Method of forming a polarization preserving optical waveguide

Claim 3

A method in accordance with claim 1 wherein the step of forming a glass preform comprises depositing on a substantially cylindrical mandrel a coating of core glass particles, depositing on said coating of core glass particles, a coating of inner cladding glass particles, and heating the resultant porous preform to form a dense glass preform.

Claim 4

A method in accordance with claim 2 wherein, after the step of removing diametrically opposed regions, the resultant article is heated and elongated to form said preform foreproduct.

Claim 5

A method in accordance with claim 1 wherein the step of forming a glass preform comprises depositing on a substantially cylindrical mandrel a coating of core glass particles, depositing on the surface of said core glass particles a coating of inner cladding glass particles, removing said mandrel to form a hollow porous preform, heating said porous preform to a temperature within the consolidation temperature range to form a consolidated dense glass preform having an aperture therethrough, closing both ends of said aperture, said step of removing diametrically opposed regions of said inner cladding glass being performed after said aperture ends have been closed, said method further comprising the steps of severing an end of said dense glass preform to expose said aperture, evacuating said aperture, heating the resultant article and stretching it to cause said aperture to close and to form an intermediate fiber, and severing a suitable long section of said intermediate fiber.

Claim 6

A method in accordance with claim 4 wherein the step of removing diametrically opposed regions comprises sawing diametrically opposed regions from said dense glass preform, and grinding the flattened surfaces formed by removing said diametrically opposed regions to smooth roughness caused by said sawing step and to round any sharp corners formed by said sawing step.

Claim 7

A method in accordance with claim 1 wherein prior to the step of depositing said layer of outer cladding glass particles, the method comprises the step of depositing a layer of glass particles having the same composition as said inner cladding glass on said inner cladding glass.

Claim 8

A method in accordance with claim 1 wherein said inner cladding glass consists of SiO 2 and wherein prior to the step of depositing said layer of outer cladding glass particles, the method comprises the step of depositing a layer of SiO 2 particles on said inner cladding glass.

Claim 9

A method in acordance with claim 5 wherein prior to the step of depositing said layer of outer cladding glass particles, said method comprises the step of etching the surface of said inner cladding layer to remove a thin layer from the surface thereof.

Claim 10

A method in accordance with claim 4 wherein, after the step of removing, said method comprises grinding the surface of said inner cladding glass to round any sharp corners theron to form a preform foreproduct having an oblong cross-section.

Claim 11

In a method of forming a single-mode optical fiber having polarization-retaining characteristics comprising the steps of depositing on a substantially cylindrical mandrel a coating of core glass particles, depositing on the surface of said core glass particles a coating of inner cladding glass particles, removing said mandrel to form a hollow porous preform having a circular outer surface, heating said porous preform to a temperature within the consolidation temperature range to form a consolidated dense glass preform having an aperture therethrough, closing both ends of said aperture, removing diametrically opposed regions of said inner cladding glass to form a preform foreproduct having two rounded sides and two flattened sides, grinding the flattened surfaces formed by removing said diametrically opposed regions to smooth the surface of said foreproduct and to round any sharp corners thereon to form a preform foreproduct having an oblong cross-section, depositing on said oblong foreproduct a layer of glass particles having the same composition as said inner cladding glass and then, depositing on the surface of the resultant article a layer of glass particles having a thermal coefficient of expansion which differs from that of the inner cladding layer by at least 1×10 -7 /C.° which forms a circular outer stress cladding, heating the resultant article to consolidate said layer of glass particles, thereby forming a solid glass draw blank, and drawing said solid glass draw blank to form a single-mode optical fiber comprising a circular core, on oblong layer of inner cladding glass and a circular outer stress cladding, said inner cladding layer having a high aspect ratio and a thin minimum thickness on opposite sides of said core whereby said optical fiber exhibits stress-induced birefringence sufficient to form polarization, wherein the step of depositing on said oblong foreproduct substantially preventing the formation of seeds at the interface between the inner and outer cladding of said optical fiber.

Claim 12

In a method of forming a single-mode optical fiber having polarization-retaining characteristics comprising the steps of depositing on a substantially cylindrical mandrel a coating of core glass particles, depositing on the surface of said core glass particles a coating of inner cladding glass particles, removing said mandrel to form a hollow porous preform having a circular outer surface, heating said porous preform to a temperature within the consolidation temperature range to form a consolidated dense glass preform having an aperture therethrough, closing both ends of said aperture, removing diametrically opposed regions of said inner cladding glass to form a preform foreproduct having two rounded sides and two flattened sides, grinding the flattened surfaces formed by removing said diametrically opposed regions to smooth the surface of said foreproduct and to round any sharp corners thereon to form a preform foreproduct having an oblong cross-section, depositing on said oblong foreproduct a layer of glass particles having the same composition as said inner cladding glass and then, depositing on the surface of the resultant article a layer of glass particles having a thermal coefficient of expansion which differs from that of the inner cladding layer by at least 1×10 -7 /C.° which forms a circular outer stress cladding, heating the resultant article to consolidate said layer of glass particles, thereby forming a solid glass draw blank, and drawing said solid glass draw blank to form a single-mode optical fiber comprising a circular core, on oblong layer of inner cladding glass and a circular outer stress cladding, said inner cladding layer having a high aspect ratio and a thin minimum thickness on opposite sides of said core whereby said optical fiber exhibits stress-induced birefringence sufficient to form polarization, wherein the step of depositing on said oblong foreproduct substantially preventing the formation of seeds at the interface between the inner and outer cladding of said optical fiber.

Claim 13

A method in accordance with claim 10 wherein said inner cladding glass is SiO 2 and wherein the step of depositing a layer of glass particles having the same composition as said inner cladding glass comprises depositing SiO 2 particles.

Claim 14

A method in accordance with claim 11 wherein, prior to the step of depositing on said foreproduct a layer of glass particles, said method comprises the step of etching the surface of said inner cladding layer to remove a thin layer from the surface thereof.