Rail having high resistance to wear in its head and high resistance to rupture in its foot
Assignee: Krupp Stahl AG
•
Filing: 1984-10-01
•
Granted: 1986-03-11
•
Expires: 2004-10-01
Abstract
Abstract The invention relates to a rail having high resistance to wear in its head and high resistance to rupture in its foot. It is the characteristic feature of the invention that after rolling followed by heat treatment the rail has a fine pearlitic structure in the head and a martensitic annealed grain structure in the foot. The invention also includes preferred methods of heat treatment for the rail.
Inventors
- 👤 Wilhelm Heller
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 10:56
CPC Classifications
C; C21; C21D; C21D9/00; C21D9/04; Y; Y10; Y10S; Y10S148/00; Y10S148/902
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
53 words
In a rail for a rail vehicle comprising a head and a foot interjoined by a web, the improvement wherein said rail is one having a fine pearlitic structure in its head to at least a depth of 20 mm from the surface and a martensitic annealed grain structure throughout its entire foot.
Claim 2
Dependent Claim
53 words
In a rail for a rail vehicle comprising a head and a foot interjoined by a web, the improvement wherein said rail is one having a fine pearlitic structure in its head to at least a depth of 20 mm from the surface and a martensitic annealed grain structure throughout its entire foot.
Claim 3
Dependent Claim
73 words
A rail according to claim 1 having the following composition: carbon: 0.60 to 0.82 weight percent silicon: up to 0.5 weight percent manganese: 0.70 to 1.70 weight percent balance iron with usual impurities resulting from smelting, said rail having a tensile strength above 1100 N/mm 2 in the head and a crack resistance value of greater than 3000 N/mm 3/2 with a tensile strength of greater than 900 N/mm 2 in the foot.
Claim 4
Dependent Claim
89 words
A rail according to claim 1 having the following composition: carbon: 0.65 to 0.82 weight percent silicon: 0.1 to 1.20 weight percent manganese: 0.70 to 1.50 weight percent chromium: 0.40 to 1.30 weight percent vanadium: up to 0.2% by weight molybdenum: up to 0.15% by weight balance iron with usual impurities resulting from smelting, said rail having a tensile strength of over 1100 N/mm 2 in the head and a crack resistance value greater than 2000 N/mm 2/3 with a tensile of over 1000 N/mm 2 in the foot.
Claim 5
Independent Claim
135 words
A method for producing a rail for a rail vehicle and having a head and a foot interjoined by a web, which comprises the steps of: subjecting a rail which has been rolled and air-cooled to room temperature to a temperature from 810° to 890° C. to austenized the same and thereafter cooling the same such that the rate of cooling in the head region is such to impart a fine pearlitic structure to such head region to at least to a depth of 20 mm from the surface after the same has been cooled to room temperature, the rate of cooling in the foot region being selected such that the resultant foot has a martensitic structure throughout after being cooled and thereafter heat treating said foot at a temperature of 600° to 700° C.
Claim 6
Independent Claim
135 words
A method for producing a rail for a rail vehicle and having a head and a foot interjoined by a web, which comprises the steps of: subjecting a rail which has been rolled and air-cooled to room temperature to a temperature from 810° to 890° C. to austenized the same and thereafter cooling the same such that the rate of cooling in the head region is such to impart a fine pearlitic structure to such head region to at least to a depth of 20 mm from the surface after the same has been cooled to room temperature, the rate of cooling in the foot region being selected such that the resultant foot has a martensitic structure throughout after being cooled and thereafter heat treating said foot at a temperature of 600° to 700° C.
Claim 7
Dependent Claim
57 words
A method according to claim 4 wherein the head region of said rail is cooled at a mean rate of cooling of 15° to 50° C. per second down to a temperature of 450° C. and the foot is cooled at a rate of 5° to 60° C. per second down to a temperature of 100° C.
