Hydrocracking process and catalyst therefor
Assignee: Honeywell UOP LLC
•
Filing: 1985-02-01
•
Granted: 1986-03-18
•
Expires: 2005-02-01
Abstract
Abstract A hydrocracking process, of especial use in the production of a relatively high yield of middle distillate products along with a smaller but still significant yield of gasoline from high boiling gas oils and the like, comprises contacting a gas oil or other hydrocarbon feedstock under hydrocracking conditions with a novel catalyst comprising one or more hydrogenation components on a support material comprising, in combination, a dispersion of silica-alumina in alumina and a zeolite of the Y crystalline structure but having a silica-to-alumina ratio above about 6.0.
Inventors
- 👤 John W. Ward
- 👤 Timothy L. Carlson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 10:41
CPC Classifications
C; C10; C10G; C10G47/00; C10G47/02; C10G47/10; C10G47/12; C10G47/16; C10G47/20; B; B01; B01J; B01J29/00; B01J29/04; B01J29/06; B01J29/08; B01J29/084; B01J29/10; B01J29/106; B01J29/16; B01J29/166
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
71 words
In a catalytic hydrocracking process, the improvement comprising contacting a hydrocarbon feedstock with a hydrocracking catalyst under hydrocracking conditions producing a product hydrocarbon of lower average molecular weight than said feedstock with a catalyst comprising an active hydrogenation metal component on a support comprising in admixture a dispersion of silica-alumina in alumina and a crystalline aluminosilicate zeolite having the zeolite Y crystal structure and a silica-to-alumina mole ratio above about 6.0.
Claim 2
Dependent Claim
71 words
In a catalytic hydrocracking process, the improvement comprising contacting a hydrocarbon feedstock with a hydrocracking catalyst under hydrocracking conditions producing a product hydrocarbon of lower average molecular weight than said feedstock with a catalyst comprising an active hydrogenation metal component on a support comprising in admixture a dispersion of silica-alumina in alumina and a crystalline aluminosilicate zeolite having the zeolite Y crystal structure and a silica-to-alumina mole ratio above about 6.0.
Claim 3
Dependent Claim
91 words
In a catalytic hydrocracking process, the improvement comprising contacting a hydrocarbon feedstock with a hydrocracking catalyst under hydrocracking conditions producing a product hydrocarbon of lower average molecular weight than said feedstock with a catalyst comprising a Group VIB or Group VIII active metal component on a support comprising in admixture a dispersion of silica-alumina in alumina and a crystalline aluminosilicate zeolite having catalytic cracking activity, a silica-to-alumina mole ratio above about 6.0, and an X-ray diffraction pattern consistent with a Y zeolite of unit cell size of 24.75 angstroms or less.
Claim 4
Dependent Claim
91 words
In a catalytic hydrocracking process, the improvement comprising contacting a hydrocarbon feedstock with a hydrocracking catalyst under hydrocracking conditions producing a product hydrocarbon of lower average molecular weight than said feedstock with a catalyst comprising a Group VIB or Group VIII active metal component on a support comprising in admixture a dispersion of silica-alumina in alumina and a crystalline aluminosilicate zeolite having catalytic cracking activity, a silica-to-alumina mole ratio above about 6.0, and an X-ray diffraction pattern consistent with a Y zeolite of unit cell size of 24.75 angstroms or less.
Claim 5
Dependent Claim
23 words
A process as defined in claim 1 or 2 wherein the alkali metal content of said zeolite is less than 0.5 weight percent.
Claim 6
Dependent Claim
17 words
A process as defined in claim 3 wherein said silica-to-alumina mole ratio is between 8.5 and 15.
Claim 7
Dependent Claim
23 words
A process as defined in claim 1 or 2 wherein the silica-to-alumina mole ratio of said zeolite is between about 8.5 and 15.
Claim 8
Dependent Claim
46 words
A process as defined in claim 2 wherein said catalyst comprises a Group VIII metal component selected from the group consisting of nickel, cobalt, and the compounds thereof, and a Group VIB metal component selected from the group consisting of molybdenum, tungsten, and the compounds thereof.
