists essentially of about 10 wt percent of the zircon matrix.
Claim 15
Dependent Claim
19 words
A method as defined in claim 4, in which the zirconia concentration consists essentially of about 10 wt percent.
Claim 16
Dependent Claim
19 words
A method as defined in claim 7, in which the zirconia concentration consists essentially of about 10 wt percent.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-03-31 | 1989-09-30 | 1990-04-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-03-31 | 1993-09-30 | 1994-04-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-03-31 | 1997-09-30 | 1998-04-01 | $7700.00 | Window Closed / Lapsed |