Suspension method of impregnating active material into composite nickel plaque
Assignee: United States Department of the Navy
•
Filing: 1985-05-29
•
Granted: 1986-03-04
•
Expires: 2005-05-29
Abstract
Abstract A process for impregnating nickel or cadmium active material into a sintered nickel coated graphite fiber composite plaque electrode in which a suspension of 1-20 micron particles of active material in ethylene glycol in a 1:1 to 1:4 weight ratio of glycol to particles is gently worked into the plaque and the ethylene glycol is then evaporated off leaving the particles of active material distributed throughout the plaque. This procedure is repeated until the desired level of loading is achieved.
Inventors
- 👤 William Ferrando
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 01:48
CPC Classifications
C; C22; C22C; C22C49/00; C22C49/14; H; H01; H01M; H01M4/00; H01M4/02; H01M4/04; H01M4/0402; H01M4/0416; H01M4/043; H01M4/0435; H01M4/24; H01M4/26; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
185 words
A process for impregnating a sintered nickel coated graphite fiber plaque with a nickel active material to form a nickel electrode comprising: (1) forming a suspension of particles of a nickel active material selected from the group consisting of nickel hydroxide, nickel oxide, and mixtures thereof in ethylene glycol wherein the particles are 20 microns or less in size and wherein the weight ratio of ethylene glycol to nickel active material is from 1:1 to 1:4, (2) gently working the suspension of nickel active material in ethylene glycol into the sintered nickel coated graphte fiber plaque by (a) applying the suspension onto the top surface of the plaque, (b) gently pushing the suspension into the plaque while allowing the pull of gravity on the suspension to do much of the work; and (c) removing any excess of suspension from the surface of the plaque; (3) evaporating the ethylene glycol from the plaque to leave the particles of nickel active material distributed throughout the plaque; and (4) repeating steps (2) through (3) until the desired amount of nickel active material has been deposited in the plaque.
Claim 2
Dependent Claim
185 words
A process for impregnating a sintered nickel coated graphite fiber plaque with a nickel active material to form a nickel electrode comprising: (1) forming a suspension of particles of a nickel active material selected from the group consisting of nickel hydroxide, nickel oxide, and mixtures thereof in ethylene glycol wherein the particles are 20 microns or less in size and wherein the weight ratio of ethylene glycol to nickel active material is from 1:1 to 1:4, (2) gently working the suspension of nickel active material in ethylene glycol into the sintered nickel coated graphte fiber plaque by (a) applying the suspension onto the top surface of the plaque, (b) gently pushing the suspension into the plaque while allowing the pull of gravity on the suspension to do much of the work; and (c) removing any excess of suspension from the surface of the plaque; (3) evaporating the ethylene glycol from the plaque to leave the particles of nickel active material distributed throughout the plaque; and (4) repeating steps (2) through (3) until the desired amount of nickel active material has been deposited in the plaque.
Claim 3
Dependent Claim
14 words
A process according to claim 1 wherein the nickel active material is nickel hydroxide.
Claim 4
Dependent Claim
41 words
A process according to claim 1 wherein from more than zero to about 10 weight percent of a cobalt additive material selected from the group consisting of cobalt hydroxide, cobalt oxide, and mixtures thereof is included with the nickel active material.
Claim 5
Dependent Claim
27 words
A process according to claim 3 wherein from about 5 to about 7 weight percent of the cobalt additive material is included with the nickel active material.
Claim 6
Dependent Claim
14 words
A process according to claim 1 wherein the cobalt active material is cobalt hydroxide.
Claim 7
Dependent Claim
22 words
A process according to claim 1 wherein the weight ratio of ethylene glycol to nickel active material is from 1:2 to 1:3.
Claim 8
Dependent Claim
20 words
A process according to claim 1 wherein the particles of nickel active material are less than 5 microns in size.
Claim 9
Dependent Claim
23 words
A process according to claim 1 wherein the evaporation in step (3) is performed at a temperature of from 50° to 150° C.
Claim 10
Dependent Claim
23 words
A process according to claim 8 wherein the evaporation in step (3) is performed at a temperature of from 150° to 190° C.
Claim 11
Dependent Claim
186 words
A process for impregnating a sintered nickel coated graphite fiber plaque with a cadmium active material to form a cadmium electrode comprising: (1) forming a suspension of particles of a cadmium active material selected from the group consisting of cadmium hydroxide, cadmium oxide, and mixtures thereof in ethylene glycol wherein the particles are 20 microns or less in size and wherein the weight ratio of ethylene glycol to cadmium active material is from 1:1 to 1:4; (2) gently working the suspension of cadmium active material in ethylene glycol into the sintered nickel coated graphite fiber plaque by (a) applying the suspension onto the top surface of the plaque, (b) gently pushing the suspension into the plaque while allowing the pull of gravity on the suspension to do much of the work; and (c) removing any excess of suspension from the surface of the plaque; (3) evaporating the ethylene glycol from the plaque to leave the particles of the cadmium active material distributed throughout the plaque; and (4) repeating steps (2) through (3) until the desired amount of nickel activated material has been deposited in the plaque.
Claim 12
Dependent Claim
186 words
A process for impregnating a sintered nickel coated graphite fiber plaque with a cadmium active material to form a cadmium electrode comprising: (1) forming a suspension of particles of a cadmium active material selected from the group consisting of cadmium hydroxide, cadmium oxide, and mixtures thereof in ethylene glycol wherein the particles are 20 microns or less in size and wherein the weight ratio of ethylene glycol to cadmium active material is from 1:1 to 1:4; (2) gently working the suspension of cadmium active material in ethylene glycol into the sintered nickel coated graphite fiber plaque by (a) applying the suspension onto the top surface of the plaque, (b) gently pushing the suspension into the plaque while allowing the pull of gravity on the suspension to do much of the work; and (c) removing any excess of suspension from the surface of the plaque; (3) evaporating the ethylene glycol from the plaque to leave the particles of the cadmium active material distributed throughout the plaque; and (4) repeating steps (2) through (3) until the desired amount of nickel activated material has been deposited in the plaque.
Claim 13
Dependent Claim
14 words
A process according to claim 10 wherein the cadmium active material is cadmium hydroxide.
Claim 14
Dependent Claim
22 words
A process according to claim 10 wherein the weight ratio of ethylene glycol to cadmium active material is from 1:2 to 1:3.
Claim 15
Dependent Claim
20 words
A process according to claim 10 wherein the particles of cadmium active material are less than 5 microns in size.
Claim 16
Dependent Claim
23 words
A process according to claim 10 wherein the evaporation in step (3) is performed at a temperature of from 50° to 150° C.
Claim 17
Dependent Claim
23 words
A process according to claim 14 wherein the evaporation in step (3) is performed at a temperature of from 150° to 190° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-03-03 | 1989-09-02 | 1990-03-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-03-03 | 1993-09-02 | 1994-03-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-03-03 | 1997-09-02 | 1998-03-04 | $7700.00 | Window Closed / Lapsed |