Claim 9
Dependent Claim
63 words
A process as defined in claim 1, 2, or 6 wherein said feedstock is converted to a product hydrocarbon containing hydrocarbons boiling in the C 4 to 700° F. range, of which hydrocarbons at least 50 volume percent boil in the 300° to 700° F. middle distillate range and at least 15 volume percent boil in the 185° to 300° F. gasoline range.
Claim 10
Dependent Claim
43 words
A process as defined in claim 7 wherein at least about 50% of the components in said hydrocarbon feedstock boil above 700° F., and of said components, at least 90% by volume are converted during said contacting to products boiling below 700° F.
Claim 11
Dependent Claim
18 words
A process as defined in claim 8 wherein said zeolite has a silica-to-alumina mole ratio above about 8.5.
Claim 12
Dependent Claim
21 words
A process as defined in claim 9 wherein said zeolite comprises betweeh about 30% and 45% by weight of said support.
Claim 13
Dependent Claim
45 words
A process as defined in claim 7 wherein at least 50% by volume of the components in said hydrocarbon feedstock boil above 550° F., and of said components, at least 60% by volume are converted during said contacting to product components boiling below 550° F.
Claim 14
Dependent Claim
57 words
A process as defined in claim 11 wherein said product hydrocarbon contains a substantial proportion of product components boiling in the C 4 to 700° F. range, with those product components boiling in the 300° to 550° F. turbine fuel range comprising at least 40% by volume of the total C 4 to 700° F. product components.
Claim 15
Dependent Claim
52 words
A process as defined in claim 12 wherein, of said product components boiling in the C 4 to 700° F. range, at least about 50 volume percent boil in the 300° to 550° F. turbine fuel range and at least 15 volume percent boil in the 185° to 300° F. gasoline range.
Claim 16
Dependent Claim
164 words
In a catalytic hydrocracking process, the improvement comprising contacting a hydrocarbon feedstock with a hydrocracking catalyst under hydrocracking conditions producing a substantial number of product hydrocarbon components boiling in the C 4 to 700° F. range, with more than 50 volume percent of said product hydrocarbon components being a middle distillate product boiling in the range of about 300° tc 700° F. and at least about 15 volume percent of said components being a gasoline product boiling in the range of about 185° and 300° F., said hydrocracking catalyst comprising a nickel.or cobalt active metal component and a molybdenum or tungsten active metal component on a support comprising in intimate admixture (1) a dispersion of silica-alumina in alumina and (2) a zeolite comprising at least 25 percent by weight of said support and having an X-ray powder diffraction pattern consistent with a Y zeolite of unit cell size below about 24.55 angstroms and a SiO 2 to Al 2 O 3 ratio above 6.
Claim 17
Dependent Claim
164 words
In a catalytic hydrocracking process, the improvement comprising contacting a hydrocarbon feedstock with a hydrocracking catalyst under hydrocracking conditions producing a substantial number of product hydrocarbon components boiling in the C 4 to 700° F. range, with more than 50 volume percent of said product hydrocarbon components being a middle distillate product boiling in the range of about 300° tc 700° F. and at least about 15 volume percent of said components being a gasoline product boiling in the range of about 185° and 300° F., said hydrocracking catalyst comprising a nickel.or cobalt active metal component and a molybdenum or tungsten active metal component on a support comprising in intimate admixture (1) a dispersion of silica-alumina in alumina and (2) a zeolite comprising at least 25 percent by weight of said support and having an X-ray powder diffraction pattern consistent with a Y zeolite of unit cell size below about 24.55 angstroms and a SiO 2 to Al 2 O 3 ratio above 6.
Claim 18
Dependent Claim
31 words
A process as defined in claim 14 wherein said zeolite has a silica-to-alumina mole ratio between 8.5 and 15.0 and comprises more than 30 percent by weight of said hydrocracking catalyst.
Claim 19
Dependent Claim
29 words
A process as defined in claim 15 wherein said middle distillate product comprises more than.about 65 percent by volume of said C 4 to 700° F. product hydrocarbon components.
