Assignee: Dow Chemical Co
•
Filing: 1978-09-05
•
Granted: 1980-02-19
•
Expires: 1998-09-05
Abstract
Abstract A porous nickel body is interiorly silver plated in a two-step procedure by: first, acid etching the nickel surface for activation; then plating the activated surface by replacement of elemental nickel thereon with silver from a dissolved aqueous cyanide or equivalent silver salt.
Inventors
- 👤 James A. McIntyre
- 👤 Robert F. Phillips
- 👤 Joseph D. Lefevre
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 02:55
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/31; C23C18/42
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
110 words
Two-step procedure for replacement plating silver on at least the interior surface areas of a porous nickel substrate body comprising: as the first step, etching the surface areas of the porous nickel body over which silver plate is to be laid with an aqueous solution of a mineral acid capable of removing oxide deposits from the nickel on bare elemental nickel on said surface areas to activate same; then subsequently and as the second step, contacting the activated nickel surface areas with an aqueous plating solution of a silver salt capable of laying silver plate by displacement of nickel in the substrate and replacement thereof with silver from the solution.
Claim 2
Dependent Claim
110 words
Two-step procedure for replacement plating silver on at least the interior surface areas of a porous nickel substrate body comprising: as the first step, etching the surface areas of the porous nickel body over which silver plate is to be laid with an aqueous solution of a mineral acid capable of removing oxide deposits from the nickel on bare elemental nickel on said surface areas to activate same; then subsequently and as the second step, contacting the activated nickel surface areas with an aqueous plating solution of a silver salt capable of laying silver plate by displacement of nickel in the substrate and replacement thereof with silver from the solution.
Claim 3
Dependent Claim
43 words
The essential procedure of claim 1 and including, in addition thereto and in combination therewith, thoroughly water washing the acid etched body as part of said first step to render it free from acid prior to performance of said second plate laying step.
Claim 4
Dependent Claim
17 words
The procedure of claim 1, wherein the acid is hydrochloric of at least one (1) Molar strength.
Claim 5
Dependent Claim
11 words
The procedure of claim 1, wherein the acid is concentrated hydrochloric.
Claim 6
Dependent Claim
22 words
The procedure of claim 1, wherein the plating solution is comprised of silver cyanide as the essential plating agent in said solution.
Claim 7
Dependent Claim
22 words
The procedure of claim 1, wherein the plating solution is comprised of a mixture of silver cyanide and an alkali metal cyanide.
Claim 8
Dependent Claim
35 words
The procedure of claim 1, wherein the plating solution is comprised of a mixture of silver cyanide and potassium cyanide containing at least about 30 g/l AgCN and not more than about 75 g/l KCN.
Claim 9
Dependent Claim
34 words
The procedure of claim 1, wherein the plating solution is comprised of a mixture of silver cyanide and potassium cyanide in a respective Molar ratio of at least about 1:1 of AgCN to KCN.
Claim 10
Dependent Claim
23 words
A procedure according to the procedure of claim 8, wherein said plating solution contains about 60 g/l AgCN and about 30 g/l KCN.
Claim 11
Dependent Claim
46 words
The procedure of claim 1, wherein the porous nickel substrate body to be plated is a sintered, fabricated powder metal form adapted to electrode usage having pores therein with an average nominal pore diameter in the range of from about 0.1 micron to about 25 microns.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-02-18 | 1983-08-20 | 1984-02-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-02-18 | 1987-08-20 | 1988-02-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-02-18 | 1991-08-20 | 1992-02-19 | $7700.00 | Window Closed / Lapsed |