Claim 8
Dependent Claim
52 words
A method according to claim 4 wherein the rail is continuously heated at a temperature of 810° to 890° C. to austenitize the same and then is continuously quenched by applying compressed air or mixtures of compressed air and water or mixtures of compressed air and water vapor thereto through a nozzle.
Claim 9
Independent Claim
135 words
A method of producing a rail for a rail vehicle and having a head and a foot interjoined by a web, which comprises the steps of: subjecting a rolled rail which has been air-cooled to room temperature to impart a fine pearlitic structure to the head region to at least a depth of 20 mm from the surface to heating to a temperature of 810° to 890° C. in the foot of the rail and thereafter continuously cooling the same at a mean rate of cooling of 5° to 60° C. per second by applying thereto a mixture of compressed air and water or a mixture of water and steam via nozzles whereby to impart to said foot a martensitic structure throughout and, thereafter, heating said foot at a temperature of 600° to 700° C.
Claim 10
Independent Claim
135 words
A method of producing a rail for a rail vehicle and having a head and a foot interjoined by a web, which comprises the steps of: subjecting a rolled rail which has been air-cooled to room temperature to impart a fine pearlitic structure to the head region to at least a depth of 20 mm from the surface to heating to a temperature of 810° to 890° C. in the foot of the rail and thereafter continuously cooling the same at a mean rate of cooling of 5° to 60° C. per second by applying thereto a mixture of compressed air and water or a mixture of water and steam via nozzles whereby to impart to said foot a martensitic structure throughout and, thereafter, heating said foot at a temperature of 600° to 700° C.
Claim 11
Independent Claim
86 words
A method of producing a rail for a rail vehicle and having a pearlitic head and a martensitic foot interjoined by a web, which comprises the steps of rolling a rail at a rolling heat and, thereafter, cooling the foot portion of such rail at a rate of 5° to 60° C. per second by applying a mixture of compressed air and water or a mixture of water and steam via nozzles whereby to form a martensitic structure throughout until such rail has reached room temperature.
Claim 12
Independent Claim
86 words
A method of producing a rail for a rail vehicle and having a pearlitic head and a martensitic foot interjoined by a web, which comprises the steps of rolling a rail at a rolling heat and, thereafter, cooling the foot portion of such rail at a rate of 5° to 60° C. per second by applying a mixture of compressed air and water or a mixture of water and steam via nozzles whereby to form a martensitic structure throughout until such rail has reached room temperature.
Claim 13
Dependent Claim
39 words
A method according to claim 4 wherein said rail has the following composition: carbon: 0.60 to 0.82 weight percent silicon: up to 0.5 weight percent manganese: 0.70 to 1.70 weight percent balance iron with usual impurities resulting from smelting.
Claim 14
Dependent Claim
57 words
A method according to claim 7 wherein said rail has the following composition: carbon: 0.65 to 0.82 weight percent silicon: 0.1 to 1.20 weight percent manganese: 0.70 to 1.50 weight percent chromium: 0.40 to 1.30 weight percent vanadium: up to 0.2% by weight molybdenum: up to 0.15% by weight balance iron with usual impurities resulting from smelting.
Claim 15
Dependent Claim
57 words
A method according to claim 8 wherein said rail has the following composition: carbon: 0.65 to 0.82 weight percent silicon: 0.1 to 1.20 weight percent manganese: 0.70 to 1.50 weight percent chromium: 0.40 to 1.30 weight percent vanadium: up to 0.2% by weight molybdenum: up to 0.15% by weight balance iron with usual impurities resulting from smelting.
References Cited (Backward Citations)
US1285749A
Cited
US1418985A
Cited
US1828325A
Cited
US2793947A
Cited
DE1583418A1
Cited
US3726724A
Cited
US4082577A
Cited
US4486248A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-03-10 | 1989-09-09 | 1990-03-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-03-10 | 1993-09-09 | 1994-03-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-03-10 | 1997-09-09 | 1998-03-11 | $7700.00 | Window Closed / Lapsed |