Claim 20
Dependent Claim
30 words
A process as defined in claim 15 wherein said middle distillate product comprises more than about 70 percent by volume of said C 4 to 700° F. product hydrocarbon components.
Claim 21
Dependent Claim
29 words
A process as defined in claim 17 wherein said gasoline product comprises more than about 20 percent by volume of said C 4 to 700° F. product hydrocarbon components.
Claim 22
Dependent Claim
47 words
A process as defined in claim 15 wherein at least 50 percent by volume of the components in said hydrocarbon feedstock boils above about 550° F., and of said components, at least 90 percent by volume are converted during said contacting to products boiling below 550° F.
Claim 23
Dependent Claim
29 words
A process as defined in claim 14, 15, 18, or 19 wherein said zeolite contains less than about 0.2 percent by weight of alkali metals, calculated as the monoxides.
Claim 24
Dependent Claim
130 words
In a catalytic hydrocracking process, the improvement comprising contacting a hydrocarbon feedstock with a hydrocracking catalyst under hydrocracking conditions, including the presence of hydrogen, producing a product hydrocarbon of lower average molecular weight than said feedstock with a catalyst comprising a Group VIB or Group VIII metal component in intimate admixture with a dispersion of silica-alumina in alumina and a zeolite, said zeolite being prepared by a method comprising: (1) contacting a Y zeolite with a fluorosilicate compound, said Y zeolite having been at least partially cation-exchanged to contain ammonium cations and said contacting yielding a resultant zeolite having a silica-to-alumina mole ratio above 6.0; and (2) calcining the resultant zeolite at an elevated temperature in the presence of water vapor at a partial pressure of at least 0.2 p.s.i.a.
Claim 25
Dependent Claim
130 words
In a catalytic hydrocracking process, the improvement comprising contacting a hydrocarbon feedstock with a hydrocracking catalyst under hydrocracking conditions, including the presence of hydrogen, producing a product hydrocarbon of lower average molecular weight than said feedstock with a catalyst comprising a Group VIB or Group VIII metal component in intimate admixture with a dispersion of silica-alumina in alumina and a zeolite, said zeolite being prepared by a method comprising: (1) contacting a Y zeolite with a fluorosilicate compound, said Y zeolite having been at least partially cation-exchanged to contain ammonium cations and said contacting yielding a resultant zeolite having a silica-to-alumina mole ratio above 6.0; and (2) calcining the resultant zeolite at an elevated temperature in the presence of water vapor at a partial pressure of at least 0.2 p.s.i.a.
Claim 26
Dependent Claim
48 words
A process as defined in claim 21 wherein said fluorosilicate contacted with said Y zeolite in step (1) comprises an aqueous liquid solution of ammonium fluorosilicate, and wherein, after calcination in step (2), the sodium content of the resulting zeolite is reduced by cation exchange with ammonium cations.
Claim 27
Dependent Claim
15 words
A process as defined by claim 1 wherein said crystalline aluminosilicate zeolite comprises LZ-210 zeolite.
References Cited (Backward Citations)
US3130007A
Cited
US3251902A
Cited
US3277018A
Cited
US3312615A
Cited
US3542670A
Cited
US3506400A
Cited
US3783124A
Cited
US3640681A
Cited
US3694345A
Cited
US3997618A
Cited
US3729521A
Cited
US3835028A
Cited
US3929672A
Cited
US3853742A
Cited
US3897327A
Cited
US3926780A
Cited
US3838040A
Cited
US3945943A
Cited
US3835027A
Cited
US4120825A
Cited
US4085068A
Cited
US4097365A
Cited
US4062809A
Cited
US4115248A
Cited
US4179356A
Cited
DE2906656A1
Cited
US4377468A
Cited
US4503023A
Cited
US4419271A
Cited
EP0028938A1
Cited
US4401556A
Cited
US4517073A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-03-17 | 1989-09-16 | 1990-03-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-03-17 | 1993-09-16 | 1994-03-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-03-17 | 1997-09-16 | 1998-03-18 | $7700.00 | Window Closed / Lapsed |